Observation of a double maximum in the dependence of conductivity on oxidation state in potassium fulleride nanowires supported by a mesoporous niobium oxide host lattice

Advanced Materials

Volumn 13, Issue 8, 2001, Pages 561-565

  Ye, Bing ^a   Trudeau, Michel L ^b   Antonelli, David M ^a  

^a UNIVERSITY OF WINDSOR   (Canada)

^b HYDRO QUÉBEC   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

ADDITION REACTIONS; CRYSTAL LATTICES; ELECTRIC CONDUCTIVITY OF SOLIDS; NANOSTRUCTURED MATERIALS; NIOBIUM COMPOUNDS; NUMERICAL ANALYSIS; OXIDATION; SYNTHESIS (CHEMICAL);

ALKALI FULLERIDES; MESOPOROUS NIOBIUM OXIDE; POTASSIUM FULLERIDE NANOWIRES;

POTASSIUM COMPOUNDS;

EID: 0035906207     PISSN: 09359648     EISSN: None     Source Type: Journal    
DOI: 10.1002/1521-4095(200104)13:8<561::AID-ADMA561>3.0.CO;2-B     Document Type: Article

References (29)

1. P. Ball, Made to Measure, Princeton University Press, Princeton, NJ 1997.
2. H. W. Kroto, J. R. Heath, S. C. O'Brien, R. F. Curl, R. E. Smalley, Nature 1985, 318, 162.
3. A. F. Hebard, M. J. Rosseinsky, R. C. Haddon, D. W. Murphy, S. H. Glarum, T. T. M. Palstra, A. P. Ramirez, A. R. Kortan, Nature 1991, 350, 600.
4. P. J. Benning, J. L. Martins, J. H. Weaver, L. P. F. Chibante, R. E. Smalley, Science 1991, 252, 1417.
5. S. Chakraverty, M. P. Gelfand, S. Kivelson, Science 1991, 254, 970.
6. M. Kosaka, K. Tanigaki, K. Prassides, S. Margedonna, A. Lappas, C. M. Brown, A. N. Fitch, Phys. Rev. 1999, 59, 6628.
7. T. Yildrium, L. Barbedette, J. E. Fischer, C. L. Lin, J. Robert, P. Petit, T. T. M. Palstra, Phys. Rev. Lett. 1996, 77, 167.
8. T. T. M. Palstra, A. F. Hebard, R. C. Haddon, B. Littlewood, Phys. Rev. B 1994, 50, 3462.
9. R. W. Lof, M. A. van Veenendaal, B. Koopmans, H. T. Jonkman, G. A. Sawatzky, Phys. Rev. Lett. 1992, 68, 3924.
10. D. M. Antonelli, J. Y. Ying, Angew. Chem. Int. Ed. Engl. 1996, 35, 426.
11. B. Ye, M. Trudeau, D. M. Antonelli, Adv. Mater. 2001, 13, 29.
12. a) M. Vettraino, M. Trudeau, D. M. Antonelli, Adv. Mater. 2000, 12, 337.
13. b) S. Murray, M. Trudeau, D. M. Antonelli, Inorg. Chem. 2000, 34, 5901.
14. c) S. Murray, M. Trudeau, D. M. Antonelli, Adv. Mater. 2000, 12, 1339.
15. d) M. Vettraino, M. Trudeau, D. M. Antonelli, Inorg. Chem., in press.
16. C. T. Kresge, M. E. Leonowicz, W. J. Roth, J. C. Vartulli, J. S. Beck, Nature 1992, 359, 710.
17. Q. Huo, D. I. Margolese, U. Ciesla, D. G. Demuth, P. Feng, T. E. Gier, P. Sieger, A. Firouzi, B. F. Chmelka, F. Schuth, G. D. Stucky, Chem. Mater. 1994, 6, 1176.
18. C.-Y. Chen, S. L. Burkette, H.-X. Li, M. E. Davis, Microporous Mater. 1993, 2, 27.
19. P. T. Tanev, M. Chibwe, T. J. Pinnavaia, Nature 1994, 368, 321.
20. P. Behrens, Angew. Chem. Int. Ed. Engl. 1996, 35, 515.
21. D. M. Antonelli, J. Y. Ying, Curr. Opin. Colloid Interface Sci. 1996, 1, 523.
22. U. Ciesla, S. Schacht, G. D. Stucky, K. Unger, F. Schüth, Angew. Chem. Int. Ed. Engl. 1996, 35, 541.
23. D. M. Antonelli, J. Y. Ying, Angew. Chem. Int. Ed. Engl. 1995, 34, 2014.
24. D. M. Antonelli, Adv. Mater. 1999, 11, 487.
25. Z. R. Tian, J. Y. Wang, N. G. Duan, V. V. Krishnan, S. L. Suib, Science 1997, 276, 426.
26. D. M. Antonelli, M. Trudeau, Angew. Chem. Int. Ed. 1999, 38, 1471.
27. J. Chen, Q. Li, H. Ding, W. Peng, R. Xu, Langmuir 1997, 13, 2050.
28. F. Bensebaa, B. Xiang, L. Kevan, J. Phys. Chem. 1992, 96, 10258.
29. M. M. Khaled, R. T. Carlin, P. C. Trulove, G. R. Eaton, S. S. Eaton, J. Am. Chem. Soc. 1994, 116, 3465.