Weibull strength statistics of hydrothermally aged 3 mol% yttria-stabilised tetragonal zirconia

Ceramics International

Volumn 40, Issue 8 PART B, 2014, Pages 12777-12782

  Marro, F G ^a   Mestra, A ^a   Anglada, M ^a  

^a UNIVERSITAT POLITÈCNICA DE CATALUNYA   (Spain)

Author keywords

C. Fracture; C. Strength; Degradation; Weibull; Zirconia

Indexed keywords

DEGRADATION; FRACTURE; STRENGTH OF MATERIALS; SURFACE DEFECTS; YTTRIA STABILIZED ZIRCONIA; YTTRIUM ALLOYS; ZIRCONIA;

C. STRENGTH; FOUR-POINT BENDING TEST; FRACTURE STATISTICS; HYDROTHERMAL DEGRADATION; TETRAGONAL ZIRCONIA; WEIBULL; WEIBULL STATISTICS; YTTRIA-STABILIZED;

WEIBULL DISTRIBUTION;

EID: 84903890345     PISSN: 02728842     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ceramint.2014.04.131     Document Type: Article

References (17)

1. J. Chevalier, L. Gremillard, A.V. Virkar, and D.R. Clarke The tetragonal-monoclinic transformation in zirconia: lessons learned and future trends J. Am. Ceram. Soc. 92 2009 1901 1920
2. J. Chevalier, L. Gremillard, and S. Deville Low-temperature degradation of zirconia and implications for biomedical implants Annu. Rev. Mater. Res. 37 2007 1 32
3. Y. Gaillard, E. Jimenez-Piqué, F. Soldera, F. Mücklich, and M. Anglada Quantification of hydrothermal degradation in zirconia by nanoindentation Acta Mater. 56 2008 4206
4. T. Sato, T. Ohtaki, T. Fukushima, T. Endo, and M. Shimada Mechanical properties and termal stability of yttria-doped tetragonal zirconia polycrystals with diffused ceria in the surface Mater. Res. Soc. Symp. Proc. 78 1987 147
5. F.G. Marro, R. Chintapalli, P. Hvizdos, F. Soldera, F. Mücklich, and M. Anglada Study of near surface changes in yttria-doped tetragonal zirconia after low temperature degradation Int. J. Mater. Res. 100 2009 92 96
6. T. Kosmac, C. Oblak, P. Jevnikar, N. Funduk, and L. Marion Strength and reliability of surface treated Y-TZP dental ceramics J. Biomed. Mater. Res. 53 4 2000 304 313
7. 3 nanocomposite and Y-TZP as dental restoratives J. Biomed. Mater. Res. Part B: Appl. Biomater. 2008 492 598
8. C. Piconi, and G. Maccauro Zirconia as a ceramic biomaterial Biomaterials 20 1999 1 25
9. H. Papanagiotou, S. Morgano, R. Giordano, and R. Pober In vitro evaluation of low-temperature aging effects and finishing procedures on the flexural strength and structural stability of Y-TZP dental ceramics J. Prosthet. Dent. 96 2006 154 164
10. C. Piconi, W. Burger, H.G. Richter, A. Cittadini, G. Maccaureo, V. Covacci, N. Bruzzese, G.A. Ricci, and E. Marmo Y-TZP ceramics for artificial joint replacements Biomaterials 19 1998 1489 1494
11. D. Casellas, J. Alcalá, L. Llanes, and M. Anglada Indentation precracking of Y-TZP: implications to R-curve and strength Mater. Sci. Eng. A 245 1998 267 276
12. ASTM C1161-02, Standard test method for flexural strength of advanced ceramics at ambient temperature.
13. ASTM C1683-08, Standard practice for size scaling of tensile strengths using Weibull statistics for advanced ceramics.
14. ASTM C1239-00, Standard practice for reporting uniaxial strength data and estimating Weibull distribution parameters for advanced ceramics.
15. 2 polycrystals S. Somiya, N. Yamamoto, H. Yanagida., Science and Technology of Zirconia III 1988 American Ceramic Society Westerville, OH 537 544
16. J.C. Newman, and I.S. Raju Stress Intensity Factors Equations for Cracks in Three Dimensional Finite Bodies Subjected to Tension and Bending Loads 1984 NASA Langley Research Center Hampton, VA (NASA Technical Memorandum 85793)
17. J. Eichler, U. Eisele, and J. Rödel Mechanical properties of monoclinic zirconia J. Am. Ceram. Soc. 87 7 2004 1401 1403