Prepreg treatment with Ar+ ion irradiation to improve GIc of unidirectional graphite/epoxy laminated composites

Journal of Composite Materials

Volumn 35, Issue 18, 2001, Pages 1684-1697

  Rhee, Kyong Y ^a   Choi, Nak Sam ^b   Han, Young G ^c   Koh, Seok K ^c  

^a Kyung Hee University   (South Korea)

^b Hanyang University   (South Korea)

^c Korea Institute of Science and Technology   (South Korea)

Author keywords

Ar+ ion irradiation; Compliance calibration method; Contact angle; Delamination toughness; Fiber bridging; Resistance curve

Indexed keywords

ARGON; CONTACT ANGLE; DELAMINATION; FRACTURE TOUGHNESS; GRAPHITE FIBER REINFORCED PLASTICS; IONS; IRRADIATION; SURFACE TREATMENT;

DELAMINATION RESISTANCE; ION IRRADIATION; PREPREG TREATMENT;

LAMINATED COMPOSITES;

EID: 0034758722     PISSN: 00219983     EISSN: None     Source Type: Journal    
DOI: 10.1106/8YMW-Q0QP-TDYY-FM83     Document Type: Article

References (22)

1. Round Robin testing for mode I interlaminar fracture toughness of composite materials
2. Delamination fracture criteria for composite laminates
3. Use of end-load-split (ELS) test to study stable fracture behavior of composites under mode II loading
4. Fatigue delamination behavior of PEEK thermoplastic composite laminates
5. Characterization of matrix toughness effect on cyclic delamination growth in graphite fiber composites
6. Matrix toughness, long-term behavior and damage tolerance of notched graphite fiber-reinforced composite materials
7. The characterization of mode I delamination failure in Nonwoven, multidirectional laminates
8. Mode I and mode II fracture toughness measured between differently oriented plies in graphite/epoxy composites
9. Effects of stacking sequence on delamination toughness and delamination growth behavior in composite end-notched flexure specimens
10. Ic of a unidirectional graphite/epoxy composites
11. Mode I Interlaminar fracture of symmetrical cross-ply composites
12. Mode I delamination and fiber bridging in carbon-fiber/epoxy composites with and without Pval coating
13. Effect of surface treatment of pitch-based carbon fiber on mechanical properties of polyethernitrile composites
14. Evaluation fiber surface treatment and sizing on the shear and transverse tensile strength of carbon fiber-reinforced thermoset and thermoplastic matrix composites
15. A review of methods for improving the interfacial adhesion between carbon fiber and polymer matrix
16. Surface pretreatment and adhesive bonding of carbon fiber-reinforced epoxy composites
17. Fractography analysis of surface preparation on graphite/epoxy composites used in adhesive bonding
18. Estimation of the surface free energy of polymer
19. Thin film growth and surface modification by keV ion beam
20. + ion in oxygen environment
21. Mode I interlaminar fracture toughness of unidrectional fiber-reinforced polymer matrix composites
22. Fracture toughness characterization of phenolic resin and its composites