Review and hypothesis for the stress corrosion mechanism of carbon steel in alcohols

Corrosion

Volumn 64, Issue 11, 2008, Pages 819-823

  Newman, Roger C ^a  

^a UNIVERSITY OF TORONTO   (Canada)

Author keywords

Alcohols; Non aqueous solvents; Stress corrosion cracking

Indexed keywords

ALCOHOLS; CARBON DIOXIDE; CARBON MONOXIDE; CARBON STEEL; CORROSION; CRACKS; DIRECT ALCOHOL FUEL CELLS (DAFC); FORMIC ACID; FREE RADICALS; FUEL CELLS; HYDROGEN EMBRITTLEMENT; LOAD TESTING; RESIDUAL STRESSES; STRAIN RATE; TEXTURES;

ANHYDROUS AMMONIA; CRACKING MECHANISMS; CRITICAL EXPERIMENT; FREE RADICAL OXIDATION; NON-AQUEOUS SOLVENTS; SLOW STRAIN RATE TESTING; STRESS CORROSION; TRANSGRANULAR FRACTURE;

STRESS CORROSION CRACKING;

EID: 56849094675     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3279915     Document Type: Review

References (57)

1. K. Matsukura, K. Sato, Y. Kokabu, Tetsu-to-Hagane 62 (1976): p. 1,025-1,034.
2. K. Matsukura, K. Sato, Trans. Iron Steel Inst. Jpn. 18 (1978): p. 554-563.
3. G. Capobianco, G. Faita, "Corrosion Behavior and Stress Corrosion Cracking of Iron and Low-Alloy Steel in Methanol Solutions," in Proc. 9th Int. Congress on Metallic Corrosion, vol. 3 (Ottawa, ON, Canada: National Research Council [NRC], 1984), p. 532-537.
4. C.A. Farina, U. Grassini, "Water as Stress Corrosion Cracking Inhibitor in Non-Aqueous Media," in Proc, 6th European Symp. on Corrosion Inhibitors (Ferrara, Italy: Universita Degli Studi di Ferrara, 1985), p. 715-727.
5. E. Wendler-Kalsch, "Corrosion and Stress Corrosion Cracking of Iron Materials in Methanol Under Practical Conditions," in Proc. 8th European Congress on Corrosion, vol. 1 (Paris, France: Centre Francais de la Corrosion, Societe de Chimie Industrielle, 1986), p 56.1-56.6.
6. C.A. Farina, U. Grassini, Electrochim. Acta 32 (1987): p. 977-980.
7. E. Wendler-Kalsch, Werkst. Korros. 39 (1988): p. 432-433.
8. R. Kefferstein, X. Jartoux, Rev. Metal. D 95 (1998): p. 389-399.
9. R. Kefferstein, D. Petelot, F. Fouquart, "Stress Corrosion Cracking of Mild Steels in Alcoholic Environments," in Abstracts of EUROCORR'98 (Bilthoven, The Netherlands: The Netherlands Corrosion Centre, 1998).
10. E. Risson, T. Magnin, R. Kefferstein, B. Bayle, "Factors Influencing Stress Corrosion Cracking of Mild Steels in Methanol," in Hydrogen Effects on Materials Behavior and Corrosion Deformation Interactions (Warrendale, PA: The Mineral, Metals, and Materials Society [TMS]; Littleton, CO: American Institute of Mining, Metallurgical, and Petroleum Engineers [AIME], 2003), p. 663-671.
11. R.D. Kane, J.G. Maldonado, L.J. Klein, "Stress Corrosion Cracking in Fuel Ethanol: A Newly Recognized Phenomenon," CORROSION/2004, paper no. 04543 (Houston, TX: NACE International, 2004).
12. R.D. Kane, N. Sridhar, M.P. Brongers, J.A. Beavers, A.K. Agrawal, L.J. Mein, Mater. Perform. 44, 12 (2005): p. 50-55.
13. N. Sridhar, K. Price, J. Buckingham, J. Dante, Corrosion 62 (2006): p. 687-702.
14. J.G. Maldonado, N. Sridhar, "SCC of Carbon Steel in Fuel Ethanol Service: Effect of Corrosion Potential and Ethanol Processing Source," CORROSION/2007, paper no. 07574 (Houston, TX: NACE, 2007).
15. B.R.W. Hinton, R.P.M. Procter, Corros. Sci. 23 (1983): p. 101-123.
16. 2 Environments," in Hydrogen Effects on Materials Behavior (Warrendale, PA: The Minerals, Metals, and Materials Society [TMS]. 1990), p. 965-973.
17. R.N. Parkins, Z.A. Foroulis, Mater. Perform. 27, 1 (1988): p. 19-29.
18. R.N. Parkins, W.K. Blanchard, B.S. Delanty, Corrosion 50 (1994): p. 394-408.
19. R.N. Parkins, S. Zhou, Corros. Sci. 39 (1997): p. 159-173.
20. B.A. Harle, J.A. Beavers, Corrosion 49 (1993): p. 861-863.
21. R.P.M. Procter, M.V.E. Omideyi, R.C. Newman, W. Zheng, Corros. Sci. 33 (1992): p. 1,009-1,031.
22. R.C. Newman, W. Zheng, R.P.M. Procter, Corros. Sci. 33 (1992): p. 1,033-1,051.
23. R.N. Parkins, Corros. Sci. 36 (1994): p. 2,097-2,110.
24. R.N. Parkins, Br. Corros. J. 31 (1996): p. 288-293.
25. H. Grafen, H. Schlecker, Werkst. Korros. 35 (1984): p. 278-280.
26. K. Nakagawa, T. Kawamoto, Boshoku Gijutsu (Corros. Eng.) 33 (1984): p. 559-565.
27. 2O System," in Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys (Houston, TX: NACE, 1977), p. 686-695.
28. A. Brown, J.T. Harrison, R. Wilkins, Corros. Sci. 10 (1970): p. 547-548.
29. N.J.H. Holroyd, R.N. Parkins, Corros. Sci. 20 (1980): p. 707-721.
30. J.G. Parker, W.G. Pearce, Corrosion 30 (1974): p. 18-23.
31. J. Jiang, J.F. Bank, C.P. Scholes, J. Am. Chem. Soc. 115 (1993): p. 4,742-4,746.
32. S. Zecevic, D.M. Drazic, S. Gojkovic, Electrochim. Acta 36 (1991): p. 5-14.
33. V. Jovancicevic, J.O'M. Bockris, J. Electrochem. Soc. 133 (1986): p. 1,797-1,807.
34. E.R. Vago. E.J. Calvo, J. Electroanal. Chem. 388 (1995): p. 161-165.
35. E.R. Vago, E.J. Calvo, M. Stratmann, Electrochim. Acta 39 (1994): p. 1,655-1,659.
36. D. Gervasio, I. Song, J.H. Payer, J. Appl. Electrochem. 28 (1998): p. 979-992.
37. A. Leng, H. Streckel, K. Hofmann, M. Stratmann, Corros. Sci. 41 (1999): p. 599-620.
38. E.J. Calvo, D.J. Schiffrin, J. Electroanal. Chem. 243 (1988): p. 171-185.
39. M. Bonifacic, D.A. Armstrong, I. Stefanie, K.-D. Asmus, J. Phys. Chem. B 107 (2003): p. 7,268-7,276.
40. F.C. Simoes, D.M. dos Anjos, F. Vigier, J.M. Leger, F. Hahn, C. Coutanceau, E.R. Gonzalez, G. Tremiliosi, A.R. de Andrade, P. Olivi, K. B. Kokoh, J. Power Sources 167 (2007): p. 1-10.
41. R. Miles, J. Chem. Technol. Biotechnol. 30 (1980): p. 35-43.
42. G. Kawamura, H. Okamoto, A. Ishikawa, T. Kudo, J. Electrochem, Soc. 134 (1987): p. 1,653-1,658.
43. H. Scholl, B. Hofman, A. Rauscher, Electrochim. Acta 37 (1992): p. 447-452.
44. G.T. Burstein, C.J. Barnett, A.R.J. Kucernak, K.R. Williams, J. Electrochem. Soc. 143 (1996): p. L139-L140.
45. C.J. Barnett, G.T. Burstein, A.R.J. Kucernak. K.R. Williams, Electrochim. Acta 42 (1997): p. 2,381-2,388.
46. H.H. Hwu, J.G.G. Chen, K. Kourtakis, J.G. Lavin, J. Phys. Chem. B 105 (2001): p. 10,037-10,044.
47. G.T. Burstein, D.R. McIntyre, A. Vossen, Electrochem. Solid State Lett. 5 (2002): p. A80-A83.
48. D.R. McIntyre, A. Vossen, J.R. Wilde, G.T. Burstein, J. Power Sources 108 (2002): p. 1-7.
49. R. Ganesan, J.S. Lee, Angewandte Chem. Int. 44 (2005): p. 6,557-6,560.
50. E.C. Weigert, J. South, R.A. Rykov, J.G.G. Chen, Catal. Today 99 (2005): p. 285-290.
51. H.H. Hwu, J.G.G. Chen, J. Vac. Sci. Technol. A 21 (2003): p. 1,488-1,493.
52. G.T. Burstein, private communication.
53. C.W. Hills, M.S. Nachner, A.I. Frenkel, J.R. Shapley, R.G. Nuzzo, Langmuir 15 (1999): p. 690-700.
54. G. Neri, A. Bonavita, G. Rizzo, S. Galvagno, S. Capone, P. Siciliano, Sens. Actuators B 114 (2006): p. 687-695.
55. K. Arshak, I. Gaidan, Sens. Actuators B 111-112 (2005): p. 58-62.
56. C.V. Gopal Reddy, K. Kalyana Seela, S.V. Manorama, Int. J. Inorg. Mater. 2 (2000): p. 301-307.
57. S. Wang, W. Wang, W. Wang, Z. Jiao, J. Lu, Y. Qian, Sensors and Actuators B 69 (2000): p. 22-27.