The effect of thermo-oxidation on matrix cracking of cross-ply [0/90] S composite laminates

Composites Part A: Applied Science and Manufacturing

Volumn 44, Issue 1, 2013, Pages 114-121

  Vu, Dinh Quy ^a   Gigliotti, Marco ^a   Lafarie Frenot, Marie Christine ^a  

^a UPR 3346   (France)

Author keywords

A. Polymer matrix composites (PMCs); B. Environmental degradation; C. Numerical analysis; D. Mechanical testing

Indexed keywords

APPLIED STRESS; CARBON/EPOXY; COMPOSITE LAMINATE; CRACK DENSITY; CRITICAL ENERGY RELEASE RATE; CROSS-PLY; INDUCED DAMAGE; LOCAL SCALE; MATRIX CRACK; MATRIX CRACKING; POLYMERMATRIX COMPOSITES (PMCS); QUASI-STATIC TENSILE TEST; SAMPLE SURFACE; TENSILE TESTS;

CRACKS; ENERGY RELEASE RATE; LAMINATES; NUMERICAL ANALYSIS; POLYMER MATRIX COMPOSITES; SCANNING ELECTRON MICROSCOPY; TENSILE TESTING;

OXIDATION;

EID: 84867583750     PISSN: 1359835X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compositesa.2012.08.013     Document Type: Article

References (29)

1. J.B. Nelson Long-term behavior of composites, ASTM STP 813 1983 American Society for Testing and Materials Philadelphia p. 206-21
2. Bowles KJ, Meyers AE. In: Covina CA, Bauer JL, Dunaetz R, editors. 31st International SAMPE symposium and exhibition, Society for The Advancement of Material and Process Engineering (SAMPE); 1986.
3. K.J. Bowles, and G. Nowak Thermo-oxidative stability studies of celion 6000/PMR-15 unidirectional composites, PMR-15, and celion 6000 fiber J Compos Mater 22 1988 966 985
4. X. Colin, C. Marais, and J. Verdu A new method for predicting the thermal oxidation of thermoset matrices: application to an amine crosslinked epoxy Polym Testing 20 7 2001 795 803 (Pubitemid 32724654)
5. X. Colin, C. Marais, and J. Verdu Kinetic modelling of the stabilizing effect of carbon fibres on thermal ageing of thermoset matrix composites Compos Sci Technol 65 1 2005 117 127 (Pubitemid 40234030)
6. S. Rouquie, M.C. Lafarie-Frenot, J. Cinquin, and A.M. Colombaro Thermal cycling of carbon/epoxy laminates in neutral and oxidative environments Compos Sci Technol 65 3-4 2005 403 409 (Pubitemid 40077553)
7. L. Olivier, N.Q. Ho, J.C. Grandidier, and M.C. Lafarie-Frenot Characterization by ultra-micro indentation of an oxidized epoxy polymer: correlation with the predictions of a kinetic model of oxidation Polym Degrad Stabil 93 2 2008 489 497
8. L. Olivier, C. Baudet, D. Bertheau, J.C. Grandidier, and M.C. Lafarie-Frenot Development of experimental, theoretical and numerical tools for studying thermo-oxidation of CFRP composites Compos A: Appl Sci Manuf 40 8 2009 1008 1016
9. M.C. Lafarie-Frenot, J.C. Grandidier, M. Gigliotti, L. Olivier, X. Colin, and J. Verdu Thermo-oxidation behaviour of composite materials at high temperatures: a review of research activities carried out within the COMEDI program Polym Degrad Stabil 95 6 2010 965 974
10. X. Colin, and J. Verdu Strategy for studying thermal oxidation of organic matrix composites Compos Sci Technol 65 3-4 2005 411 419 (Pubitemid 40077554)
11. D.Q. Vu, M. Gigliotti, and M.C. Lafarie-Frenot Experimental characterization of thermo-oxidation-induced shrinkage and damage in polymer-matrix composites Compos A: Appl Sci Manuf 43 4 2012 577 586
12. M. Gigliotti, L. Olivier, D.Q. Vu, J.C. Grandidier, and M.C. Lafarie-Frenot Local shrinkage and stress induced by thermo-oxidation in composite materials at high temperatures J Mech Phys Solids 59 3 2011 696 712
13. G.A. Schoeppner, G.P. Tandon, and E.R. Ripberger Anisotropic oxidation and weight loss in PMR-15 composites Compos A: Appl Sci Manuf 38 3 2007 890 904 (Pubitemid 44909024)
14. Vu DQ. Thermo-oxidation-induced damages in carbon/epoxy composite, PhD Thesis. Ecole Nationale Supérieure de Mécanique et d'Aérotechnique, published by Editions Universitaires Européennes; 2011. ISBN: 978-3-8417-8925-9
15. X. Colin, A. Mavel, C. Marais, and J. Verdu Interaction between cracking and oxidation in organic matrix composites J Compos Mater 39 15 2005 1371 1389 (Pubitemid 41165655)
16. G.P. Tandon, and W.R. Ragland Influence of laminate lay-up on oxidation and damage growth: isothermal aging Compos A: Appl Sci Manuf 42 9 2011 1127 1137
17. M.C. Lafarie-Frenot, and C. Hénaff-Gardin Formation and growth of 90° ply fatigue cracks in carbon/epoxy laminates Compos Sci Technol 40 3 1991 307 324
18. Hénaff-Gardin C. Influence de la séquence d'empilement sur la fissuration en fatigue des plis transverses de stratifiés à fibres longues, PhD Thesis. France: Université de Poitiers; 1990.
19. T. Palin-Luc, E. Sellier, F. D'Errico, and M. Vanhaeren Elastomer and resin replicas for SEM observation of metallic materials Exp Tech 26 2002 33 37 (Pubitemid 34789782)
20. J.A. Nairn, and D.A. Mendels On the use of planar shear-lag methods for stress-transfer analysis of multilayered composites Mech Mater 33 6 2001 335 362 (Pubitemid 32457490)
21. J.W. Lee, and I.M. Daniel Progressive transverse cracking of cross-ply composite laminates J Compos Mater 24 1990 1225 1243
22. J. Berthelot, P. Leblond, A. El Mahi, and J.F. Le Corre Transverse cracking of cross-ply laminates: Part 1. Analysis Compos A: Appl Sci Manuf 27 1996 989 1001 (Pubitemid 126341115)
23. J.A. Nairn Fracture mechanics of composites with residual thermal stresses J Appl Mech 64 1997 804 810 (Pubitemid 127754975)
24. Z. Hashin Finite thermoelastic fracture criterion with application to laminate cracking analysis J Mech Phys Solids 44 1996 1129 1145 (Pubitemid 126374367)
25. Y. Han, H. Hahn, and R. Croman A simplified analysis of transverse ply cracking in cross-ply laminates Compos Sci Technol 31 1988 165 177 (Pubitemid 18611125)
26. Hahn H, Han Y, Kim R. Resistance curves for ply cracking in composite laminates. In: 33rd international SAMPE, symposium; 1988.
27. K. Ogi, and Y. Takao Modeling of time-dependent behaviour of deformation and transverse cracking in cross-ply laminates Adv Compos Mater 10 1 2001 39 62 (Pubitemid 32887684)
28. V. Vinogradov, and Z. Hashin Probabilistic energy based model for prediction of transverse cracking in cross-ply laminates Int J Solids Struct 42 2005 365 392
29. Lamon J. Mécanique de la rupture fragile et de l'endommagement: approches statistiques et probabilistes, Lavoisier; 2007.