Vacuum-dried robust bridged silsesquioxane aerogels

Advanced Materials

Volumn 25, Issue 32, 2013, Pages 4494-4497

  Wang, Zhen ^a,b   Dai, Zhen ^a   Wu, Junjie ^a,b   Zhao, Ning ^a   Xu, Jian ^a  

^a INSTITUTE OF CHEMISTRY   (China)

^b UNIVERSITY OF CHINESE ACADEMY OF SCIENCES   (China)

Author keywords

aerogels; bridged silsesquioxanes; click chemistry; robustness; vacuum drying

Indexed keywords

BRIDGED SILSESQUIOXANES; CLICK CHEMISTRY; FACILE PREPARATION; FUNCTIONALIZATIONS; LOW DENSITY; SILSESQUIOXANES; THIOL-ENES; VACUUM DRYING;

ROBUSTNESS (CONTROL SYSTEMS); VACUUM;

AEROGELS;

EID: 84882567128     PISSN: 09359648     EISSN: 15214095     Source Type: Journal    
DOI: 10.1002/adma.201301617     Document Type: Article

References (35)

1. S. S. Kistler, Nature 1931, 127, 741.
2. a) N. Hüsing, U. Schubert, Angew. Chem. Int. Ed. 1998, 37, 23
3. b) C. Tan, B. M. Fung, J. K. Newman, C. Vu, Adv. Mater. 2001, 13, 644
4. c) H. D. Gesser, P. C. Goswami, Chem. Rev. 1989, 89, 765
5. d) A. C. Pierre, G. M. Pajonk, Chem. Rev. 2002, 102, 4243
6. e) J. Choi, D. J. Suh, Catal. Surv. Asia 2007, 11, 123.
7. J. P. Randall, M. A. B. Meador, S. C. Jana, ACS Appl. Mater. Interfaces 2011, 3, 613.
8. a) A. Fidalgo, J. P. S. Farinha, J. M. G. Martinho, M. E. Rosa, L. M. Ilharco, Chem. Mater. 2007, 19, 2603
9. b) J. Cai, S. Liu, J. Feng, S. Kimura, M. Wada, S. Kuga, L. Zhang, Angew. Chem.Int. Ed. 2012, 51, 2076
10. c) N. Leventis, C. Sotiriou-Leventis, G. H. Zhang, A. M. M. Rawashdeh, Nano Lett. 2002, 2, 957
11. d) D. J. Boday, R. J. Stover, B. Muriithi, M. W. Keller, J. T. Wertz, K. A. D. Obrey, D. A. Loy, ACS Appl. Mater. Interfaces 2009, 1, 1364
12. e) M. A. B. Meador, E. F. Fabrizio, F. Ilhan, A. Dass, G. H. Zhang, P. Vassilaras, J. C. Johnston, N. Leventis, Chem. Mater. 2005, 17, 1085
13. f) K. Kanamori, M. Aizawa, K. Nakanishi, T. Hanada, Adv. Mater. 2007, 19, 1589.
14. H. Tamon, H. Ishizaka, T. Yamamoto, T. Suzuki, Carbon 1999, 37, 2049.
15. A. P. Rao, G. M. Pajonk, A. V. Rao, J. Mater. Sci. 2005, 40, 3481.
16. A. S. Dorcheh, M. Abbasi, J. Mater. Process. Technol. 2008, 199, 10.
17. a) D. A. Loy, K. J. Shea, Chem. Rev. 1995, 95, 1431
18. b) K. J. Shea, D. A. Loy, Chem. Mater. 2001, 13, 3306
19. c) L. Hu, K. J. Shea, Chem. Soc. Rev. 2011, 40, 688.
20. a) D. A. Loy, G. M. Jamison, B. M. Baugher, E. M. Russick, R. A. Assink, S. Prabakar, K. J. Shea, J. Non-Cryst. Solids 1995, 186, 44
21. b) D. W. Schaefer, G. Beaucage, D. A. Loy, K. J. Shea, J. S. Lin, Chem. Mater. 2004, 16, 1402
22. c) D. J. Boday, R. J. Stover, B. Muriithi, D. A. Loy, J. Mater. Sci. 2011, 46, 6371.
23. a) H. C. Kolb, M. G. Finn, K. B. Sharpless, Angew. Chem. Int. Ed. 2001, 40, 2004
24. b) K. Kempe, A. Krieg, C. R. Becer, U. S. Schubert, Chem. Soc. Rev. 2012, 41, 176.
25. A. V. Rao, E. Nilsen, M. A. Einarsrud, J. Non-Cryst. Solids 2001, 296, 165.
26. a) M. A. B. Meador, E. J. Malow, R. Silva, S. Wright, D. Quade, S. L. Vivod, H. Guo, J. Guo, M. Cakmak, ACS Appl. Mater. Interfaces 2012, 4, 536
27. b) K. H. Kim, S. Park, S. Hwang, M. D. Cho, Chem. Commun. 2012, 48, 386.
28. a) S. Xiang, L. Li, J. Zhang, X. Tan, H. Cui, J. Shi, Y. Hu, L. Chen, C. Y. Su, S. L. James, J. Mater. Chem. 2012, 22, 1862
29. b) M. Kruk, M. Jaroniec, Chem. Mater. 2001, 13, 3169.
30. a) S. Choi, J. H. Drese, C. W. Jones, ChemSusChem 2009, 2, 796
31. b) X. C. Xu, C. S. Song, J. M. Andresen, B. G. Miller, A. W. Scaroni, Energy Fuels 2002, 16, 1463.
32. S. Cui, W. Cheng, X. Shen, M. Fan, A. Russell, Z. Wu, X. Yi, Energy Environ. Sci. 2011, 4, 2070.
33. a) Y. Kuwahara, D. Y. Kang, J. R. Copeland, N. A. Brunelli, S. A. Didas, P. Bollini, C. Sievers, T. Kamegawa, H. Yamashita, C. W. Jones, J. Am. Chem. Soc. 2012, 134, 10757
34. b) B. Aziz, N. Hedin, Z. Bacsik, Microporous Mesoporous Mater. 2012, 159, 42
35. c) Y. Ling, M. Deng, Z. Chen, B. Xia, X. Liu, Y. Yang, Y. Zhou, L. Weng, Chem. Commun. 2013, 49, 78.