Influence of microstructural barriers on short fatigue crack growth

12th International Conference on Fracture 2009, ICF-12

Volumn 8, Issue , 2009, Pages 5866-5874

  Marx, M ^a   Schaf W ^a   Vehoff, H ^a  

^a SAARLAND UNIVERSITY   (Germany)

Author keywords

Crack tomography; Focused ion beam (FIB); Grain boundaries; Microstructural crack propagation

Indexed keywords

CRACK LENGTH; CRACK PATHS; INFLUENCING PARAMETERS; INITIATION SITES; ION BEAM MICROSCOPE; MICRO-STRUCTURAL; MICROSTRUCTURAL BARRIERS; MICROSTRUCTURAL ELEMENTS; NATURAL CRACKS; PHYSICAL PRINCIPLES; QUANTITATIVE DATA; SHORT CRACKS; SYSTEMATIC EXPERIMENT; SYSTEMATIC INVESTIGATIONS;

FOCUSED ION BEAMS; FRACTURE; GRAIN BOUNDARIES; TOMOGRAPHY;

CRACKS;

EID: 84869778304     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (11)

1. M. Marx, H. Vehoff: Microcracks in superalloys: From local in-situ measurements to lifetime prediction, Int. J. Mat. Res., 97 (2006) 1617-1626
2. G.P. Potirniche, S R. Daniewicz, J.C. Newman, Simulating small crack growth behaviour using crystal plasticity theory and finite element analysis, Fatigue & Fract. Eng. Mater. Struct. 27 (2004) 59-71.
3. M. Marx, W. Schäf, H. Vehoff, C. Holzapfel, Interaction of microcracks with selected interfaces: Focused ion beam for a systematic crack initiation, Mater. Sci. Eng. A 435-436 (2006) 595
4. M. Marx, W. Schaef, M. Welsch H. Vehoff, Local investigations of the interaction of microcracks with grain boundaries to quantify the qualitative models, J. of ASTM int. in press
5. M. T. Welsch, M. Marx, H. Vehoff, Local incompatibility stresses and dislocation structures during cyclic loading, this conference
6. M. T. Welsch, M. Henning, M. Marx, H. Vehoff, Measuring the plastic zone size by orientation gradient mapping (OGM) and electron channeling contrast imaging, Adv. Eng. Mater., 9 (2007) 31-37
7. K. Tanaka, Y. Akiniwa, Y. Nakai, R.P. Wei, Modelling of small fatigue crack growth interacting with grain boundary, Eng. Fracture Mech., 24 (1986) 803
8. A. Navarro, E. R. De Los Rios, Short and long Fatigue crack-growth - a unified model, Phil. Mag. A, 57 (1988) 15
9. O. Dueber, B. Kuenkler, U. Krupp, H. J. Christ, C. P. Fritzen, Int. J. Fatigue, 28 (2006) 983
10. T. Zhai, X.P. Jiang, X. J. Li, M. D. Garratt, G. H. Bray, The grain boundary geometry for optimum resistance to growth of short fatigue cracks in high strength Al-alloys, Int J Fatigue, 27 (2005) 1202
11. Holzapfel C., Schäf W., Marx M., Vehoff H., Mücklich F.: Interaction of cracks with precipitates and grain boundaries: Understanding crack growth mechanisms through FIB tomography, Scripta Mater., 56 (2007) 697-700