Improvement of dimensional stability of wood by in situ synthesis of organo-montmorillonite: Preparation and properties of modified Southern pine wood

Holzforschung

Volumn 68, Issue 1, 2014, Pages 29-36

  Wang, Wang ^a   Zhu, Yuan ^a   Cao, Jinzhen ^a   Liu, Ru ^a  

^a BEIJING FORESTRY UNIVERSITY   (China)

Author keywords

Anti swelling efficiency; Compression strength; Didecyldimethylammonium chloride; Dimensional stability; Organo montmorillonite; Shore hardness; Sodium montmorillonite; Two step process; Volumetric swelling rate; Water absorption rate; Wood

Indexed keywords

ANTI-SWELLING EFFICIENCIES; COMPRESSION STRENGTH; DIDECYLDIMETHYLAMMONIUM CHLORIDE; ORGANO-MONTMORILLONITE; SHORE HARDNESS; SODIUM MONTMORILLONITE; TWO-STEP PROCESS; VOLUMETRIC SWELLING; WATER ABSORPTION RATES;

CHLORINE COMPOUNDS; CLAY MINERALS; COMPRESSIVE STRENGTH; DIMENSIONAL STABILITY; FOURIER TRANSFORM INFRARED SPECTROSCOPY; SILICATES; SODIUM; X RAY DIFFRACTION; X RAY SPECTROSCOPY;

WOOD;

CHLORINE COMPOUNDS; COMPRESSION STRENGTH; DIMENSIONAL STABILITY; SILICATES; SODIUM; WATER ABSORPTION; WOOD; X RAY DIFFRACTION; X RAY SPECTROSCOPY;

EID: 84900150951     PISSN: 00183830     EISSN: 1437434X     Source Type: Journal    
DOI: 10.1515/hf-2013-0038     Document Type: Article

References (39)

1. Anandhan, S., Patil, H.G., Babu, R.R. (2011) Characterization of poly(ethylene-co-vinyl acetate-co-carbon monoxide)layered silicate clay hybrids obtained by melt mixing. J. Mater. Sci. 46:7423-7430.
2. Anderson, S., Serimaa, R., Paakkari, T., Saranpaa, P., Pesonen, E. (2003) Crystallinity of wood and the size of cellulose crystallites in Norway spruce (Picea abies). J. Wood Sci. 49:531-537.
3. Borysiak, S., Doczekalska, B. (2005) X-ray diffraction study of pine wood treated with NaOH. Fibres Textiles Eastern Europe 13:87-89.
4. Bryne, L.E., Walinder, M.E.P. (2010) Ageing of modified wood. Part 1: wetting properties of acetylated, furfurylated, and thermally modified wood. Holzforschung 64:295-304.
5. Cai, X., Riedl, B., Zhang, S. (2007a) Formation and properties of nanocomposites made up from solid aspen wood, melamineurea-formaldehyde, and clay. Holzforschung 61:148-154.
6. Cai, X., Zhang, S., Wan, H. (2007b) Effects of nanofillers on water resistance and dimensional stability of solid wood modified by melamine-urea-formaldehyde resin. Wood Fiber Sci. 39:307-318.
7. Cai, X., Riedl, B., Wan, H., Zhang, S. (2010) Montmorillonite nanoparticle distribution and morphology in melamine-ureaformaldehyde resin-impregnated wood nanocomposites. Wood Fiber Sci. 42:285-291.
8. Chaudhary, D., Liu, H. (2013) Ultrasonic treatment and synthesis of sugar alcohol modified Na+-montmorillonite clay. Ultrason. Sonochem. 20:63-68.
9. Deka, M., Gindl, W., Wimmer, R. (2007) Chemical modification of Norway spruce (Picea abies (L) Karst) wood with melamine formaldehyde resin. Indian J. Chem. Technol. 14:134-138.
10. Devi, R.R., Manabendra, M., Maji, T.K. (2012) Physical properties of simul (red-silk cotton) wood (Bombax ceiba L.) chemically modified with styrene acrylonitrile co-polymer and nanoclay. Holzforschung 66:365-371.
11. Dong, Y., Bhattacharyya, D. (2012) Investigation on the competing effects of clay dispersion and matrix plasticisation for polypropylene/clay nanocomposites. Part I morphology and mechanical properties. J. Mater. Sci. 47:3900-3912.
12. Dun, L., Sur, G. (2011) Comparison of Na+-MMT and Ca2+-MMT for the preparation and characterization of poly(ethylene-coacrylic acid) ionomer/MMT nanocomposites. Macromol. Res. 19:1035-1040.
13. Eranna, P.B., Pandey, K.K. (2012) Solvent-free chemical modification of wood by acetic and butyric anhydride with iodine as catalyst. Holzforschung 66:967-971.
14. Fang, C., Yu, R., Zhang, Y., Hu, J., Zhang, M., Mi, X. (2012) Combined modification of asphalt with polyethylene packaging waste and organophilic montmorillonite. Polym. Test. 31:276-281.
15. Gabrielli, C., Kamke, F.A. (2008) Treatment of chemically modified wood with VTC process to improve dimensional stability. For. Prod J. 58:82-86.
16. Gawad, A.A., Esawi, A.M.K., Ramadan, A.R. (2010) Structure and properties of nylon 6-clay nanocomposites effect of temperature and reprocessing. J. Mater. Sci. 45:6677-6684.
17. Gindl, W., Zargar-Yaghubi, F., Wimmer, R. (2003) Impregnation of softwood cell walls with melamine-formaldehyde resin. Bioresour. Technol. 87:325-330.
18. Hill, C.A.S. (2008) The reduction in the fibre saturation point of wood due to chemical modification using anhydride reagents: a reappraisal. Holzforschung 62:423-428.
19. Hoadley, R.B. Understanding Wood. The Taunton Press, Newtown, CT, 2000.
20. Lin, K., Jeng, U., Lin, K. (2011) Adsorption and intercalation processes of ionic surfactants on montmorillonite associated with their ionic charge. Mater. Chem. Phys. 131:120-126.
21. Liu, R., Cao, J., Luo, S., Wang, X. (2013a) Effects of two types of clay on physical and mechanical properties of poly(lactic acid)/ wood flour composites at various wood flour contents. J. Appl. Polym. Sci. 127:2566-2573.
22. Liu, R., Cao, J., Ou-Yang, L. (2013b) Degradation of wood flour/poly (lactic acid) composites reinforced by coupling agents and organo- montmorillonite in a compost test. Wood Fiber Sci. 45:105-118.
23. Lv, W., Zhao, G., Xue, Z. (2006) Preparation and characterization of wood montmorillonite nanocomposites. For. Stud. China 8:35-40.
24. Park, H.M., Lee, W.K., Park, C.Y., Cho, W.J., Ha, C.S. (2003) Environmentally friendly polymer hybrids. Part I: mechanical, thermal, and barrier properties of thermoplastic starch clay nanocomposites. J. Mater. Sci. 38:909-915.
25. Pfriem, A., Zauer, M., Wagenführ, A. (2010) Alteration of the unsteady sorption behaviour of maple (Acer pseudoplatanus L.) and spruce (Picea abies (L.) Karst.) due to thermal modification. Holzforschung 64:235-241.
26. Ran, Q., Zou, H., Wu, S., Shen, J. (2007) Study on thermoplastic polyurethane/montmorillonte nanocomposites. Polym. Composite 29:119-124.
27. Rowell, R. The chemistry of Solid Wood. American Chemical Society, Washington, DC, 1984.
28. Stanzl-Tschegg, S., Beikircher, W., Loidl, D. (2009) Comparison of mechanical properties of thermally modified wood at growth ring and cell wall level by means of instrumented indentation tests. Holzforschung 63:443-448.
29. Strawhecker, K.E., Manias, E. (2000) Structure and properties of poly(vinyl alcohol)/Na+ montmorillonite nanocomposites. Chem. Mater. 12:2943-2949.
30. Thygesen, L.G., Tang Engelund, E., Hoffmeyer, P. (2010) Water sorption in wood and modified wood at high values of relative humidity. Part I: results for untreated, acetylated, and furfurylated Norway spruce. Holzforschung 64:315-323.
31. Tuong, V.M., Li, J. (2010) Effect of heat treatment on the change in color and dimensional stability of acacia hybrid wood. Bioresources 5:1257-1267.
32. Varghese, S., Karger-Kocsis, J., Gatos, K.G. (2003) Melt compounded epoxidized natural rubber/layered silicate nanocomposites: structure-properties relationships. Polymer 44:3977-3983.
33. Windeisen, E., Bächle, H., Zimmer, B., Wegener, G. (2009) Relations between chemical changes and mechanical properties of thermally treated wood. 10th EWLP, Stockholm, Sweden, August 25-28, 2008. Holzforschung 63:773-778.
34. Xiao, Z., Xie, Y., Militz, H., Mai, C. (2010) Effect of glutaraldehyde on water related properties of solid wood. Holzforschung 64:483-488.
35. Xu, W., Liang, G., Zhai, H., Tang, S., Hang, G., Pan, W. (2003) Preparation and crystallization behaviour of PP/PP-g-MAH/ Org-MMT nanocomposite. Eur. Polym. J. 39:1467-1474.
36. Yu, X., Sun, D., Li, X. (2011) Preparation and characterization of urea-formaldehyde resin-sodium montmorillonite intercalation-modified poplar. J. Wood Sci. 57:501-506.
37. Zelinka, S., Glass, S. (2010) Water vapor sorption isotherms for southern pine treated with several waterborne preservatives. J. Test. Eval. 38:1-5.
38. Zeng, Q., Wang, D., Yu, A., Lu, G. (2002) Synthesis of polymermontmorillonite nanocomposites by in situ intercalative polymerization. Nanotechnology 13:549-553.
39. Zhang, X., Xu, R., Wu, Z., Zhou, C. (2003) The synthesis and characterization of polyurethane/clay nanocomposites. Polym. Int. 52:790-794.