Biodegradable poly(butylene succinate) composites reinforced by cotton fiber with silane coupling agent

Polymers

Volumn 5, Issue 1, 2013, Pages 128-141

  Calabia, Buenaventurada P ^a   Ninomiya, Fumi ^a   Yagi, Hisaaki ^a   Oishi, Akihiro ^a   Taguchi, Kazuhiro ^a   Kunioka, Masao ^a   Funabashi, Masahiro ^a  

^a NATIONAL INSTITUTE OF ADVANCED INDUSTRIAL SCIENCE AND TECHNOLOGY AIST   (Japan)

Author keywords

Composites; Cotton fiber; Poly(butylene succinate); Silane coupling agent

Indexed keywords

BIODEGRADATION RATE; CARBON CONTENT; FILLER LOADING; FRACTURE SURFACES; POLY (BUTYLENE SUCCINATE); SILANE COUPLING AGENT; SILANE TREATMENT; THERMO-GRAVIMETRIC;

BIODEGRADATION; BUTENES; COMPOSITE MATERIALS; COTTON FIBERS; COUPLING AGENTS; FIBERS; FILLERS; MECHANICAL PROPERTIES; SCANNING ELECTRON MICROSCOPY; TENSILE STRENGTH; THERMODYNAMIC STABILITY; THERMOGRAVIMETRIC ANALYSIS;

LOADING;

BIODEGRADATION; COMPOSITES; COTTON; COUPLING AGENTS; FIBERS; FILLERS; GRAVIMETRY; LOADING; MECHANICAL PROPERTIES; SCANNING ELECTRON MICROSCOPY; SILANES; TENSILE STRENGTH; THERMAL ANALYSIS;

EID: 84883269259     PISSN: None     EISSN: 20734360     Source Type: Journal    
DOI: 10.3390/polym5010128     Document Type: Article

References (37)

1. Tachibana, Y.; Giang, N.T.G.; Ninomiya, F.; Funabashi, M.; Kunioka, M. Cellulose acetate butyrate as multifunctional additive for poly(butylene succinate) by melt blending: Mechanical properties, biomass carbon ratio, and control of biodegradability. Polym. Degrad. Stab. 2010, 95, 1406-1413.
2. Ku, H.; Wang, H.; Pattarachaiyakoop, N.; Trada, M. A review on the tensile properties of natural fiber reinforced polymer composites. Compos. Part B 2009, 42, 856-873.
3. Zhao, Y.; Qui, J.; Feng, H.; Zhang, M. The interfacial modification of rice straw fiber reinforced poly(butylene succinate) composites: Effect of aminosilane with different alkoxy groups. J. Appl. Polym. Sci. 2012, 125, 3211-3220.
4. Teramoto, N.; Urata, K.; Ozawa, K.; Shibata M. Biodegradation of aliphatic polyester composites reinforced by abaca fiber. Polym. Degrad. Stab. 2004, 86, 401-409.
5. Liang, Z.; Pan, P.; Zhu, B.; Dong, T.; Inoue, Y. Mechanical and thermal properties of poly(butylene succinate)/plant fiber biodegradable composite. J. Appl. Polym. Sci. 2010, 115, 3559-3567.
6. Liu, L.; Yu, J.; Cheng, L.; Yang, X. Biodegradability of poly(butylene succinate) (PBS) composite reinforced with jute fibre. Polym. Degrad. Stab. 2009, 94, 90-94.
7. Fan, D.; Chang, P.R.; Lin, N.; Yu, J.; Huang, J. Structure and properties of alkaline lignin-filled poly(butylene succinate) plastics. Iran. Polym. J. 2011, 20, 3-14.
8. Lee, S.H.; Wang, S. Biodegradable polymers/bamboo fiber biocomposite with bio-based coupling agent. Compos. Part A 2006, 37, 80-91.
9. Shih, Y.F.; Lee, W.C.; Jeng, R.J.; Huang, C.M. Water bamboo husk-reinforced poly(butylene succinate) biodegradable composites J. Appl. Polym. Sci. 2006, 99, 188-199.
10. Kim, H.S.; Yang, H.S.; Kim, H.J. Biodegradability and mechanical properties of agro-flour-filled polybutylene succinate biocomposites. J. Appl. Polym. Sci. 2005, 97, 1513-1521.
11. Flores, E.D.; Funabashi, M.; Kunioka, M. Mechanical properties and biomass carbon ratios of poly(butylene succinate) composites filled with starch and cellulose filler using furfural as plasticizer. J. Appl. Polym. Sci. 2009, 112, 3410-3417.
12. Ohkita, T.; Lee, S.H. Crystallization behavior of poly(butylene succinate)/corn starch biodegradable composite. J. Appl. Polym. Sci. 2005, 97, 1107-1114.
13. Silva, C.G.; Benaducci, D.B.; Frollini, E. Lyocell and cotton fibers as reinforcements for a thermoset polymer. Bioresources 2011, 7, 78-98.
14. Raftoyiannis, I.G. Experimental testing of composite panels reinforced with cotton fibers. Open J. Compos. Mater. 2012, 2, 31-39.
15. Bledzki, A.K.; Gassan, J. Composites reinforced with cellulose based fibers. Prog. Polym. Sci. 1999, 24, 221-274.
16. Mohanty, A.K.; Misra, M.; Drzal, L.T. Sustainable bio-composites from renewable resources: Opportunities and challenges in the green materials world. J. Polym. Environ. 2002, 10, 19-26.
17. Rozman, H.D..; Tan, K.W.; Kumar, R.N.; Abubakar, A.; Mohd Ishak, Z.A.; Ismail, H. Effect of lignin as a compatibilizer on the physical properties of coconut fiber-polypropylene composites. Eur. Polym. J. 2000, 36, 1483-1494.
18. Peltola, H.; Laatkainen, E.; Jetsu, P. Effects of physical treatment of wood fibres on fibre morphology and biocomposite properties. Plast. Rubber Compos. 2011, 40, 86-92.
19. Kabir, M.M.; Wang, H.; Lau, K.T.; Cardona, F. Chemical treatments on plant-based natural fibre reinforced polymer composites: An overview. Compos. Part B 2012, http://dx.doi.org/10.1016/j.compositesb.2012.04.053
20. Abdelmouleh, M.; Boufi, S.; Belgacem, M.N.; Duarte, A.P.; Salah, A.B.; Gandini, A. Modification of cellulosic fibres with functionalized silanes: Development of surface properties. Int. J. Adhes. Adhes. 2004, 24, 43-54.
21. Castellano, M.; Gandini, A.; Fabbri, P.; Belgacem, M.N. Modification of cellulose fibres with organosilanes: Under what conditions does coupling occur? J. Colloid. Interface Sci. 2004, 273, 505-511.
22. Funabashi, M.; Ninomiya, F.; Flores, E.D.; Kunioka, M. Biomass carbon ratio of polymer composites measured by accelerator mass spectrometry. J. Polym. Environ. 2010, 18, 85-93.
23. Funabashi, M.; Ninomiya, F.; Ohara, K.; Kunioka, M. Biomass carbon ratio of biomass chemicals measured by accelerator mass spectrometry. Bull. Chem. Soc. Jpn. 2009, 82, 1538-1547.
24. Funabashi, M.; Kunioka, M.; Listyarini, A. Biomass carbon ratio of biobased polymer composites filled with cellulose fillers measured by accelerator mass spectrometry. WIT Trans. Built. Environ. 2008, 97, 221-230.
25. Listyarini, A.; Kunioka, M.; Funabashi, M. Biodegradable poly(butylene succinate) blended with biorenewable derivatives from polysaccharides. Trans. Mater. Res. Soc. Jpn. 2008, 33, 1159-1164.
26. Kunioka, M.; Ninomiya, F.; Funabashi, M. Biobased contents of organic fillers and polycaprolactone composites with cellulose fillers measured by accelerator mass spectrometry based on ASTM D6866. J. Polym. Environ. 2007, 15, 281-287.
27. Kunioka, M.; Ninomiya, F.; Funabashi, M. Novel evaluation method of biodegradabilities for oil-based polycaprolactone by naturally occurring radiocarbon-14 concentration using accelerator mass spectrometry based on ISO 14855-2 in controlled compost. Polym. Degrad. Stab. 2007, 92, 1279-1288.
28. Kunioka, M.; Inuzuka, Y.; Ninomiya, F.; Funabashi, M. Biobased contents of biodegradable poly(e-caprolactone) composites polymerized and directly molded using aluminum triflate from caprolactone with cellulose and inorganic filler. Macromol. Biosci. 2006, 6, 517-523.
29. Determination of the Ultimate Aerobic Biodegradability of Plastic Materials under Controlled Composting Conditions-Method by Analysis of Evolved Carbon Dioxide-Part 2: Gravimetric Measurement of Carbon Dioxide Evolved In a Laboratory-Scale Test; ISO 14855-2; ISO: Geneva, Switzerland, 2007.
30. Kunioka, M.; Ninomiya, F.; Funabashi, M. Biodegradation of poly(butylene succinate) powder in a controlled compost at 58 °C evaluated by naturally-occurring Carbon 14 amounts in evolved CO2 based on the ISO 14855-2 method. Int. J. Mol. Sci. 2009, 10, 4267-4283.
31. Funabashi, M.; Ninomiya, F.; Kunioka, M. Biodegradability evaluation of polymers by ISO 14855-2. Int. J. Mol. Sci. 2009, 10, 3635-3654.
32. Standard test Methods for Determining the Biobased Content of Solid, Liquid, and Gaseous Samples using Radiocarbon Analysis. ASTM D6866-12; ASTM: West Conshohocken, PA, USA, 2012.
33. Nakatani, H.; Iwakura, K.; Miyazaki, K.; Okazaki, N.; Terrano, M. Effect of chemical structure of silane coupling agent on interface adhesion properties of syndiotactic polypropylene/cellulose composite. J. Appl. Polym. Sci. 2011, 119, 1732-1741.
34. Sombatsompop, N.; Chaochanchaikul, K. Average mixing torque, tensile and impact properties, and thermal stability of poly(vinyl chloride)/sawdust composites with different silane coupling agents. J. Appl. Polym. Sci. 2005, 96, 213-221.
35. Correlo, V.M.; Boesel, L.F.; Pinho, E.; Costa-Pintp, A.R.; Alves da Silva, M.L.; Bhattacharya, M.; Mano, J.F.; Neves, N.M.; Reis, R.L. Melt-based compression-molded scaffolds from chitosan-polyester blends and composites: Morphology and mechanical properties. J. Biomed. Mater. Res. 2009, 91A, 489-504.
36. Kokta, B.V.; Dembele, F.; Daneult, C.B. Polymer Science and Technology; Carraher, J.R., Sperling, L.H., Eds.; Plenum: New York, NY, USA, 1985; Volume 33.
37. Huda, M.S.; Drzal, L.T.; Mohanty, A.K.; Misra, M. The effect of silane treated-and untreated-talc on the mechanical and physic-mechanical properties of poly(lactic acid)/newspaper fibers/talc hybrid composites. Compos. Part B 2007, 38, 367-379.