Microstructure and phase evolution during the dealloying of bi-phase Al-Ag alloy

Corrosion Science

Volumn 68, Issue , 2013, Pages 256-262

  Song, T T ^a,b   Gao, Y L ^a   Zhang, Z H ^c   Zhai, Q J ^a  

^a SHANGHAI UNIVERSITY   (China)

^b UNIVERSITY OF QUEENSLAND   (Australia)

^c SHANDONG UNIVERSITY   (China)

Author keywords

A. Alloy; A. Silver; B. Potentiostatic; C. Dealloying

Indexed keywords

AG ATOMS; DEALLOYING; INITIAL STAGES; PHASE EVOLUTIONS; POTENTIOSTATICS; ROLE OF DIFFUSION; TIME DEPENDENCE;

ATOMS; DIFFUSION; SILVER; SILVER ALLOYS;

ALUMINUM;

EID: 84872170236     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2012.11.027     Document Type: Article

References (54)

1. Xu C., Xu X., Su J., Ding Y. Research on unsupported nanoporous gold catalyst for CO oxidation. J. Catal. 2007, 252:243-248.
2. Zeis R., Lei T., Sieradzki K., Snyder J., Erlebacher J. Catalytic reduction of oxygen and hydrogen peroxide by nanoporous gold. J. Catal. 2008, 253:132-138.
3. Wang X., Wang W., Qi Z., Zhao C., Ji H., Zhang Z. High catalytic activity of ultrafine nanoporous palladium for electro-oxidation of methanol, ethanol, and formic acid. Electrochem. Commun. 2009, 11:1896-1899.
4. Qiu H., Xue L., Ji G., Zhou G., Huang X., Qu Y., Gao P. Enzyme-modified nanoporous gold-based electrochemical biosensors. Biosens. Bioelectron. 2009, 24:3014-3018.
5. Jin H.J., Wang X.L., Parida S., Wang K., Seo M., Weissmuller J. Nanoporous Au-Pt alloys as large strain electrochemical actuators. Nano Lett. 2010, 10:187-194.
6. Qiu H., Lu L., Huang X., Zhang Z., Qu Y. Immobilization of horseradish peroxidase on nanoporous copper and its potential applications. Bioresour. Technol. 2010, 101:9415-9420.
7. Qiu H., Xu C., Huang X., Ding Y., Qu Y., Gao P. Adsorption of lacease on the surface of nanoporous gold and the direct electron transfer between them. J. Phys. Chem. C 2008, 112:14781-14785.
8. Newman R.C., Sieradzki K. Metallic corrosion. Science 1994, 263:1708-1709.
9. Erlebacher J., Aziz M.J., Karma A., Dimitrov N., Sieradzki K. Evolution of nanoporosity in dealloying. Nature 2001, 410:450-453.
10. Lee H.O., Kim E.M., Yu H., Jung J., Chae W. Advanced porous gold nanofibers for highly efficient and stable molecular sensing platforms. Nanotechnology 2009, 20:3256041-3256046.
11. Johnston K.P., Shah P.S. Making nanoscale materials with supercritical fluids. Science 2004, 303:482-483.
12. Wang X., Qi Z., Zhao C., Wang W., Zhang Z. Influence of alloy composition and dealloying solution on the formation and microstructure of monolithic nanoporous silver through chemical dealloying of Al-Ag alloys. J. Phys. Chem. C 2009, 113:13139-13150.
13. Ding Y., Kim Y.-J., Erlebacher J. Nanoporous gold leaf: "ancient technology" /advanced material. Adv. Mater. 2004, 16:1897-1900.
14. Liu W.B., Zhang S.C., Li N., Zheng J.W., Xing Y.L. A facile one-pot route to fabricate nanoporous copper with controlled hierarchical pore size distributions through chemical dealloying of Al-Cu alloy in an alkaline solution. Microporous Mesoporous Mater. 2011, 138:1-7.
15. Chen Y.-C.K., Chu Y.S., Yi J., McNulty I., Shen Q., Voorhees P.W., Dunand D.C. Morphological and topological analysis of coarsened nanoporous gold by x-ray nanotomography. Appl. Phys. Lett. 2010, 96:431221-431223.
16. Hakamada M., Mabuchi M. Preparation of nanoporous palladium by dealloying: anodic polarization behaviors of Pd-M (M=Fe, Co, Ni) alloys. Mater. Trans. 2009, 50:431-435.
17. 4. J. Alloys Compd. 2010, 494:309-314.
18. Forty A.J. Corrosion micromorphology of noble metal alloys and depletion gilding. Nature 1979, 282:597-598.
19. Sieradzki K. Curvature effects in alloy dissolution. J. Electrochem. Soc. 1993, 140:2868-2872.
20. Sun Y., Balk T.J. Evolution of structure, composition, and stress in nanoporous gold thin films with grain-boundary cracks. Metall. Mater. Trans. A 2008, 39:2656-2665.
21. Liu Z., Searson P.C. Single nanoporous gold nanowire sensors. J. Phys. Chem. B 2006, 110:4318-4322.
22. Ji C., Searson P.C. Synthesis and characterization of nanoporous gold nanowires. J. Phys. Chem. B 2003, 107:4494-4499.
23. Dixon M.C., Daniel T.A., Hieda M., Smilgies D.M., Chan M.H.W., Allara D.L. Preparation, structure, and optical properties of nanoporous gold thin films. Langmuir 2007, 23:2414-2422.
24. Hakamada M., Mabuchi M. Microstructural evolution in nanoporous gold by thermal and acid treatments. Mater. Lett. 2008, 62:483-486.
25. Petegem S.V., Brandstetter S., Maass R., Hodge A.M., El-Dasher B.S., Biener J., Schmitt B., Borca C., Swygenhoven H.V. On the microstructure of nanoporous gold: an X-ray diffraction study. Nano Lett. 2009, 9:1158-1163.
26. Liu L., Pippel E., Scholz R., Gosele U. Nanoporous Pt-Co alloy nanowires: fabrication, characterization, and electrocatalytic properties. Nano Lett. 2009, 9:4352-4358.
27. Chen L.-Y., Yu J.-S., Fujita T., Chen M.-W. Nanoporous copper with tunable nanoporosity for SERS applications. Adv. Funct. Mater. 2009, 19:1221-1226.
28. Qi Z., Zhao C., Wang X., Lin J., Shao W., Zhang Z., Bian X. Formation and characterization of monolithic nanoporous copper by chemical dealloying of AlCu alloys. J. Phys. Chem. C 2009, 113:6694-6698.
29. Zhao C., Qi Z., Wang X., Zhang Z. Fabrication and characterization of monolithic nanoporous copper through chemical dealloying of Mg-Cu alloys. Corros. Sci. 2009, 51:2120-2125.
30. Lu H.-B., Li Y., Wang F.-H. Dealloying behaviour of Cu-20Zr alloy in hydrochloric acid solution. Corros. Sci. 2006, 48:2106-2119.
31. Lu H.-B., Li Y., Wang F.-H. Synthesis of porous copper from nanocrystalline two-phase Cu-Zr film by dealloying. Scripta Mater. 2007, 56:165-168.
32. Zhang Q., Zhang Z.H. On the electrochemical dealloying of Al-based alloys in a NaCl aqueous solution. Phys. Chem. Chem. Phys. 2010, 12:1453-1472.
33. Lu X., Bischoff E., Spolenak R., Balk T.J. Investigation of dealloying in Au-Ag thin films by quantitative electron probe microanalysis. Scripta Mater. 2007, 56:557-560.
34. Qian S., Newman R.C., Cottis R.A., Sieradzki K. Computer simulation of alloy passivation and activation. Corros. Sci. 1990, 31:621-626.
35. Massalsky T.B. Binary Phase Diagrams 1986, Ohio, ASM, p. 8. second ed.
36. Smith A.J., Trimm D.L. The preparation of skeletal catalysts. Annu. Rev. Mater. Res. 2005, 35:127-142.
37. Yamauchi I., Kajiwara T., Mase T., Saraoka M. Formation of highly saturated Al-Ag precursor by rapid solidification for skeletal silver synthesis. J. Alloys Compd. 2002, 336:206-212.
38. Lu X., Balk T.J., Spolenak R., Arzt E. Dealloying of Au-Ag thin films with a composition gradient: Influence on morphology of nanoporous Au. Thin Solid Films 2007, 515:7122-7126.
39. Forty A.J. Micromorphological studies of the corrosion of gold alloys. Gold bull. 1981, 14:25-35.
40. Snyder J., Erlebacher J. Kinetics of crystal etching limited by terrace dissolution. J. Electrochem. Soc. 2010, 157:C125-C130.
41. Ji H., Zhang C., Xu J., Zhao C., Wang X., Zhang Z. On the vacancy-controlled dealloying of rapidly solidified Mg-Ag alloys. CrystEngComm 2011, 13:4846-4849.
42. Moore K.T., Johnson W.C., Howe J.M., Aaronson H.I., Veblen D.R. On the interaction between Ag-depleted zones surrounding [gamma] plates and spinodal decomposition in an Al-22at.% Ag alloy. Acta Mater. 2002, 50:943-956.
43. Song G., Atrens A., Stjohn D., Nairn J., Li Y. The electrochemical corrosion of pure magnesium in 1N NaCl. Corros. Sci. 1997, 39:855-875.
44. Liu W.B., Zhang S.C., Li N., Zheng J.W., An S.S., Xing Y.L. A general dealloying strategy to nanoporous intermetallics, nanoporous metals with bimodal, and unimodal pore size distributions. Corros. Sci. 2012, 58:133-138.
45. Dona J.M., Gonzalez-Velasco J. Mechanism of surface diffusion of gold adatoms in contact with an electrolytic solution. J. Phys. Chem. 1993, 97:4714-4719.
46. Zhang Z., Wang Y., Wang Y., Wang X., Qi Z., Ji H., Zhao C. Formation of ultrafine nanoporous gold related to surface diffusion of gold adatoms during dealloying of Al2Au in an alkaline solution. Scripta Mater. 2010, 62:137-140.
47. Zhang Z., Wang Y., Qi Z., Zhang W., Qin J., Frenzel J. Generalized fabrication of nanoporous metals (Au, Pd, Pt, Ag, and Cu) through chemical dealloying. J. Phys. Chem. C 2009, 113:12629-12636.
48. Qian L.H., Chen M.W. Ultrafine nanoporous gold by low-temperature dealloying and kinetics of nanopore formation. Appl. Phys. Lett. 2007, 91:083105.
49. Hirai N., Tanaka H., Hara S. Enhanced diffusion of surface atoms at metal/electrolyte interface under potential control. Appl. Surf. Sci. 1998, 130-132:506-511.
50. Sun Y., Balk T.J. A multi-step dealloying method to produce nanoporous gold with no volume change and minimal cracking. Scripta Mater. 2008, 58:727-730.
51. Xu C., Su J., Xu X., Liu P., Zhao H., Tian F., Ding Y. Low temperature CO oxidation over unsupported nanoporous gold. J. Amer. Chem. Soc. 2006, 129:42-43.
52. Zhang J., Liu P., Ma H., Ding Y. Nanostructured porous gold for methanol electro-oxidation. J. Phys. Chem. C 2007, 111:10382-10388.
53. Balluffi R.W., Allen S.M., Carter W.C., Kemper R.A. Kinetics of materials 2005, Wiley-Interscience, Hoboken, pp. 368-402. first ed.
54. Song T., Gao Y., Zhang Z., Zhai Q. Dealloying behavior of rapidly solidified Al-Ag alloys to prepare nanoporous Ag in inorganic and organic acidic media. CrystEngComm 2011, 13:7058-7067.