A model for predicting the mixed-mode fatigue crack growth in a bonded joint

Fatigue and Fracture of Engineering Materials and Structures

Volumn 37, Issue 4, 2014, Pages 380-390

  Marannano, G ^a   Pasta, A ^a   Giallanza, A ^a  

^a UNIVERSITY OF PALERMO   (Italy)

Author keywords

bonded joint; damage models; fatigue crack propagation; FEM analysis; mixed mode crack growth; VCCT

Indexed keywords

ADHESIVE JOINTS; COMPUTER SIMULATION; CRACKS; FATIGUE CRACK PROPAGATION; FATIGUE DAMAGE; FINITE ELEMENT METHOD;

BONDED JOINT; DAMAGE MODEL; FEM ANALYSIS; MIXED-MODE CRACK GROWTH; VCCT;

FAILURE (MECHANICAL);

EID: 84895926147     PISSN: 8756758X     EISSN: 14602695     Source Type: Journal    
DOI: 10.1111/ffe.12121     Document Type: Article

References (27)

1. Schindler, H. J., and, Leinenbach, C., (2012) Mechanics of fatigue crack growth in a bonding interface. Engineering Fracture Mechanics, 89, 52-64.
2. Fernlund, G., and, Spelt, J. K., (1994) Mixed-mode fracture characterization of adhesive joints. Composites Science and Technology, 50, 441-449.
3. Pirondi, A., and, Nicoletto, G., (2006). Mixed mode I/II fatigue crack growth in adhesive joints. Engineering Fracture Mechanics, 73, 2557-2568.
4. Fernando, M., Harjoprayitno, W. W., and, Kinloch, A. J., (1996) A fracture mechanics study of the influence of moisture on the fatigue behaviour of adhesively bonded aluminium-alloy joints. Int. J. Adhesion and Adhesives, 16, 113-119.
5. Pitt, S., Jones, R., and, Peng, D., (2012) Characterization of the durability of adhesive bonds. Fatigue & fracture of engineering materials & structures, 35, 998-1006.
6. Marannano, G. V., and, Pasta, A., (2007) An analysis of interface delamination mechanisms in orthotropic and hybrid fiber-metal composite laminates. Engineering Fracture Mechanics, 74, 612-626.
7. Zeng, Q., and, Sun, C. T., (2004) Fatigue performance of a bonded wavy composite lap joint. Fatigue & Fracture of Engineering Materials & Structures, 27, 413-422.
8. Jones, R., Kotousov, A., and, Marshall, I. H., (2002) Adhesively bonded joints under cyclic loading spectra. Fatigue & Fracture of Engineering Materials & Structures, 25, 173-185.
9. Pugno, N., and, Carpinteri, A., (2002) Strength, stability and size effects in the brittle behaviour of bonded joints under torsion: theory and experimental assessment. Fatigue & Fracture of Engineering Materials & Structures, 25, 55-62.
10. Parrinello, F., Marannano, G., Borino, G., and, Pasta, A., (2013) Frictional effect in mode II delamination: experimental test and numerical simulation. Engineering Fracture Mechanics, 110, 258-269.
11. Pasta, S., and, Reynolds, A. P., (2008) Evaluation of residual stresses during fatigue test in an FSW joint. Strain, 44 (2), 147-152.
12. Hashemi, S., Kinloch, A. J., and, Williams, J. G., (1990) The analysis of interlaminar fracture in uniaxial fiber polymer composites. Proc R Soc London Ser A Math Phys Eng Sci, 427, 173-199.
13. Kinloch, A. J., Wang, Y., Williams, J. G., and, Yayla, P., (1993) The mixed-mode delamination of fiber composite materials. Compos Sci Technol, 47, 225-237.
14. Williams, J. G., (1988) On the calculation of energy release rates for cracked laminates. Int J Fract, 36, 101-119.
15. Davidson, B. D., Gharibian, S. J., and, Yu, L., (2000) Evaluation of energy release rate based approaches for predicting delamination growth in laminated composites. Int J Fract, 105, 343-365.
16. Rybicki, E. F., and, Kanninen, M. F., (1977) Finite-element calculation of stress intensity factors by a modified crack closure integral. Eng Frac Mech, 9, 931-938.
17. Krueger, R., (2004) Virtual crack closure technique: history, approach, and applications. Appl Mech Rev, 57, 109-143.
18. Marannano, G. V., Mistretta, L., Cirello, A., and, Pasta, S., (2008) Crack growth analysis at adhesive-adherent interface in bonded joints under mixed mode I/II. Engineering Fracture Mechanics, 75, 5122-5133.
19. He, X., (2011) A review of finite element analysis of adhesively bonded joints. International Journal of Adhesion & Adhesives, 31, 248-264.
20. Blanco, N., Gamstedt, E. K., Costa, J., and, Trias, D., (2006) Analysis of the mixed-mode end load split delamination test. Composite Structures, 76, 14-20.
21. Reeder, J. R., and, Crews, J. H., (1990) Mixed mode bending method for delamination testing. AIAA J., 28, 1270-1276.
22. Reeder, J. R., and, Crews, J. H., (1992) Redesign of the mixed-mode bending delamination test to reduce nonlinear effects. J. Compos. Technol., 14, 12-19.
23. TM Epoxy Adhesive DP760, 3M Product data sheet.
24. Higgins, A., (2000) Adhesive of aircraft structures. International Journal of Adhesion & Adhesives, 20, 367-376.
25. Baldan, A., (2004) Review-Adhesively-bonded joints and repairs in metallic alloys, polymers and composite materials: adhesives, adhesion theories and surface pretreatment. Journal of materials science, 39, 1-49.
26. Paris, P. C., and, Sih, G. C., (1965) Stress analysis of cracks. Fracture Toughness Testing. ASTM STP, 381, 30-83.
27. Kenane, M., Benmedakhene, S., and, Azari, Z., (2010) Fracture and fatigue study of unidirectional glass/epoxy laminate under different mode of loading. Fatigue & Fracture of Engineering Materials & Structures, 33, 284-293.