Environmental assisted cracking behavior of sigmatized super duplex stainless steel in oilfield production brine

Corrosion

Volumn 69, Issue 3, 2013, Pages 276-285

  Saithala, J R ^a   Mahajanam, S ^b   Ubhi, H S ^c   Atkinson, J ^d  

^a GL Noble Denton   (United Kingdom)

^b Production Assurance Technology   (United States)

^c OXFORD INSTRUMENTS PLASMA TECHNOLOGY   (United Kingdom)

^d SHEFFIELD HALLAM UNIVERSITY   (United Kingdom)

Author keywords

Electron backscattered diffraction; Sigma phase; Stress corrosion cracking; Super duplex stainless steel

Indexed keywords

ENVIRONMENTAL ASSISTED CRACKINGS; FRACTOGRAPHIC OBSERVATIONS; MECHANICAL AND CORROSION PROPERTIES; OILFIELD PRODUCTION; SIGMA PHASE; SLOW STRAIN RATE TESTS; SUPER DUPLEX STAINLESS STEEL; TRANSGRANULAR CRACKING;

BRITTLE FRACTURE; CARBON DIOXIDE; CRACK TIPS; DIFFRACTION; DUCTILE FRACTURE; SCANNING ELECTRON MICROSCOPY; STAINLESS STEEL; STRAIN; STRESS CORROSION CRACKING;

CRACKS;

EID: 84876265951     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/0696     Document Type: Article

References (22)

1. H. Sieurin, R. Sandstorm, Mater. Sci. Eng., A 444 (2007): p. 271-276.
2. T. Borvik, H. Lange, L.A. Marken, M. Langseth, O.S. Hopperstad, M. Aursand, G. Rorvik, Mater. Sci. Eng., A 527 (2010): p. 6945-6955.
3. S.P.V. Mahajanam, R.P. Case, H.E. Rincon, D.R. McIntyre, M.W. Joosten, S. Gjesdal, H. Monsen, Corrosion 67, 12 (2011): p. 125002-1-125002-14, doi: http://dx.doi.org/10.5006/1.3665356.
4. S. Mahajanam, R.P. Case, H.E. Rincon, D.R. McIntyre, M.W. Joosten, S. Gjesdal, H. Monsen, "Effect of Sigma Phase on the Corrosion and Stress Corrosion of 2205 and 2507 Duplex Stainless Steels," CORROSION/2011, paper no 11173 (Houston, TX: NACE International, 2011).
5. C.J. Park, V. Shankar Rao, H.S. Kwon, Corrosion 61, 1 (2005): p. 76-83, doi: http://dx.doi.org/10.5006/1.3278163.
6. W.-T. Tsai, M.-S. Chen, Corros. Sci. 42 (2000): p. 545-559.
7. R. Oltra, A. Desestret, E. Mirabal, J.P. Bizouard, Corros. Sci. 27, 10/11 (1987): p. 1251-1269.
8. S.T. Tsai, K.P. Yen, H.C. Shih, Corros. Sci. 40, 2/3 (1998): p. 281-295.
9. K. Van Gelder, J.G. Erlings, J.W.M. Damen, A. Visser, Corros. Sci. 27, 10/11 (1987): p. 1271-1279.
10. H.-S. Kwon, H.-S. Kim, Mater. Sci. Eng., A 72 (1993): p. 159-166.
11. R.F.A. Jargelius, R. Blom, S. Hertzman, J. Linder, "Chloride Induced Stress Corrosion Cracking of Duplex Stainless Steels in Concentrated Chloride Environments," in Duplex Stainless Steels (Beaune, France, 1991), p. 211-220.
12. J.R. Saithala, J.D. Atkinson, H.S. Ubhi, "Stress Corrosion Cracking of Super Duplex Stainless Steels Above and Below Pitting Potentials," CORROSION/2009, paper no 09300 (Houston, TX: NACE, 2009).
13. ASTM G129-00 "Standard Practice for Slow Stress Rate Testing to Evaluate the Susceptibility of Metallic Materials to Environmentally Assisted Cracking" (West Conshohocken, PA: ASTM International, 2000).
14. NACE TM0198, "Slow Strain Rate Test Method for Screening Corrosion- Resistant Alloys (CRAs) for Stress Corrosion Cracking in Sour Oilfield Service" (Houston, TX: NACE, 2004).
15. J. Saithala, S. Mahajanam, H. Rincon, U. Singh, "Effect of Sigma Phase on the EAC of Super Duplex Stainless Steel in Oil Field Environments," paper no. C2012-0001272 (Houston, TX: NACE, 2012).
16. J.R. Saithala, H.S. Ubhi, J.D. Atkinson, "Corrosion Behavior of Lean Duplex, Duplex, and Super Duplex Stainless Steels," Duplex Stainless Steels, paper no. 111.B.6 (Beaune France, 2010).
17. J.R. Saithala, H.S. Ubhi, J.D. Atkinson, "Pitting Corrosion Mechanisms of Lean Duplex, Duplex, and Super Duplex Stainless Steels in Chloride Solutions at Elevated Temperatures," CORROSION/ 2011, paper no. 11255 (Houston, TX: NACE, 2011).
18. R. Sriram, D. Tromans, Corrosion 45, 10 (1989): p. 804-810, doi: http://dx.doi.org/10.5006/1.3584986.
19. R. Magnabosco, N. Alonso-Falleiros, Corrosion 61, 2 (2005): p. 130-136, doi: http://dx.doi.org/10.5006/1.3278167.
20. J.S. Ubhi, J.R. Saithala, "An EBSD Study of Microstructural Development During Annealing in Super Duplex Stainless Steels," paper no. 0238, BAO Steel Conf. (China: BAO Steel quarterly supplement issue, 2010), p. 115.
21. A.A. El-Yazgi, D. Hardie, Corros. Sci. 40, 6 (1998).
22. M.A. Dominguez-Aguilar, R.C. Newman, Corros. Sci. 48 (2006): p. 2560-2576.