Organization of microcrystals on glass by adenine-thymine hydrogen bonding

Journal of the American Chemical Society

Volumn 124, Issue 45, 2002, Pages 13366-13367

  Park, Jin Seon ^a   Lee, Goo Soo ^a   Lee, Yun Jo ^a   Park, Yong Soo ^a   Yoon, Kyung Byung ^a  

^a Sogang University   (South Korea)

Author keywords

[No Author keywords available]

Indexed keywords

ADENINE; GLASS; NANOPARTICLE; THYMINE; ZEOLITE;

ARTICLE; CRYSTAL; CRYSTAL STRUCTURE; HYDROGEN BOND; METHODOLOGY; PARTICLE SIZE; SCANNING ELECTRON MICROSCOPY;

ADENINE; CRYSTALLIZATION; DNA; GLASS; HYDROGEN BONDING; MICROSCOPY, ELECTRON, SCANNING; SURFACE PROPERTIES; THYMINE;

EID: 0037073226     PISSN: 00027863     EISSN: None     Source Type: Journal    
DOI: 10.1021/ja0270569     Document Type: Article

References (31)

1. (a) Bowden, N. B.; Weck, M.; Choi, I. S.; Whitesides, G. M. Acc. Chem. Res. 2001, 34, 231.
2. (b) Ozin, G. A. Adv. Mater. 1992, 4, 612.
3. (c) Ozin, G. A. Chem. Commun. 2000, 419.
4. (d) Calzaferri, G.; Pauchard, M.; Maas, H.; Huber, S.; Khatyr, A.; Schaafsma, T. J. Mater. Chem. 2002, 12, 1.
5. (e) Weiner S.; Addadi, L. J. Mater. Chem. 1997, 7, 689.
6. (f) Stupp, S. I.: Braun, P. V. Science 1997, 277, 1242.
7. (a) Clark, T. D.; Tien, J.; Duffy, D. C.; Paul, K. E.; Whitesides, G. M. J. Am. Chem. Soc. 2001, 123, 7677.
8. (b) Li, Z.; Lai, C.; Mallouk, T. E. Inorg. Chem. 1989, 28, 178.
9. (a) Lainé, P.; Seifert, R.; Giovanoli, R.; Calzaferri, G. New J. Chem. 1997, 21, 453.
10. (b) Ban, T.; Ohwaki, T.; Ohya, Y.; Takahashi, Y. Angew. Chem., Int. Ed. 1999, 38, 3324.
11. (a) Kulak, A.; Lee, Y.-J.; Park, Y. S.; Yoon, K. B. Angew. Chem., Int. Ed. 2000, 39, 950.
12. (b) Choi, S. Y.; Lee, Y. -J.; Park, Y. S.; Ha, K.; Yoon, K. B. J. Am. Chem. Soc. 2000, 122, 5201.
13. (c) Kulak, A.; Park, Y. S.; Lee, Y.-J.; Chun, Y. S., Ha, K.; Yoon, K. B. J. Am. Chem. Soc. 2000, 122, 9308.
14. (d) Ha, K.; Lee, Y.-J.; Lee, H. J.; Yoon, K. B. Adv. Mater. 2000, 12, 1114.
15. (e) Lee, G. S.; Lee, Y.-J.; Yoon, K. B. J. Am. Chem. Soc. 2001, 123, 9769.
16. (a) Loweth, C. J.; Caldwell, W. B.; Peng, X.; Alivisatos, A. P.; Schultz, P. G. Angew. Chem., Int. Ed. 1999, 38, 1808.
17. (b) Taton, T. A.; Mucic, R. C.; Mirkin, C. A. Letsinger, R. L. J. Am. Chem. Soc. 2000, 122, 6305.
18. (c) Mbindyo, J. K. N.; Reiss, B. D.; Martin, B. R.; Keating, C. D.; Natan, M. J.; Mallouk, T. E. Adv. Mater. 2001, 13, 249.
19. (d) Boal, A. K.; Ilhan, F.; DeRouchey, J. E.; Thurn-Albrecht, T.; Russell, T. P.; Rotello, V. M. Nature, 2000, 404, 746.
20. (e) Patolsky, F.; Ranjit, K. T.; Lichtenstein, A.; Willner, I. Chem Commun. 2000, 1025.
21. (f) Niemeyer, C. M. Angew. Chem., Int. Ed. 2001, 40, 4128.
22. It was reported that bare glass plates can also adsorb monolayers of bare zeolite crystals through hydrogen bonding between the surface hydroxy groups. However, the above process is highly sensitive to pH and the degree of packing between the crystals is rather poor. See ref 3.
23. The boundary between zeolite crystals becomes dim and fuzzy in the optical microscope image when the crystals closely pack.
24. (a) Mirkin, C. A.; Letsinger, R. L.; Mucic, R. C.; Storhoff, J. J. Nature 1996, 382, 607.
25. (b) Storhoff, J. J.; Lazarides, A. A.; Music, R. C.; Mirkin, C. A.; Letsinger, R. L.; Schatz, G. C. J. Am. Chem. Soc. 2000, 122, 4640.
26. (c) Voet, D.; Voet, J. G. B. Biochemistry; John Wiley & Sons Inc.: New York, 1990; p 806.
27. Freifelder, D. Molecular Biology, 2nd Ed.; Jones and Bartlett, Boston, 1990; p 85.
28. As for the driving force for the close packing, the weak hydrogen-bonding interaction between the surface-bound T groups, hydrophobic interaction of the modified surfaces, and capillary forces are likely to be responsible.
29. As a means to avoid obscurity caused by the very strong DSC curve of water, the samples were loaded in the dry state.
30. The shift of the melting temperature from 55 (in water) to 30 °C (no solvent) may arise due to change of the medium since the medium is known to sensitively affect the DSC endotherms (see. ref 8d, p 89).
31. The endotherm from the mixture of parent A and T powders is likely to arise due to the hydrogen-bonding interaction at the interfaces between the complementary solid particles.