An investigation on hot corrosion behavior of YSZ-Ta2O5 in Na2SO4+V2O5 salt at 1100°C

Corrosion Science

Volumn 75, Issue , 2013, Pages 409-414

  Habibi, M H ^a   Wang, Li ^a   Liang, Jiandong ^a   Guo, S M ^a  

^a LOUISIANA STATE UNIVERSITY   (United States)

Author keywords

A. Tantalum oxide; A. Thermal barrier coating (TBC); A. YSZ; C. Hot corrosion

Indexed keywords

A. YSZ; COMPOSITE SAMPLES; HOT CORROSION; HOT CORROSION RESISTANCE; MOLTEN MIXTURES; SYNERGIC EFFECTS; THERMAL BARRIER COATING (TBC); YTTRIA-STABILIZED ZIRCONIAS (YSZ);

CORROSION RESISTANCE; THERMAL BARRIER COATINGS; ZIRCONIA; ZIRCONIUM ALLOYS;

TANTALUM OXIDES;

EID: 84880956589     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2013.06.025     Document Type: Article

References (40)

1. 3-stabilized zirconia thermal barrier coatings - crystal habit and phase composition. Surf. Coat. Technol. 1995, 82:259-269.
2. Rabiei A.G.E.A. Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings. Acta Mater. 2000, 48:3963-3976.
3. Ahmaniemi S., Vippola M., Vuoristo P., Mäntylä T., Cernuschi F., Lutterotti L. Modified thick thermal barrier coatings: microstructural characterization. J. Eur. Ceram. Soc. 2004, 24:2247-2258.
4. Cao X.Q., Vassen R., Stoever D. Ceramic materials for thermal barrier coatings. J. Eur. Ceram. Soc. 2004, 24:1-10.
5. Levi C.G. Emerging materials and processes for thermal barrier systems. Curr. Opin. Solid State Mater. Sci. 2004, 8:77-91.
6. Xie L., Dorfman M.R., Cipitria A., Paul S., Golosnoy I.O., Clyne T.W. Properties and performance of high-purity thermal barrier coatings. J. Therm. Spray Technol. 2007, 16:804-808.
7. Ahmaniemi S., Vuoristo P., Mäntylä T., Gualco C., Bonadei A., Di Maggio R. Thermal cycling resistance of modified thick thermal barrier coatings. Surf. Coat. Technol. 2005, 190:378-387.
8. 19 composite coatings in molten sulfate-vanadate salt. Corros. Sci. 2011, 53:2335-2343.
9. 4-10wt.% NaCl melt. Corros. Sci. 2010, 52:2592-2602.
10. 3 Co-doped zirconias for thermal barrier coatings. J. Am. Ceram. Soc. 2004, 87:431-437.
11. Haynes M.K.F.J.A., Porter W.D. Thermal cycling behavior of plasma-sprayed thermal barrier coatings with various MCrAIX bond coats. J. Therm. Spray Technol. 2000, 9:38-48.
12. Brandon J.R., Taylor R. Thermal properties of ceria and yttria partially stabilized zirconia thermal barrier coatings. Surf. Coat. Technol. 1989, 39-40(Part 1):143-151.
13. Jones R.L. Some aspects of the hot corrosion of thermal barrier coatings. J. Therm. Spray Technol. 1997, 6:77-84.
14. Ramachandran C.S., Balasubramanian V., Ananthapadmanabhan P.V., Viswabaskaran V. Influence of the intermixed interfacial layers on the thermal cycling behaviour of atmospheric plasma sprayed lanthanum zirconate based coatings. Ceram. Int. 2012, 38:4081-4096.
15. 5 stabilized orthorhombic zirconia for thermal barrier coating applications. Surf. Coat. Technol. 2002, 160:187-196.
16. Braue W. Environmental stability of the YSZ layer and the YSZ/TGO interface of an in-service EB-PVD coated high-pressure turbine blade. J. Mater. Sci. 2009, 44:1664-1675.
17. 4 using impedance spectroscopy. Corros. Sci. 2011, 53:1369-1374.
18. 5 at temperatures of 600-800°C in air. Corros. Sci. 2010, 52:3568-3572.
19. Yugeswaran S., Kobayashi A., Ananthapadmanabhan P.V. Initial phase hot corrosion mechanism of gas tunnel type plasma sprayed thermal barrier coatings. Mater. Sci. Eng. B-Solid 2012, 177:536-542.
20. 3. Mater. Sci. Eng. A-Struct. 2008, 478:264-269.
21. 5 at 1050°C. J. Eur. Ceram. Soc. 2012, 32:1635-1642.
22. Afrasiabi A., Kobayashi A. Hot corrosion control in plasma sprayed YSZ coating by alumina layer with evaluation of microstrcuture and nanoindentation data (H, E). Vacuum 2013, 88:103-107.
23. 5 molten salt. Ceram. Int. 2012, 38:6613-6620.
24. Park S.Y., Kim J.H., Kim M.C., Song H.S., Park C.G. Microscopic observation of degradation behavior in yttria and ceria stabilized zirconia thermal barrier coatings under hot corrosion. Surf. Coat. Technol. 2005, 190:357-365.
25. Chen Z., Mabon J., Wen J.-G., Trice R. Degradation of plasma-sprayed yttria-stabilized zirconia coatings via ingress of vanadium oxide. J. Eur. Ceram. Soc. 2009, 29:1647-1656.
26. Mohan P., Yuan B., Patterson T., Desai V.H., Sohn Y.H. Degradation of yttria-stabilized zirconia thermal barrier coatings by vanadium pentoxide, phosphorous pentoxide, and sodium sulfate. J. Am. Ceram. Soc. 2007, 90:3601-3607.
27. 5 at 1050°C. Supplemental Proceedings, Materials Processing and Energy Materials 2011, John Wiley & Sons, Inc., Hoboken, NJ, USA. http://dx.doi.org/10.1002/9781118062111.ch48. 1.
28. Jones R.L., Williams C.E. Hot corrosion studies of zirconia ceramics. Surf. Coat. Technol. 1987, 32:349-358.
29. Jones R.L. Vanadate-sulfate melt thermochemistry relating to hot corrosion of thermal barrier coatings. Nav. Res. Lab. 1997, 1-23.
30. Chen Z., Speakman S., Howe J., Wang H., Porter W., Trice R. Investigation of reactions between vanadium oxide and plasma-sprayed yttria-stabilized zirconia coatings. J. Eur. Ceram. Soc. 2009, 29:1403-1411.
31. 7 thermal barrier coatings. J. Eur. Ceram. Soc. 2012, 32:823-834.
32. 2 system. J. Eur. Ceram. Soc. 2011, 31:2897-2901.
33. 2.5 system. Surf. Coat. Technol. 2007, 201:6044-6050.
34. Brandon J.R., Taylor R. Phase stability of zirconia-based thermal barrier coatings part II. Zirconia-ceria alloys. Surf. Coat. Technol. 1991, 46:91-101.
35. Raghavan H.W.S., Porter W.D., Dinwiddie R.B., Mayo M.J. Thermal properties of zirconia co-doped with trivalent and pentavalent oxides. Acta Mater. 2001, 49:169-179.
36. 2 system: experimental study and preliminary thermodynamic description. J. Eur. Ceram. Soc. 2011, 31:691-695. 249-257.
37. 2.5-stabilized tetragonal zirconia ceramics. Acta Mater. 2010, 58:4424-4431.
38. 2 systems: structure, surface acidity, and catalytic properties. Chem. Mater. 2007, 19:1445-1451.
39. Hertl W. Vanadia reaction with yttria stabilized zirconia. J. Appl. Phys. 1988, 63:5514-5520.
40. 5. Cryst. Res. Technol. 1992, 27:691-695.