3D carbon/cobalt-nickel mixed-oxide hybrid nanostructured arrays for asymmetric supercapacitors

Small

Volumn 10, Issue 14, 2014, Pages 2937-2945

  Zhu, Jianhui ^a,b   Jiang, Jian ^a,b   Sun, Zhipeng ^a   Luo, Jingshan ^a   Fan, Zhanxi ^c   Huang, Xintang ^b   Zhang, Hua ^c   Yu, Ting ^a,d  

^a NANYANG TECHNOLOGICAL UNIVERSITY   (Singapore)

^b CENTRAL CHINA NORMAL UNIVERSITY   (China)

^c NANYANG TECHNOLOGICAL UNIVERSITY   (Singapore)

^d NATIONAL UNIVERSITY OF SINGAPORE   (Singapore)

Author keywords

asymmetric supercapacitors; cobalt; electrodes; hierarchical materials; nickel; oxides

Indexed keywords

COBALT; ELECTROCHEMICAL ELECTRODES; ELECTRODES; FABRICATION; LIGHT EMITTING DIODES; LITHIUM COMPOUNDS; NETWORK ARCHITECTURE; NICKEL; OXIDES;

ASYMMETRIC SUPERCAPACITOR; ELECTROCHEMICAL PERFORMANCE; ELECTRODE ARCHITECTURE; HIERARCHICAL ARCHITECTURES; HIERARCHICAL MATERIALS; HIGH SPECIFIC SURFACE AREA; SUPERCAPACITOR APPLICATION; SUPERCAPACITOR ELECTRODES;

ELECTROLYTIC CAPACITORS;

EID: 84904423699     PISSN: 16136810     EISSN: 16136829     Source Type: Journal    
DOI: 10.1002/smll.201302937     Document Type: Article

References (61)

1. a) P. Simon, Y. Gogotsi, Nat. Mater. 2008, 7, 845
2. b) J. R. Miller, P. Simon, Science 2008, 321, 651
3. c) J. Jiang, Y. Y. Li, J. P. Liu, X. T. Huang, C. Z. Yuan, X. W. Lou, Adv. Mater. 2012, 24, 5166.
4. a) X. H. Lu, M. H. Yu, G. M. Wang, T. Zhai, S. L. Xie, Y. C. Ling, Y. X. Tong, Y. Li, Adv. Mater. 2013, 25, 267
5. b) X. Xiao, T. Q. Li, P. H. Yang, Y. Gao, H. Y. Jin, W. J. Ni, W. H. Zhan, X. H. Zhang, Y. Z. Cao, J. W. Zhong, L. Gong, W.-C. Yen, W. J. Mai, J. Chen, K. F. Huo, Y. L. Chuen, Z. L. Wang, J. Zhou, ACS Nano 2012, 6, 9200.
6. a) Y. P. Fu, X. Cai, H. W. Wu, Z. B. Lv, S. C. Hou, M. Peng, X. Yu, D. C. Zou, Adv. Mater. 2012, 24, 5713
7. b) L. H. Bao, X. D. Li, Adv. Mater. 2012, 24, 3246.
8. a) J. Jiang, J. P. Liu, W. W. Zhou, J. H. Zhu, X. T. Huang, X. Y. Qi, H. Zhang, T. Yu, Energy Environ. Sci. 2011, 4, 5000
9. b) L. Q. Mai, F. Yang, Y. L. Zhao, X. Xu, L. Xu, Y. Z. Luo, Nat. Commun. 2011, 2, 381
10. c) C. Guan, X. L. Li, Z. L. Wang, X. H. Cao, C. Soci, H. Zhang, H. J. Fan, Adv. Mater. 2012, 24, 4186.
11. a) J. Xu, Q. F. Wang, X. W. Wang, Q. Y. Xiang, B. Liang, D. Chen, G. Z. Shen, ACS Nano 2013, 7, 5432
12. b) J. Yan, Z. J. Fan, W. Sun, G. Q. Ning, T. Wei, Q. Zhang, R. F. Zhang, L. J. Zhi, F. Wei, Adv. Funct. Mater. 2012, 22, 2632
13. c) J. T. Zhang, J. W. Jiang, H. L. Li, X. S. Zhao, Energy Environ. Sci. 2011, 4, 4009.
14. a) P.-C. Chen, G. Z. Shen, Y. Shi, H. T. Chen, C. W. Zhou, ACS Nano 2012, 4, 4403
15. b) Z. P. Sun, S. Firdoz, E. Y.-X. Yap, L. Li, X. M. Lu, Nanoscale 2013, 5, 4379.
16. a) X. Zhao, L. L. Zhang, S. Murali, M. D. Stoller, Q. H. Zhang, Y. W. Zhu, R. S. Ruoff, ACS Nano 2012, 6, 5404
17. b) Y. G. Wang, Z. S. Hong, M. D. Wei, Y. Y. Xia, Adv. Funct. Mater. 2012, 22, 5185.
18. a) C. Zhou, Y. W. Zhang, Y. Y. Li, J. P. Liu, Nano Lett. 2013, 13, 2078
19. b) Z.-S. Wu, Y. Sun, Y.-Z. Tan, S. B. Yang, X. L. Feng, K. Müllen, J. Am. Chem. Soc. 2012, 134, 19532.
20. a) C. Z. Yuan, J. Y. Li, L. R. Hou, X. G. Zhang, L. F. Shen, X. W. Lou, Adv. Funct. Mater. 2012, 22, 4592
21. b) X. Wang, A. Sumboja, M. F. Lin, J. Yan, P. S. Lee, Nanoscale 2012, 4, 7266.
22. a) C.-C. Hu, L. C. Chen, K.-H. Chang, J. Power Sources 2013, 221, 128
23. b) W. W. Zhou, J. P. Liu, T. Chen, K. S. Tan, X. T. Jia, Z. Q. Luo, C. X. Cong, H. P. Yang, C. M. Li, T. Yu, Phys. Chem. Chem. Phys. 2011, 13, 14462.
24. a) Z. Tang, C.-H. Tang, H. Gong, Adv. Funct. Mater. 2012, 22, 1272
25. b) D.-W. Wang, F. Li, H.-M. Cheng, J. Power Sources 2008, 185, 1563
26. c) J. P. Liu, C. W. Cheng, W. W. Zhou, H. X. Li, H. J. Fan, Chem. Commun. 2011, 47, 3436.
27. a) H. L. Wang, Q. M. Gao, L. Jiang, Small 2011, 7, 12454
28. b) H. Jiang, J. Ma, C. Z. Li, Chem. Commun. 2012, 48, 4465
29. c) X. H. Liu, R. Z. Ma, Y. S. Bando, T. Sasaki, Adv. Mater. 2012, 24, 2148.
30. a) J. Chang, J. Sun, C. H. Xu, H. Xu, L. Gao, Nanoscale 2012, 4, 6786
31. b) C. H. Tang, Z. Tang, H. Gong, J. Electrochem. Soc. 2012, 159, A651.
32. a) X. F. Wang, B. Liu, Q. F. Wang, W. F. Song, X. J. Hou, Y.-B. Cheng, G. Z. Shen, Adv. Mater. 2013, 25, 1479
33. b) J. Jiang, Y. Y. Li, J. P. Liu, X. T. Huang, Nanoscale 2011, 3, 45
34. c) J. Y. Ji, L. L. Zhang, H. X. Ji, Y. Li, X. Zhao, X. Bai, X. B. Fan, F. B. Zhang, R. S. Ruoff, ACS Nano 2013, 7, 6237.
35. a) E. Lyyamperumal, S. Y. Wang, L. M. Dai, ACS Nano 2012, 6, 5259
36. b) J. T. Li, W. Zhao, F. Q. Huang, A. Manivanan, N. Q. Wu, Nanoscale 2011, 3, 5103
37. c) J. H. Zhong, A.-L. Wang, G.-R. Li, J.-W. Wang, Y.-N. Ou, Y. X. Tong, J. Mater. Chem. 2012, 22, 5656.
38. a) Y. S. Luo, J. Jiang, W. W. Zhou, H. P. Yang, J. S. Luo, X. Y. Qi, H. Zhang, D. Y. W. Yu, C. M. Li, T. Yu, J. Mater. Chem. 2012, 22, 8634
39. b) J. S. Luo, X. H. Xia, Y. S. Luo, C. Guan, J. L. Liu, X. Y. Qi, C. F. Ng, T. Yu, H. Zhang, H. J. Fan, Adv. Energy Mater. 2013, 3, 737.
40. a) H. G. Zhang, X. D. Yu, P. V. Braun, Nat. Nanotechnol. 2011, 6, 277
41. b) J. P. Liu, J. Jiang, C. W. Cheng, H. X. Li, J. X. Zhang, H. Gong, H. J. Fan, Adv. Mater. 2011, 23, 2076.
42. a) J. H. Zhu, J. Jiang, Y. M. Feng, G. X. Meng, H. Ding, X. T. Huang, ACS Appl. Mater. Interfaces 2013, 5, 2634
43. b) J. Jiang, J. H. Zhu, Y. M. Feng, J. P. Liu, X. T. Huang, Chem. Commun. 2012, 48, 7471.
44. J. Jiang, J. P. Liu, X. T. Huang, Y. Y. Li, R. M. Ding, X. X. Ji, Y. Y. Hu, Q. B. Chi, Z. H. Zhu, Cryst. Growth Des. 2010, 10, 70.
45. H.-C. Chien, W.-Y. Cheng, Y.-H. Wang, S.-Y. Lu, Adv. Funct. Mater. 2012, 22, 5038.
46. J. H. Zhu, J. Jiang, J. P. Liu, R. M. Ding, Y. Y. Li, H. Ding, Y. M. Feng, G. M. Wei, X. T. Huang, RSC Adv. 2011, 1, 1020.
47. G. X. Hu, C. H. Tang, C. X. Li, H. M. Li, Y. Wang, H. Gong, J. Electrochem. Soc. 2011, 158, A695.
48. a) B. Liu, D. S. Tan, X. F. Wang, D. Chen, G. Z. Shen, Small 2013, 9, 1998
49. b) J. Jiang, J. P. Liu, R. M. Ding, J. H. Zhu, Y. Y. Li, A. Z. Hu, X. Li, X. T. Huang, ACS Appl. Mater. Interfaces 2011, 3, 99.
50. a) B. Liu, J. Zhang, X. F. Wang, G. Chen, C. W. Zhou, G. Z. Shen, Nano Lett. 2012, 12, 3005
51. b) W. W. Zhou, J. P. Liu, T. Chen, K. S. Tan, X. T. Jia, Z. Q. Luo, C. X. Cong, H. P. Yang, C. M. Li, T. Yu, Phys. Chem. Chem. Phys. 2011, 13, 14462.
52. L. L. Zhang, X. Zhao, H. X. Ji, M. D. Stoller, L. F. Lai, S. Murali, S. Mcdonnell, B. Cleveger, R. M. Wllace, R. S. Ruoff, Energy Environ. Sci. 2012, 5, 9618.
53. Q. F. Wang, X. F. Wang, B. Liu, G. Yu, X. J. Hou, D. Chen, G. Z. Shen, J. Mater. Chem. A 2013, 1, 2468.
54. J. P. Liu, C. W. Cheng, W. W. Zhou, H. X. Li, H. J. Fan, Chem. Commun. 2011, 47, 3436.
55. Y. Y. Li, Z. S. Li, P. K. Shen, Adv. Mater. 2013, 25, 2474.
56. D.-W. Wang, F. Li, M. Liu, G. Q. Lu, H. M. Cheng, Angew. Chem. Int. Ed. 2008, 47, 373.
57. C. J. Yu, C. Masarapu, J. P. Rong, B. Q. Wei, H. Q. Jiang, Adv. Mater. 2009, 21, 4793.
58. H. L. Wang, Y. Y. Liang, T. Mirfakhrai, Z. Chen, H. S. Casalongue, H. J. Dai, Nano Res. 2011, 4, 729.
59. H. L. Wang, C. M. B. Holt, Z. Li, X. H. Tan, B. S. Amirkhiz, Z. W. Xu, B. C. Olsen, T. Stephenson, D. Mitlin, Nano Res. 2012, 5, 605.
60. H. Inoue, Y. Namba, E. Higuchi, J. Power Sources 2010, 195, 6239.
61. C. Guan, J. P. Liu, C. W. Cheng, H. X. Li, X. L. Li, W. W. Zhou, H. Zhang, H. J. Fan, Energy Environ. Sci. 2011, 4, 4496.