Stress ratio effects on crack opening loads and crack growth rates in aluminum alloy 2024

ASTM Special Technical Publication

Volumn , Issue 1332, 1999, Pages 407-425

  Riddell, William T ^a   Piascik, Robert S ^a  

^a NASA LANGLEY RESEARCH CENTER   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CALCULATIONS; CRACK INITIATION; CRACK PROPAGATION; FATIGUE OF MATERIALS; FRACTOGRAPHY; MATERIALS TESTING; MECHANICAL VARIABLES MEASUREMENT; STRESSES;

CLOSURE MEASUREMENTS; CRACK OPENING LOADS; FATIGUE SURFACE MICROVOID DENSITY; STRESS RATIO EFFECTS;

ALUMINUM ALLOYS;

EID: 0032662485     PISSN: 10403094     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1520/stp14961s     Document Type: Article

References (40)

1. Forman, R.G., Shivakumar, V., Mettu, S.R., Newman, J.C., Jr., "Fatigue Crack Growth Computer Program NASGRO Version 3.0 User's Manual," JSC-22267B, NASA Johnson Space Center, July 1996.
2. Hudson, C.M., "Effect of Stress Ratio on Fatigue Crack Growth in 7075-T6 and 2024-T3 Aluminum Alloy Specimens," NASA TND-5390, 1969.
3. Ibrahim, F.K., "The Effect of Stress Level, Compressive Peak Stress and Maximum Stress Level on Fatigue Behavior of 2024-T3 Aluminum Alloy," Fatigue and Fracture of Engineering Materials and Structures, Vol. 12, No. 1, 1989, pp. 1-8.
4. Bilir, O.G., Harun, M., "Effect of Stress Ratio on the Rate of Growth of Fatigue Cracks in 1100 Al-Alloy," Engineering Fracture Mechanics, Vol. 37, No. 6, 1990, pp. 1203-1206.
5. Phillips, E.P., "The Influence of Crack Closure on Fatigue Crack Growth Thresholds in 2024-T3 Aluminum Alloy," Mechanics of Fatigue Crack Closure, ASTM STP 982, J.C. Newman, Jr., W. Elber, Eds., ASTM Philadelphia, PA, 1988, pp. 505-515.
6. Couper, M.J., Griffiths, J.R., "Effects of Crack Closure and Mean Stress on the Threshold Stress Intensity Factor for Fatigue of an Aluminum Casting Alloy," Fatigue and Fracture of Engineering Materials and Structures, Vol. 13, No. 6, 1990, pp. 615-624.
7. Salivar, G.C., Heine, J.E., Haake, F.K., "The Effect of Stress Ratio on the Near-Threshold Fatigue Crack Growth Behavior of Ti-8Al-1Mo-1V at Elevated Temperature," Engineering Fracture Mechanics, Vol. 32, No. 5, 1989, pp. 807-817.
8. Elber, W., "Fatigue Crack Closure Under Cyclic Tension," Engineering Fracture Mechanics, Vol. 2, 1970, pp. 37-45.
9. Elber, W., "The Significance of Fatigue Crack Closure," Damage Tolerance in Aircraft Structures, ASTM STP 486 American Society of Testing and Materials, 1971, pp. 230-242.
10. J.C. Newman, Elber, W., Eds., Mechanics of Fatigue Crack Closure, ASTM STP 982, American Society of Testing and Materials, Philadelphia, PA, 1988.
11. Vasudevan, A.K., Sadananda, K., Louat, N., "Two Critical Stress Intensity Factors for Threshold Fatigue Crack Propagation," Scripta Metallurgica et Materialia, Vol. 28, 1993, pp. 65-70.
12. Lal, D.N., "A Detailed Physical Analysis of the R-Effect on LEFM Fatigue Crack Growth -II. On the Combined Roles of Growth Mechanisms and Stress Ratio," Engineering Fracture Mechanics, Vol. 55, No. 2, 1996, pp. 289-312.
13. Chen, D.L., Weiss, B., Stickler, R., "The Effective Fatigue Crack Threshold: Significance of the Loading Cycle Below the Crack Opening Load," Fatigue, Vol. 16, 1994, pp. 485-491.
14. Park, D.H., Fine, M.E., "Origin of Crack Closure in the Near-Threshold Fatigue Crack Propagation of Fe and Al-3% Mg," Fatigue Crack Growth Threshold Concepts, Davidson, D.L., Suresh, S., Eds., The Metallurgical Society of AIME, 1983, pp. 146-161.
15. Gerberich, W.W., Yu, W., Esaklul, K., "Fatigue Threshold Studies in FE, Fe-Si and HSLA Steel: Part I. Effect of Strength and Surface Asperities on Closure," Metallurgical Transactions A, Vol. 15A, May 1984, pp. 875-888.
16. Romaniv, O.N., Tkach, A.N., Lenets, Y.N., "Effect of Fatigue Crack Closure on Near-Threshold Crack Resistance of Structural Steels," Fatigue and Fracture of Engineering Materials and Structures, Vol. 10, No. 3, 1987, pp. 203-212.
17. Soboyejo, W.O., Knott, J.F., "Effect of Stress Ratio on Fatigue Crack Propagation in Q1N (HY80) Pressure Vessel Steel," International Journal of Fatigue, Vol. 12, No. 5, 1990, pp. 403-407.
18. Allison, J.E., Ku, R.C., Pompetzki, M.A., "A Comparison of Measurement Methods and Numerical Procedures for the Experimental Characterization of Fatigue Crack Closure," Mechanics of Fatigue Crack Closure, ASTM STP 982, J.C. Newman, Jr., W. Elber, Eds. American Society for Testing and Materials, Philadelphia, PA., 1988, pp. 171-185.
19. Davidson, D.L., "Plasticity Induced Fatigue Crack Closure," Mechanics of Fatigue Crack Closure, ASTM STP 982, J.C. Newman, Jr. and W. Elber, Eds., American Society for Testing and Materials, Philadelphia, PA, 1988, pp. 171-185.
20. Elber, W., "Crack Closure and Crack Growth Measurements in Surface-Flawed Titanium Alloy Ti-6Al-4V," NASA TN D-8010, National Aeronautics and Space Administration, Washington, DC, 1975.
21. Yisheng, W., Schijve, J., "Fatigue Crack Closure Measurements on 2024-T3 Sheet Specimens," Fatigue and Fracture of Engineering Materials and Structures, Vol. 18, No. 9, 1995, pp. 917-921.
22. Chen, D.-L., Weiss, B., Strickler, R., "A New Procedure for Crack Closure," International Journal of Fatigue, Vol. 13, No. 4, 1991, pp. 327-331.
23. Piascik, R.S., Newman, J.C., Jr., Underwood, J.H., "The Extended Compact Tension Specimen," Fatigue and Fracture of Engineering Materials and Structures, Vol. 20, No. 4, 1997, pp. 559-563.
24. User's Reference Manual for Automated Fatigue Crack Growth (Compliance), Fracture Technology Associates, Star Route, Pleasant Valley, PA 18951.
25. Newman, J.C., Jr., "Fracture Analysis of Various Cracked Configurations in Sheet and Plate Materials," Properties Related to Fracture Toughness, ASTM STP 605, American Society for Testing and Materials, 1976, pp. 104-123.
26. Newman, J.C., Jr., "An Evaluation of Plasticity Induced Crack Closure Concept and Measurement Methods," Advances in Fatigue Crack Closure Measurement and Analysis: Second Volume, ASTM STP 1343, R.C. McClung, J.C. Newman, Jr., Eds. American Society for Testing and Materials, 1999.
27. Sutton, M.A., Zhao, W., McNeil, S.R., Helm, J.D., Piascik, R.S., Riddell, W.T., "Local Crack Closure Measurements: Development of a System Using Computer Measurements and a Far-Field Microscope," Advances in Fatigue Crack Closure Measurements and Analysis: Second Volume, ASTM STP 1343, R.C. McClung, J.C. Newman, Jr., Eds., American Society for Testing and Materials, 1999.
28. Sutton, M.A., Chao, Y.J., Lyons, J.S., "Computer Vision Methods for Surface Deformation Measurements in Fracture Mechanics," Novel Experimental Techniques in Fracture Mechanics, AMD-Vol.176, ASME, 1993, pp. 203-217.
29. Sutton, M.A., McNeil, S.R., Jang, J., Babai, M., "Effect of Subpixel Image restoration on Digital Correlation Error Estimates," Optical Engineering, Vol. 27, No. 10, 1988, pp. 870-877.
30. Abdel Mageed, A.M., Pandey, R.K., Chimadurai, R, "Effect of Measurement Location and Fatigue-Loading Parameters on Crack Closure Behavior," Material Science and Engineering, Vol. A150, 1992, pp. 43-50.
31. Ranganathan, N., Bouchet, B., Petit, J., "Fractographic Aspects of the Effect of Environment on the Fatigue Crack Propagation Mechanism in a High-Strength Aluminum Alloy," Fractography of Modern Engineering Materials: Composites and Metals, ASTM STP 948, J.E. Masters, J.J. Au, Eds., American Society for Testing and Materials, Philadelphia, 1987, pp. 424-446.
32. Bretz, P.E., Vasudevan, A. K., Bucci, R.J., Malcom, R.C., "Fatigue Crack Growth Behavior of 7XXX Aluminum Alloys under Simple Variable Amplitude Loading," Fracture Mechanics: Fifteenth Symposium, ASTM STP 833, R.J. Sanford, Ed., American Society for Testing and Materials, Philadelphia, PA, 1984, pp. 242-265.
33. max Threshold Procedures," Fatigue and Fracture of Engineering Materials and Structures, Vol. 19, No. 7, 1996, pp. 949-954.
34. Ray, S.K., Grandt, A.F., Jr., "Comparison of Methods for Measuring Fatigue Crack Closure in a Thick Specimen," Mechanics of Fatigue Crack Closure, ASTM STP 982, J.C. Newman, Jr., W. Elber, Eds., American Society for Testing and Materials, Philadelphia, PA, 1988, pp. 197-213.
35. Dawicke, D.S., Shivakumar, K. N., Newman, J.C., Jr., Grandt, A.F., Jr., "An Inverse Method for the Calculation of Through-Thickness Fatigue Crack Closure Behavior," Fracture Mechanics: Twenty Second Symposium (Vol. II), ASTM STP 1131, S.N. Atluri, J.C. Newman, Jr., I.S. Raju, and J.S. Epstein, Eds., American Society for Testing and Materials, Philadelphia, PA, 1992, pp. 46-57.
36. Chermahini, G.R., Shivakumar, K.N., Newman, J.C., Jr., "Three Dimensional Finite Element Simulation of Fatigue Crack Growth and Closure," Mechanics of Fatigue Crack Closure, ASTM STP 892, J.C. Newman, Jr., W. Elber, Eds. American Society for Testing and Materials, 1988, pp. 398-413.
37. Chermahini, G.R., Shivakumar, K.N., Newman, J.C., Jr., "Fatigue Crack Growth and Closure Behavior of Semi-Circular Elliptical Surface Flaws," International Journal of Fatigue, Vol. 15, No. 4, 1993, pp. 259-263.
38. Seshadri, B.R., Dattaguru, B., Ramamurthy, T.S., "Three Dimensional Elastic-Plastic Finite Element Analysis of Crack Closure in CT Specimen," Contemporary Research in Engineering Science, R.C. Bodra, Ed. Springer-Verlag, Berlin, 1995, pp. 491-515.
39. Riddell, W.T., Piascik, R.S., Sutton, M.A., Zhao, W., McNeill, S.R., Helm, J.D., "Determining Fatigue Crack Opening Loads from Near-Crack-Tip Displacement Measurements," Advances in Fatigue Crack Closure Measurement and Analysis: Second Volume, ASTM STP 1343, R.C. McClung, J.C. Newman, Jr., Eds. American Society for Testing and Materials, 1999.
40. Newman, J.C., Jr., Edwards, P.R., "Short Crack Growth Behavior in an Aluminum Alloy - An AGARD Cooperative Test Programme," AGARD Report No. 732, AGARD, 1988.