Fretting fatigue of Ti-6Al-4V under flat-on-flat contact

International Journal of Fatigue

Volumn 21, Issue 7, 1999, Pages 663-669

  Hutson, Alisha L ^a   Nicholas, Ted ^b   Goodman, Rick ^a  

^a UNIVERSITY OF DAYTON RESEARCH INSTITUTE   (United States)

^b Metals   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK INITIATION; DEFECTS; FATIGUE TESTING; FRACTOGRAPHY; FRETTING CORROSION; SHEAR STRESS; TITANIUM ALLOYS; TURBOMACHINE BLADES;

AXIAL LOADS; CRACK INITIATION SITES; FAILURE LOCATION; FRETTING DAMAGE; FRETTING FATIGUE; TURBOMACHINE BLADE ATTACHMENTS;

FATIGUE OF MATERIALS;

EID: 0032592142     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(99)00027-4     Document Type: Article

References (21)

1. Ruiz C., Boddington P.H.B., Chen K.C. An investigation of fatigue and fretting in a dovetail joint. Exp. Mech. 24:1984;208-217.
2. Bryggman U., Söderberg S. Contact conditions and surface degradation mechanisms in low amplitude fretting. Wear. 125:1988;39-52.
3. Del Puglia A., Pratesi F., Zonfrillo G. Experimental procedure and parameters involved in fretting fatigue tests. Waterhouse R.B., Lindley T.C. Fretting fatigue, ESIS 18. 1994;219-238 Mechanical Engineering Publications, London.
4. Elkholy A.H. Fretting fatigue in elastic contacts due to tangential micro-motion. Tribology Int. 29(4):1996;265-275.
5. Fellows L.J., Nowell D., Hills D.A. On the initiation of fretting fatigue cracks. Wear. 205:1996;120-129.
6. Fouvry S., Kapsa P., Vincent L. Quantification of fretting damage. Wear. 200:1996;186-205.
7. Vingsbo O., Schon J. Gross slip criteria in fretting. Wear. 162-164:1993;347-356.
8. Zhou Z.R., Vincent L. Mixed fretting regime. Wear. 181-183:1995;536-551.
9. Adibnazari S., Hoeppner D.W. The role of normal pressure in modeling fretting fatigue. Waterhouse R.B., Lindley T.C. Fretting fatigue, ESIS 18. 1994;125-133 Mechanical Engineering Publications, London.
10. Dobromirski J., Smith I.O. Metallographic aspects of surface damage, surface temperature and crack initiation in fretting fatigue. Wear. 117:1987;347-357.
11. Fayeulle S., Blanchard P., Vincent L. Fretting behavior in titanium alloys. Tribology Trans. 36(2):1993;267-275.
12. Lindley T.C., Nix K.J. Fretting fatigue in the power generation industry: experiments, analysis, and integrity assessment. Helmi Attia M., Waterhouse R.B. Standardization of fretting fatigue test methods and equipment, ASTM STP 1159. 1992;153-169 American Society for Testing and Materials, Philadelphia.
13. Waterhouse R.B. Effect of material and surface conditions on fretting fatigue. Waterhouse R.B., Lindley T.C. Fretting fatigue, ESIS 18. 1994;339-349 Mechanical Engineering Publications, London.
14. Dobromirski J.M. Variables of fretting processes: are there 50 of them? Waterhouse R.B., Lindley T.C. Fretting fatigue, ESIS 18. 1994;60-66 Mechanical Engineering Publications, London.
15. Attia M.H. Fretting fatigue testing: current practices and future prospects for standardization. Helmi Attia M., Waterhouse R.B. Standardization of fretting fatigue test methods and equipment, ASTM STP 1159. 1992;263-275 American Society for Testing and Materials, Philadelphia.
16. Hoeppner D.W. Mechanisms of fretting fatigue. Waterhouse R.B., Lindley T.C. Fretting fatigue, ESIS 18. 1994;3-19 Mechanical Engineering Publications, London.
17. Szolwinski M.P., Harish G., McVeigh P.A., Farris T.N. Experimental study of fretting crack nucleation in aerospace alloys with emphasis on life prediction. Hoeppner D.W., Chandrasekaran V., Elliot C.B. Fretting fatigue: current technologies and practices, ASTM STP 1367. 1999;American Society for Testing and Materials, West Conshohocken (PA).
18. Maxwell D.C., Nicholas T. A rapid method for generation of a Haigh diagram for high cycle fatigue. Panontin T.L., Sheppard S.D. Fatigue and fracture mechanics, Vol. 29, ASTM STP 1321. 1998;American Society for Testing and Materials, Philadelphia.
19. Bellows R.S., Muju S., Nicholas T. Validation of the step test method for generating Goodman for Ti-6Al-4V. Int. J. Fat. 21(7):1999;687-697.
20. Lanning D., Haritos G.K., Nicholas T. Notch size effects in HCF behavior of Ti-6Al-4V. Int. J. Fat. 21(7):1999;643-652.
21. Brown Lt. Jeff. Air Force Research Lab Propulsion Directorate, Wright-Patterson AFB, OH, private communication.