The effect of different power densities and method of exposure on the marginal adaptation of four light-cured dental restorative materials

Biomaterials

Volumn 24, Issue 20, 2003, Pages 3593-3598

  Oberholzer, Theunis G ^a   Pameijer, Cornelis H ^a,b   Grobler, Sias R ^a   Rossouw, Roelof J ^a  

^a STELLENBOSCH UNIVERSITY   (South Africa)

^b UNIVERSITY OF CONNECTICUT   (United States)

Author keywords

Adhesion; Dental resins; Polymerization shrinkage; Shear bond strengths

Indexed keywords

ADHESION; COMPOSITE MATERIALS; CURING; POLYMERIZATION; RESINS; SHRINKAGE; STAINLESS STEEL;

DENTAL RESIN COMPOSITES;

DENTAL MATERIALS;

BIOMATERIAL; HALOGEN; METAL; RESIN; STAINLESS STEEL;

ADHESION; ANALYSIS OF VARIANCE; ARTICLE; COMPARATIVE STUDY; DENSITY; ELASTICITY; ENDODONTICS; FORCE; IRRADIATION; LIGHT; LIGHT EXPOSURE; PARAMETER; POLYMERIZATION; PRIORITY JOURNAL; STRENGTH; SURFACE PROPERTY; TECHNIQUE; TENSION;

EID: 0038722676     PISSN: 01429612     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-9612(03)00211-4     Document Type: Article

References (25)

1. Koran P., Kürschner R. Effect of sequential versus continuous irradiation of a light-cured resin composite on shrinkage, viscosity, adhesion, and degree of polymerization. Am J Dent. 10:1998;17-22.
2. Lovell L.G., Newman S.M., Bowman C.N. The effects of light intensity, temperature, and comonomer composition on the polymerization behavior of dimethacrylate dental resins. J Dent Res. 78(8):1999;1469-1476.
3. Mehl A., Hickel R., Kunzelmann K. Physical properties and gap formation of light-cured composites with and without 'softstart-polymerization'. J Dent. 25(3-4):1997;321-330.
4. Price R., Bannerman R A., Rizkalla A S., Hall G C. Effect of stepped vs. continuous light-curing exposure on bond strengths to dentin. Am J Dent. 13:2000;123-128.
5. Peutzfeldt A., Garcia-Godoy F., Asmussen E. Surface hardness and wear of glass ionomers and compomers. Am J Dent. 10:1997;15-17.
6. Rueggeberg F., Caughman W., Curtis J.J. Effect of light intensity and exposure duration on cure of resin composite. Oper Dent. 19(1):1994;26-32.
7. Davidson C., De Gee A., Feilzer A. The competition between the composite-dentin bond strength and the polymerization contraction stress. J Dent Res. 63:1984;1396-1399.
8. Reinardt K., Teichert H., Vahl J. Die Bedeitung des Elastizitätmoduls fur die Randständigkeit von Kompositen. Dtsch Zahnärztl Z. Z39:1984;25-29.
9. Feilzer A.J., Dooren L.H., de Gee A.J., Davidson C.L. Influence of light intensity on polymerization shrinkage and integrity of restoration-cavity interface. Eur J Oral Sci. 103:1995;322-326.
10. Uno S., Asmussen E. Marginal adaptation of a restorative resin polymerized at reduced rate. Scand J Dent Res. 99:1991;440-444.
11. Dennison J.B., Yaman P., Seir R., Hamilton J. Effect of variable light intensity on composite shrinkage. J Prosth Dent. 84(5):2000;499-505.
12. Kanca J., Suh B.I. Pulse activation. reducing resin-based composite contraction stresses at the enamel cavosurface margins Am J Dent. 12:1999;107-112.
13. Cortes O., Garcia C., Perez L., Perez D. Marginal microleakage around enamel and cementum surfaces of two compomers. J Clin Ped Dent. 22(4):1998;307-315.
14. Goracci G., Mori G., de' Martinis L.C. Curing light intensity and marginal leakage of resin composite restorations. Quintessence Int. 27(5):1996;355-361.
15. Oberholzer T.G., Pameijer C.H., Grobler S.R., Rossouw R.J. Use of a modified dilatometer for determining volumetric polymerization shrinkage of dental restorative materials. Meas Sci Technol. 13:2002;78-83.
16. Miyazaki M., Fukuishi K., Onose H. Influence of light irradiation on the volumetric change of polyacid-modified resin composites. J Dent. 27:1999;149-153.
17. Labella R., Lambrechts P., Van Meerbeek B., Vanherle G. Polymerization shrinkage and elasticity of flowable composites and filled adhesives. Dent Mater. 15:1999;128-137.
18. Goldman M. Polymerization shrinkage of resin based restorative materials. Aust Dent J. 28:1983;156-161.
19. Oberholzer TG, Grobler SR, Pameijer CH, Rossouw RJ. Effect of different exposures on shrinkage of dental resin materials. Oper Dent, accepted for publication.
20. Sakaguchi R.L., Douglas W.H., Peters M.C.R.B. Curing light performance and polymerization of composite restorative materials. J Dent. 20:1992;183-188.
21. Yap A.U.J., Ng S.C., Siow K.S. Soft-start polymerization. influence on effectiveness of cure and post-gel shrinkage Oper Dent. 26:2001;260-266.
22. Sahafi A., Peutzfeldt A., Asmussen E. Soft-start polymerization and marginal gap formation in vitro. Am J Dent. 14:2001;145-147.
23. Fleming M.G., Maillet W.A. Photopolymerization of composite resin using the argon laser. J Can Dent Assoc. 65(8):1999;447-450.
24. Pilo R., Cardash H.S. Post-irradiation polymerization of different anterior and posterior visible-light-activated resin composites. Dent Mater. 8(5):1992;299-304.
25. Oberholzer TG, Grobler SR, Pameijer CH, Hudson APGH. The effects of light intensity and exposure on the hardness of four light-cured dental restorative materials. Int Dent J, accepted for publication.