Effect of oxygen on ethanol stress corrosion cracking susceptibility: Part 1-electrochemical response and cracking-susceptible potential region

Corrosion

Volumn 69, Issue 8, 2013, Pages 768-780

  Cao, Liu ^a   Frankel, G S ^a   Sridhar, N ^b  

^a OHIO STATE UNIVERSITY   (United States)

^b DNV GL   (Norway)

Author keywords

Ethanol; Oxygen; Potential; Stress corrosion cracking; Supporting electrolyte

Indexed keywords

ANODIC POTENTIALS; CRACKING SUSCEPTIBILITY; ELECTROCHEMICAL RESPONSE; FUEL-GRADE ETHANOLS; POTENTIAL; SATURATED CALOMEL ELECTRODE; SLOW STRAIN RATES; SUPPORTING ELECTROLYTE;

CARBON STEEL; ELECTROLYTES; ETHANOL; MICROELECTRODES; OXYGEN; STRAIN RATE; STRESS CORROSION CRACKING;

CRACKS;

EID: 84881139425     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/0885     Document Type: Article

References (39)

1. "Oxygenates Fact Book: A Compilation of Information on the Benefits of Oxygenates in Gasoline," Clean Fuels Development Coalition technical report (Bethesda, MD: Clean Fuels Development Coalition, 2007).
2. D. Keeney, Environ. Sci. Technol. 43, 1 (2009): p. 8-11.
3. "Fuel Ethanol Industry Guidelines, Specifications and Procedures," in RFA Publication no. 960501 (Washington, DC: Renewable Fuels Association, 2005).
4. "National Biofuels Action Plan," in Clean Cities (Washington, DC: Biomass Research and Development Board, U.S. Department of Agriculture and U.S. Department of Energy, 2008).
5. R.D. Kane, D. Eden, N. Sridhar, J. Maldonado, A.K. Agarwal, J.A. Beavers, M.P.H. Brongers, "Stress Corrosion Cracking of Carbon Steel in Fuel-Grade Ethanol: Review, Experience Survey, Field Monitoring, and Laboratory Testing," in API Technical Report 939-D, 2007, American Petroleum Institute: Washington, D.C.
6. R. Singh, Mater. Perform. 48, 5 (2009): p. 53-55.
7. N. Sridhar, Mater. Perform. 46, 12 (2007): p. 18-18.
8. S.M. Bhola, R. Bhola, L. Jain, B. Mishra, D.L. Olson, J. Mater. Eng. Perform. 20, 3 (2011): p. 409-416.
9. F. Gui, N. Sridhar, J.A. Beavers, Corrosion 66, 12 (2010): p. 125001.
10. X. Lou, P.M. Singh, Corros. Sci. 52, 7 (2010): p. 2303-2315.
11. F. Bellucci, G. Capobianco, G. Faita, C.A. Farina, G. Farnia, F. Mazza, S. Torchio, Corros. Sci. 28, 4 (1988): p. 371-&.
12. C.S. Brossia, E. Gileadi, R.G. Kelly, Corros. Sci. 37, 9 (1995): p. 1455-1471.
13. R.D. Kane, S. Papavinasam, "Corrosion and SCC Issues in Fuel Ethanol and Biodiesel," CORROSION/2009, paper no. 09528 (Houston, TX: NACE International, 2009).
14. J.A. Beavers, M.P. Brongers, A.K. Agrawal, F.A. Tallarida, "Prevention of Internal SCC in Ethanol Pipelines," CORROSION/ 2008, paper no. 08153 (Houston, TX: NACE, 2008).
15. R.D. Kane, N. Sridhar, M.P. Brongers, A.K. Agrawal, L.J. Klein, Mater. Perform. 44, 12 (2005): p. 50-55.
16. N. Sridhar, K. Price, J. Buckingham, J. Dante, Corrosion 62, 8 (2006): p. 687-702.
17. J.G. Maldonado, N. Sridhar, "SCC of Carbon Steel in Fuel Ethanol Service: Effect of Corrosion Potential and Ethanol Processing Source," CORROSION/2007, paper no. 07574 (Houston, TX: NACE: 2007).
18. F. Gui, S. Sridhar, J. Beavers, "Techniques for Monitoring Conditions Leading to SCC of Carbon Steel in Fuel Grade Ethanol," CORROSION/2009, paper no. 09531 (Houston, TX: NACE: 2009).
19. R.C. Newman, Corrosion 64, 11 (2008): p. 819-823.
20. N.J.H. Holroyd, R.N. Parkins, Corros. Sci. 20, 6 (1980): p. 707-721.
21. R.N. Parkins, Corros. Sci. 20, 2 (1980): p. 147.
22. R.W. Staehle, "Predictions and Experimental Verification of the Slip Dissolution Model for Stress Corrosion Cracking of Low Strength Alloys," in Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, vol. 5 (Houston, TX: NACE, 1977), p. 180.
23. ASTM D4806-13, "Standard Specification for Denatured Fuel Ethanol for Blending with Gasolines for Use as Automotive Spark-Ignition Engine Fuel" (West Conshohocken, PA: ASTM International, 2013).
24. F. Gui, N. Sridhar, J. Beavers, E. Trillo, P.M. Singh, "Effect of Ethanol Composition on the SCC Susceptibility of Carbon Steel," CORROSION/2010, paper no. 10075 (Houston, TX: NACE, 2010).
25. A. Venkatesh, B. Chambers, R.D. Kane, K. Kirkham, "Evaluation of Stress Corrosion Cracking Behavior of Steel in Multiple Ethanol Environments," CORROSION/2010, paper no. 10077 (Houston, TX: NACE, 2010).
26. J.A. Beavers, F. Gui, N. Sridhar, Corrosion 67, 2 (2011): p. 025005.
27. X. Lou, D. Yang, P.M. Singh, Corrosion 65, 12 (2009): p. 785-797.
28. L. Cao, G.S. Frankel, N. Sridhar, J. Electrochem. Soc. 160, 1 (2013): p. C19-C27.
29. C.S. Brossia, R.G. Kelly, Electrochim. Acta 41, 16 (1996): p. 2579- 2585.
30. ASTM G129-00(2006), "Standard Practice for Slow Strain Rate Testing to Evaluate the Susceptibility of Metallic Materials to Environmentally Assisted Cracking" (West Conshohocken, PA: ASTM International, 2006).
31. A. Contreras, A. Albiter, C. Angeles-Chavez, R. Perez, Rev. Mex. Fis. 50 (2004): p. 49-53.
32. J. Torkkeli, V. Hirsi, T. Saukkonen, H. Hänninen, "Evaluation of Post-Weld Heat Treatment as a Method to Prevent Stress Corrosion Cracking of Carbon Steel in Ethanol by Notched Constant Tensile Load Testing," in EUROCORR 2011 (Stockholm, Sweden: The European Corrosion Congress, 2011).
33. B.Y. Fang, R.L. Eadie, W.X. Chen, M. Elboujdaini, Corros. Eng. Sci. Technol. 45, 4 (2010): p. 302-312.
34. G.T. Burstein, C.J. Barnett, A.R. Kucernak, K.R. Williams, Catal. Today 38, 4 (1997): p. 425-437.
35. W.D. Frasch, R. Mei, M.A. Sanders, Biochemistry 27, 10 (1988): p. 3715-3719.
36. K. Kervinen, H. Korpi, J.G. Mesu, F. Soulimani, T. Repo, B. Rieger, M. Leskela, B.M. Weckhuysen, Eur. J. Inorg. Chem. 13 (2005): p. 2591-2599.
37. A. Kowal, S.N. Port, R.J. Nichols, Catal. Today 38, 4 (1997): p. 483-492.
38. H.-F. Wang, Z.-P. Liu, J. Am. Chem. Soc. 130, 33 (2008): p. 10996-11004.
39. D.L. Pavia, Introduction to Organic Laboratory Techniques: A Small Scale Approach (Thomson Brooks/Cole, 2005).