Superlattices of semiconductor quantum-size lead sulfide particles prepared by topotactic gas-solid reaction

Advanced Materials

Volumn 10, Issue 9, 1998, Pages 657-661

  Guo, Shouwu ^a   Popovitz Biro, Ronit ^a   Arad, Talmon ^a   Hodes, Gary ^a   Leiserowitz, Leslie ^a   Lahav, Meir ^a  

^a WEIZMANN INSTITUTE OF SCIENCE   (Israel)

Author keywords

[No Author keywords available]

Indexed keywords

CHARGED PARTICLES; DIFFUSION IN SOLIDS; FOURIER TRANSFORM INFRARED SPECTROSCOPY; LEAD COMPOUNDS; NANOSTRUCTURED MATERIALS; NUCLEATION; QUANTUM THEORY; REACTION KINETICS; THIN FILMS; X RAY POWDER DIFFRACTION;

LEAD SULFIDE; TOPOTACTIC GAS SOLID REACTION;

SEMICONDUCTOR SUPERLATTICES;

EID: 0032099819     PISSN: 09359648     EISSN: None     Source Type: Journal    
DOI: 10.1002/(SICI)1521-4095(199806)10:9<657::AID-ADMA657>3.0.CO;2-1     Document Type: Article

References (30)

1. P. V. Braun, P. Osenar, S. I. Stupp, Nature 1996, 380, 325.
2. H. Weller, Angew. Chem. Int. Ed. Engl. 1993, 32, 41.
3. J. H. Pendler, Curr. Opinion Colloid Interface Sci. 1996, 1, 202.
4. N. Kimizuka, T. Kunitake, Adv. Mater. 1996, 8, 89.
5. C. B. Murray, C. R. Kagan, M. G. Bawendi, Science 1995, 270, 1335.
6. P. Osenar, P. V. Braun, S. I. Stupp, Adv. Mater. 1996, 8, 1022.
7. L. Motte, F. Billoudet, E. Lacaze, J. Doin, M. P. Pileni, J. Phys. Chem. B 1997, 94, 3104.
8. W. Shenton, D. Pum, U. B. Sleytr, S. Mann, Nature 1997, 389, 585.
9. G. Friedman, M. Lahav, G. M. J. Schmidt, J. Chem. Soc. Perkin Trans. 2 1974, 428.
10. K. Penzien, G. M. J. Schimdt, Angew. Chem. Int. Ed. Engl. 1969, 8, 608.
11. S. Guo, R. Popovitz-Biro, I. Weissbuch, H. Cohen, G. Hodes, M. Lahav, Adv. Mater. 1998, 10. 121.
12. G. Cao, L, K. Rabenberg, C. M. Nunn, T.E. Mallouk. Chem. Mater. 1991, 3, 149.
13. E. Stenhagen, E. von Sydow, Ark Kemi 1953, n. 309.
14. These d-spacings are also larger than those observed in all four polymorphs of the pure carboxylic acids [13] and therefore exclude the possibility of recrystallization of the pure acids.
15. Studies on the design of superlattices of CdS by applying the present method to longer chains or other systems are currently in progress.
16. 2 and its collapse pressure is 40 mN/m. The structure of this film is currently being determined by Dr. I. Weissbuch, using grazing incidence X-ray diffraction.
17. The packing arrangements of the 3D crystals are very similar to those of the films and the generated PbS particles are also arranged in superlattices.
18. 2+ form both 1:1 and 1:2 complexes with carboxylates through specific covalent binding. The lead 1:1 complex is more stable than that of cadmium [23].
19. M. Yazdanian, H. Yu. G. Zografi. Langmuir 1992, 8, 630.
20. R. S. Urquhart, D. N. Furlong. H. Mansur, F. Grieser, K. Tanaka. Y. Okahata. Langmuir 1994, 10, 899.
21. X. Peng. S. Guan, X. Chai, Y. Jiang, T. Li, J. Phys. Chem. 1992, 96, 3170.
22. T. Yamaki, K. Asai, K. Ishigure, Chem. Phys. Lett. 1997, 273, 376.
23. J. A. Zasadzinski, R. Viswanathan, L. Madsen, J. Garnaes. D. K. Schwartz, Science 1994, 263, 1726.
24. 2S at low pressure has been reported to yield single layers of PbS between the organic acids
25. However, the formation of such layers requires either a change of the d-spacings between the layers or broadening of the (001) Bragg peaks, neither of which has been observed.
26. B. A. Jones, J. S. Bradshaw, M. Nishioka, M. L. Lee, J. Org. Chem. 1984, 49, 4947.
27. J. Majewski, L. Margulis, I. Weissbuch, R. Popovitz-Biro, T. Arad, Y. Talmon, M. Lahav, L. Leiserowitz, Adv. Mater. 1995, 7, 26.
28. Enzyme Structure (Eds: C. H. W. Hirs, S. N. Timashoff), Academic, San Diego. CA 1978, Vol. XLIX, p. 39.
29. This value is in agreement with data obtained for 3 nm spherical crystals, of approximately the same volume as our particles [29].
30. Y. Wang, A. Suna, W. Mahler, R. Kasowski, J. Chem. Phys. 1987, 87, 7315.