A review of analytical aspects of fretting fatigue, with extension to damage parameters, and application to dovetail joints

International Journal of Solids and Structures

Volumn 38, Issue 10-13, 2001, Pages 1791-1811

  Ciavarella, M ^a   Demelio, G ^b  

^a CHIRON VACCINES   (Italy)

^b POLITECNICO DI BARI   (Italy)

Author keywords

Contact stresses; Crack initiation; Dovetail joints; Fretting damage; Fretting fatigue; Gas turbine engines; High cycle fatigue; Turbine blades

Indexed keywords

FATIGUE; FRETTING; GAS TURBINE; TURBINE;

CRACK INITIATION; FRETTING CORROSION; GAS TURBINES; JOINTS (STRUCTURAL COMPONENTS); STRESS ANALYSIS; STRUCTURAL ANALYSIS; TURBOMACHINE BLADES;

CONTACT STRESS; DOVETAIL JOINTS; FRETTING FATIGUE;

FATIGUE OF MATERIALS;

EID: 0035966421     PISSN: 00207683     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0020-7683(00)00136-0     Document Type: Article

References (69)

1. Elastic deformation and the laws of friction
2. Analysis of pad size effects in fretting fatigue using short crack arrest methodologies
3. High cycle fatigue and a finite element analysis
4. The influence of strain-hardening on cumulating plastic deformation in rolling and sliding contact
5. Teoria del contatto elastico in seconda approssimazione: Compressione obliqua
6. The generalized Cattaneo partial slip plane contact problem
7. The generalized Cattaneo partial slip plane contact problem
8. Tangential loading of general 3D contacts
9. Indentation by nominally flat or conical indenters with rounded corners
10. On non-symmetrical plane contacts
11. The use of almost complete contacts for fretting fatigue tests
12. An analysis of rotating bending fretting fatigue tests using 'bridge' specimens
13. Linear elastic contact of the weierstrass profile
14. The influence of rounded edges on indentation by a flat punch
15. Brief note: Some observation on oscillating tangential forces and wear in general plane contacts
16. Analysis of plane, rough contacts, subject to a shearing force
17. Fretting fatigue mechanisms and the effect of direction of fretting motion on fatigue strength
18. Analysis of surface tractions in complex fretting fatigue cycles using quadratic programming
19. The endurance of metals
20. The application of fracture mechanics to predicting fretting fatigue
21. Initiation and propagation of fretting fatigue cracks
22. Contact stresses in a moderately thin strip with particular reference to fretting experiments
23. Analysis of crack initiation and propagation in fretting fatigue: The effective initial flaw size methodology
24. Fretting corrosion and its influence on fretting failure
25. Identification of the characteristic length scale for fatigue cracking in fretting contacts
26. Overview No. 129, aspects of equivalence between contact mechanics and fracture mechanics: Theoretical connections and a life-prediction methodology for fretting-fatigue
27. Notes on some endurance tests of metals
28. The development of a fretting fatigue experiment with well-defined characteristics
29. Origins of partial slip in fretting - A review of known potential solutions
30. Fretting fatigue considerations in engineering design
31. Fretting fatigue of Ti-6Al-4V under flat-on-contact
32. Analyses of contact pressure and stress amplitude effects on fretting fatigue life
33. A new principle in contact mechanics
34. Initiation and growth of fretting fatigue cracks in the partial slip regime
35. Compliance of elastic bodies in contact
36. Designing against fretting fatigue: Crack self-arrest
37. An analysis of coupling between plane contacts and cracks
38. Methodologies for linking nucleation and propagation approaches for predicting life under fretting fatigue
39. Fundamental investigation of fretting fatigue, On the relative slip amplitude of press-fitted axle assemblies
40. Fundamental investigation of fretting fatigue, Some phenomena and mechanism of surface cracks
41. Fundamental investigation of fretting fatigue, The effect of mean stress
42. Fundamental investigation of fretting fatigue, The effect of relative slip amplitude
43. The application of fracture-mechanics to fretting fatigue
44. Crack initiation criteria in fretting fatigue
45. Influence of contact configuration in fretting fatigue testing
46. An investigation of fatigue and fretting in a dovetail joint
47. Life assessment of dovetail joints between blades and discs in aero-engines
48. Mechanics of fretting fatigue crack formation
49. Observation, analysis and prediction of fretting fatigue in 2024-T351 aluminum alloy
50. Geometrical effects in fatigue: A unifying theoretical model
51. The national high cycle fatigue (HCF) program
52. The rusting of steel surfaces in contact
53. Fretting corrosion and fatigue strength: Brief results of preliminary experiments
54. Fretting fatigue
55. The influence of fretting and geometric stress concentrations on the fatigue strength of clamped joints
56. Lubrication in fretting - A review