ZnO multi-branched microflowers: Fabrication and temperature-dependent photoluminescence properties

Science of Advanced Materials

Volumn 6, Issue 1, 2014, Pages 198-202

  Ding, Meng ^a   Zhao, Dongxu ^b   Yao, Bin ^c   Xu, Xijin ^a  

^a UNIVERSITY OF JINAN   (China)

^b CHANGCHUN INSTITUTE OF OPTICS   (China)

^c JILIN UNIVERSITY   (China)

Author keywords

Chemisical vapor deposition; Multi branched microflowers; Photoluminescence; ZnO

Indexed keywords

EID: 84897018086     PISSN: 19472935     EISSN: 19472943     Source Type: Journal    
DOI: 10.1166/sam.2014.1700     Document Type: Article

References (27)

1. R. Könenkamp, R. C. Word, and C. Schlegel,. Appl. Phys. Lett. 85, 24 (2004).
2. M. H. Huang, S. Mao, H. Feick, H. Yan, Y. Wu, H. Kind, E. Weber, R. Russo, and P. D. Yang,. Science 292, 1897 (2001).
3. J. B. Baxter and E. S. Aydil,. Appl. Phys. Lett. 86, 053114 (2005).
4. Y. W. Zhu, H. Z. Zhang, X. C. Sun, S. Q. Feng, J. Xu, Q. Zhao, B. Xiang, and R. M. Wang,. Appl. Phys. Lett. 83, 144 (2003).
5. H. Kind, H. Yan, B. Messer, M. Law, and P. D. Yang,. Adv. Mater. 14, 158 (2002).
6. Z. W. Pan, Z. R. Dai, and Z. L. Wang,. Science 291, 1947 (2001).
7. P. D. Yang, H. Q. Yan, S. Mao, R. Russo, J. Johnson, R. Saykally, N. Morris, J. Pham, R. R. He, and H. J. Choi,. Adv. Funct. Mater. 12, 323 (2002).
8. W. I. Park, D. H. Kim, S. W. Jung, and G. C. Yi,. Appl. Phys. Lett. 80, 4232 (2002).
9. B. Liu and H. C. Zeng,. J. Am. Chem. Soc. 125, 4430 (2003).
10. J. H. Yang, G. M. Liu, J. Lu, Y. F. Qiu, and S. H. Yang,. Appl. Phys. Lett. 90, 103109 (2007).
11. S. H. Jung, E. Oh, K. H. Lee, W. J. Park, and S. H. Jeong,. Adv. Mater. 19, 749 (2007).
12. M. H. Huang, Y. Y. Wu, H. Feick, N. Tran, E. Weber, and P. D. Yang,. Adv. Mater. 13, 113 (2001).
13. P. X. Gao, C. S. Lao, Y. Ding, and Z. L. Wang,. Adv. Funct. Mater. 16, 53 (2006).
14. F. Fang, D. X. Zhao, J. Y. Zhang, D. Z. Shen, Y. M. Lu, X. W. Fan, B. H. Li, and X. H. Wang,. Nanotechnology 18, 235604 (2007).
15. X. Q. Meng, D. Z. Shen, J. Y. Zhang, D. X. Zhao, L. Dong, Y. M. Lu, Y. C. Liu, and X. W. Fan,. Nanotechnology 16, 609 (2005).
16. H. C. Hsu and W. F. Hsieh,. Solid State Commun. 131, 371 (2004).
17. B. P. Zhang, N. T. Binh, Y. Segawa, K. Wakatsuki, and N. Usami,. Appl. Phys. Lett. 83, 1635 (2003).
18. Y. H. Tong, Y. C. Liu, S. X. Lu, L. Dong, S. J. Chen, and Z. Y. Xiao,. J. Sol-Gel Sci. Technol. 30, 157 (2004).
19. Z. Guo, D. X. Zhao, D. Z. Shen, F. Fang, J. Y. Zhang, and B. H. Li,. Crystal Growth Des. 7, 2294 (2007).
20. R. Chang and S. H. Lin,. Phys. Rev. B 68, 045326 (2003).
21. W. T. Hsu, K. F. Lin, and W. F. Hsieha,. Appl. Phys. Lett. 91, 181913 (2007).
22. J. M. Calleja and M. Cardona,. Phys. Rev. B. 16, 3753 (1997).
23. T. C. Damen, S. P. S. Porto, and B. Tell,. Phys. Rev. 142, 570 (2001).
24. J. Y. Lao, J. Y. Huang, D. Z. Wang, and Z. F. Ren,. Nano Lett. 3, 235 (2003).
25. K. Vanheusden, W. L. Warren, C. H. Seager, D. R. Tallant, and J. A. Voigt,. J. Appl. Phys. 79, 7983 (1996).
26. X. L. Wu, G. G. Siu, C. L. Fu, and H. C. Ong,. Appl. Phys. Lett. 78, 2285 (2001).
27. Z. Guo, D. X. Zhao, D. Z. Shen, F. Fang, J. Y. Zhang, and B. H. Li,. Crystal Growth Des. 7, 2294 (2007).