Post-metallocenes: A new bis(salicylaldiminato) zirconium complex for ethylene polymerization

Chemistry Letters

Volumn , Issue 12, 1999, Pages 1263-1264

  Matsui, Shigekazu ^a   Mitani, Makoto ^a   Saito, Junji ^a   Tohi, Yasushi ^a   Makio, Haruyuki ^a   Tanaka, Hidetsugu ^a   Fujita, Terunori ^a  

^a MITSUI CHEMICALS INC   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

EID: 0033236831     PISSN: 03667022     EISSN: None     Source Type: Journal    
DOI: 10.1246/cl.1999.1263     Document Type: Article

References (25)

1. Reviews: a) H. H. Brintzinger, D. Fischer, R. Muelhaupt, B. Rieger, and R. M. Waymouth, Angew.Chem., Int. Ed. Engl., 34, 1143 (1995).
2. b) W. Kaminsky and H. Sinn, "Transition Metals and Organometallics for Catalysts for Olefin Polymerization", Springer, New York (1988).
3. Review: G. J. P. Biritovsek, V. C. Gibson, and D. F. Wass, Angew. Chem., Int. Ed., 38, 428 (1999).
4. a) J. D. Scollard, D. H. McConville, N. C. Payne, and J. J. Vittal, Macromolecules, 29, 5241 (1996).
5. b) F. Guerin, D. H. McConville, and J. J Vittal, Organometallics, 15, 5586 (1996).
6. c) A. Linden, C. J. Schaverien, N. Meijboom, C. Ganter, and A. G. Orpen, J. Am. Chem. Soc, 117, 3008 (1995).
7. d) L. Matilainen, M. Hlinga, and M. Leskela, J. Chem. Soc., Dalton Trans., 1996, 219.
8. e) T. Repo, M. Klinga, P. Pietikainen, M. Leskela, A. M. Uusitalo, K. Hakala, P. Aaltonen, and B. Lofgren, Macromolecules, 30, 171 (1997).
9. f) D. Jones, A. Roberts, K. Cavell, W. Keim, U. Englert, B. W. Skelton, and A. H. White, J. Chem. Soc., Dalton Trans., 1998, 255.
10. g) E. B. Tjaden, D. C. Swenson, R. F. Jordan, and J. L. Petersen, Organometallics, 14, 371 (1995).
11. h) E. B. Tjaden and R. F. Jordan, Macromol. Symp., 89, 231 (1995).
12. i) X. Bei, D. C. Swenson, and R. F. Jordan, Organometallics, 16, 3282 (1997).
13. j) T. Tsukahara, D. C. Swenson, and R. F. Jordan, Organometallics, 16, 3303 (1997).
14. k) I. Kim, Y. Nishihara, R. K. Jordan, R. D. Rogers, A. L. Rheingold, and G. P. A. Yap, Organometallics, 16, 3314 (1997).
15. a) L. K. Johnson, C. M. Killian, and M. S. Brookhart, J. Am. Chem. Soc., 117, 6414 (1995).
16. b) C. M. Killian, D. J. Temple, L. K. Johnson, and M. S. Brookhart, J. Am. Chem. Soc., 118, 11664 (1996).
17. c) C. Wang, A. Friedrich, T. R. Younkin, R. T. Li, R. H. Grubbs, A. Bansleben, and M. W. Day, Organometallics, 17, 3149 (1998).
18. d) B. L. Small, M. S. Brookhart, and A. A. Bennett, J. Am. Chem. Soc., 120, 4049 (1998).
19. e) G. J. P. Britovsek, V. C. Gibson, B. S. Kimberley, J. Maddox, S. J. McTavish, G. A. Solan, A. P. White, and D. J. Williams, Chem. Commun., 1998, 849.
20. S. Matsui, Y. Tohi, M. Mitani, J. Saito, H. Makio, H. Tanaka, M. Nitabaru, T. Nakano, and T. Fujita, Chem. Lett., in press.
21. 1.
22. 3Al) was added at 25 °C. After the prescribed time, 25 ml of isobutanol was added to terminate the polymerization. To the resulting mixture, 500 ml of methanol was added. After filteration, the polymer was dried in vacuo at 80 °C for 10 h.
23. 4 at even 0 °C under 0.1 MPa pressure, (cat. concentration: 0.8 μM).
24. 0.7. Intrinsic viscosity [η] was measured in decalin at 135 °C using an Ubbelohde viscometer.
25. T. Miyatake, K. Mizuuuma, Y. Seki, and M. Kakugo, Makromol. Chem. Rapid Commun., 10, 349 (1989).