Porous Amorphous Chalcogenides as Selective Adsorbents for Heavy Metals

Chemistry of Materials

Volumn 27, Issue 18, 2015, Pages 6189-6192

  Hassanzadeh Fard, Zohreh ^a   Islam, Saiful M ^a   Kanatzidis, Mercouri G ^a  

^a NORTHWESTERN UNIVERSITY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ALKALI METALS; HEAVY METALS;

AMORPHOUS CHALCOGENIDE; AMORPHOUS STRUCTURES; GENERAL EQUATIONS; INORGANIC SALTS; LIQUID EXTRACTION; NOMINAL COMPOSITION; SELECTIVE ADSORBENTS;

CHALCOGENIDES;

EID: 84942279570     PISSN: 08974756     EISSN: 15205002     Source Type: Journal    
DOI: 10.1021/acs.chemmater.5b02805     Document Type: Article

References (35)

1. Adam, J. L.; Zhang, X. Chalcogenide Glasses: Preparation, Properties and Applications; Woodhead Publishing: Cambridge, UK, 2013.
2. 8: A Wide Bandgap Phase-Change Material for Ultra High Density Rewritable Information Storage Adv. Mater. 2003, 15, 1428-1431 10.1002/adma.200304994
3. Wang, A.; Boolchand, P.; Micoulaut, M. Glass structure, rigidity transitions and the intermediate phase in the Ge-As-Se ternary Europhys. Lett. 2000, 52, 633-639 10.1209/epl/i2000-00485-9
4. Balan, V.; Vigreux, C.; Pradel, A.; Ribes, M. Waveguides based upon chalcogenide glasses J. Optoelectron. Adv. Mater. 2001, 3, 367-372
5. Etienne, S.; Perez, J.; Peytavin, S.; Ribes, M. Degrees of freedom and ionic mobility in silver chalcogenide glasses J. Solid State Chem. 1991, 92, 27-38 10.1016/0022-4596(91)90239-E
6. 3 pseudobinary amorphous thin films for an optical disk memory J. Appl. Phys. 1991, 69, 2849-2856 10.1063/1.348620
7. Seddon, A. B. Chalcogenide glasses: a review of their preparation, properties and applications J. Non-Cryst. Solids 1995, 184, 44-50 10.1016/0022-3093(94)00686-5
8. Sanghera, J. S.; Aggarwal, I. D. Active and passive chalcogenide glass optical fibers for IR applications: a review J. Non-Cryst. Solids 1999, 256-257, 6-16 10.1016/S0022-3093(99)00484-6
9. Savage, J. A.; Nielsen, S. Preparation of Glasses Transmitting in the Infrared between 8 and 15 microns Phys. Chem. Glasses 1964, 5, 82-86
10. Varshneya, K. Fundamentals of Inorganic Glasses; Academic Press: Boston, London, Tokyo, 1994; p 7.
11. Lezal, D.; Pedlikova, J.; Zavadila, J. Chalcogenide glasses for optical and photonics applications Chalcogenide Lett. 2004, 1, 11-15
12. Bureau, B.; Zhang, X. H.; Smektala, F.; Adam, J. L.; Troles, J.; Ma, H. L.; Boussard-Plèdel, C.; Lucas, J.; Lucas, P.; Le Coq, D.; Riley, M. R.; Simmons, J. H. Recent advances in chalcogenide glasses J. Non-Cryst. Solids 2004, 345&346, 276-283 10.1016/j.jnoncrysol.2004.08.096
13. 8 Inorg. Chem. 2012, 51, 7963-7965 10.1021/ic301276y
14. Kanatzidis, M. G. Molten alkali-metal polychalcogenides as reagents and solvents for the synthesis of new chalcogenide materials Chem. Mater. 1990, 2, 353-363 10.1021/cm00010a009
15. Gobeltz, N.; Demortier, A.; Lelieur, J. P. Identification of the Products of the Reaction between Sulfur and Sodium Carbonate Inorg. Chem. 1998, 37, 136-138 10.1021/ic970962f
16. 2 evolution. The mixture was heated gradually to 200 °C where it was kept for 5 h before being successfully brought to 800 °C. It was kept at 800 °C for 8 h. A red glassy ingot was obtained by cooling at a rate of 40 °C/h to room temperature; method.
17. -4 Torr) in a 13 mm (OD) carbon coated fused-silica tube and heated (80 °C/h) to 800 °C. It was kept there for 24 h, followed by cooling to room temperature at 40 °C/h; method.
18. 6 based on EDS analyses. The product is a red ingot.
19. 2S (1 mmol, 0.2205 g), S (5 mmol, 0.1620 g), Sn (1 mmol, 0.1187 g), and Sb (2 mmol, 0.2435 g) in accordance to the conditions and heating profile for the synthesis compound 1; method.
20. -4 Torr) in a 13 mm (OD) carbon coated fused-silica tube and heated (80 °C/h) to 800 °C for 24 h, followed by cooling to room temperature at 40 °C/h. The product is a dark red-black ingot.
21. Manos, M. J.; Kanatzidis, M. G. Sequestration of Heavy Metals from Water with Layered Metal Sulfides Chem.-Eur. J. 2009, 15, 4779-4784 10.1002/chem.200900353
22. 6 (KMS-1) J. Am. Chem. Soc. 2009, 131, 6599-6607 10.1021/ja900977p
23. Manos, M. J.; Ding, N.; Kanatzidis, M. G. Layered metal sulfides: Exceptionally selective agents for radioactive strontium removal Proc. Natl. Acad. Sci. U. S. A. 2008, 105, 3696-3699 10.1073/pnas.0711528105
24. 6 (x = 0.5-1) (KMS-2) Relevant to Nuclear Waste Remediation Chem. Mater. 2013, 25, 2116-2127 10.1021/cm400699r
25. 6 (KMS-2) Chem. Mater. 2015, 27, 1925-1928 10.1021/acs.chemmater.5b00374
26. Mertz, J. L. Synthesis and ion-exchange of framework and layered chalcogenide compounds for environmental remediation. Ph.D. thesis, Northwestern University, Evanston, IL, 2012.
27. 2/InSb interface as determined by X-ray photoelectron spectroscopy J. Appl. Phys. 1981, 52, 3509-3514 10.1063/1.329129
28. Morgan, W. E.; Van Wazer, J. E. Binding energy shifts in the x-ray photoelectron spectra of a series of related Group IVa compounds J. Phys. Chem. 1973, 77, 964-969 10.1021/j100626a023
29. Patai, S. The chemistry of the thiol group; Wiley: London, 1974.
30. 6 (x = 0.11-0.25): A Novel Reusable Sorbent for Highly Specific Mercury Capture Under Extreme pH Conditions Adv. Funct. Mater. 2009, 19, 1087-1092 10.1002/adfm.200801563
31. 20 Chem.-Eur. J. 2007, 13, 51-58 10.1002/chem.200600892
32. Fryxel, G. A.; Lin, Y.; Fiskum, S.; Birnbaum, J. C.; Wu, H. Actinide Sequestration Using Self-Assembled Monolayers on Mesoporous Supports Environ. Sci. Technol. 2005, 39, 1324-1331 10.1021/es049201j
33. 10 (A = K, Rb, Cs) J. Solid State Chem. 2015, 221, 426-432 10.1016/j.jssc.2014.10.022
34. 2O: High Ion-Exchange Capacity, Size Discrimination, and Selectivity for Cs Ions Chem. Mater. 2007, 19, 3867-3869 10.1021/cm071179g
35. Ding, N.; Kanatzidis, M. G. Selective Incarceration of Caesium Ions by Venus Flytrap Action of a Flexible Framework Sulfide Nat. Chem. 2010, 2, 187-191 10.1038/nchem.519