Experimental characterization of thermo-oxidation-induced shrinkage and damage in polymer-matrix composites

Composites Part A: Applied Science and Manufacturing

Volumn 43, Issue 4, 2012, Pages 577-586

  Vu, Dinh Quy ^a   Gigliotti, Marco ^a   Lafarie Frenot, Marie Christine ^a  

^a CNRS   (France)

Author keywords

A. Polymer matrix composites (PMCs); B. Environmental degradation; D. Electron microscopy; D. Surface analysis

Indexed keywords

A. POLYMER-MATRIX COMPOSITES (PMCS); AGING TIME; ATMOSPHERIC AIR; COMPOSITE SPECIMENS; EXPERIMENTAL CHARACTERIZATION; INTERFEROMETRIC MICROSCOPY; MICROSCOPIC SCALE; OXYGEN PRESSURE; PARTIAL OXYGEN PRESSURES; PERIODIC TESTS; SAMPLE SURFACE;

DEGRADATION; OXYGEN; POLYMER MATRIX COMPOSITES; POLYMERS; SCANNING ELECTRON MICROSCOPY; SHRINKAGE; SURFACE ANALYSIS; WEATHERING;

OXIDATION;

EID: 84856349181     PISSN: 1359835X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compositesa.2011.12.018     Document Type: Article

References (16)

1. X. Colin, C. Marais, and J. Verdu A new method for predicting the thermal oxidation of thermoset matrices: application to an amine crosslinked epoxy Polym Test 20 7 2001 795 803 (Pubitemid 32724654)
2. A. Schieffer, J.-F. Maire, and D. Lévêque A coupled analysis of mechanical behaviour and ageing for polymer-matrix composites Compos Sci Technol 62 4 2002 543 549 (Pubitemid 34213089)
3. M.C. Lafarie-Frenot Damage mechanisms induced by cyclic ply-stresses in carbon-epoxy laminates: environmental effects Int J Fatigue 28 10 2006 1202 1216 (Pubitemid 44102678)
4. K.V. Pochiraju, G.P. Tandon, and G.A. Schoeppner Evolution of stress and deformations in high-temperature polymer matrix composites during thermo-oxidative aging Mech Time-Depend Mater 12 1 2008 45 68
5. L. Olivier, N.Q. Ho, J.C. Grandidier, and M.C. Lafarie-Frenot Characterization by ultra-micro indentation of an oxidized epoxy polymer: correlation with the predictions of a kinetic model of oxidation Polym Degrad Stab 93 2 2008 489 497
6. S. Putthanarat, G. Tandon, and G. Schoeppner Influence of aging temperature, time, and environment on thermo-oxidative behavior of PMR-15: nanomechanical characterization J Mater Sci 43 20 2008 6714 6723
7. G.A. Schoeppner, G.P. Tandon, and E.R. Ripberger Anisotropic oxidation and weight loss in PMR-15 composites Composites Part A 38 3 2007 890 904 (Pubitemid 44909024)
8. S. Ciutacu, P. Budrugeac, and I. Niculae Accelerated thermal aging of glass-reinforced epoxy resin under oxygen pressure Polym Degrad Stab 31 3 1991 365 372
9. T.K. Tsotsis, S. Keller, K. Lee, J. Bardis, and J. Bish Aging of polymeric composite specimens for 5000 hours at elevated pressure and temperature Compos Sci Technol 61 1 2001 75 86
10. T.K. Tsotsis, and S.M. Lee Long-term thermo-oxidative aging in composite materials: Failure mechanisms Compos Sci Technol 58 3-4 1998 355 368 (Pubitemid 28400467)
11. J. Decelle, N. Huet, and V. Bellenger Oxidation induced shrinkage for thermally aged epoxy networks Polym Degrad Stab 81 2 2003 239 248
12. X. Colin, A. Mavel, C. Marais, and J. Verdu Interaction between cracking and oxidation in organic matrix composites J Compos Mater 39 15 2005 1371 1389 (Pubitemid 41165655)
13. Tandon GP, Ripberger ER, Schoeppner GA. Accelerated aging of PMR-15 resin at elevated pressure and/or temperature. In: Proceedings of the SAMPE 2005 symposium and exhibition, 2005, Seattle, WA; 2005.
14. Ripberger E, Tandon GP, Schoeppner GA. Characterizing oxidative degradation of PMR-15 resin. In: Proceedings of the spring SAMPE 2004 symposium/exhibition, 2004, Long Beach, CA; 2004.
15. T.K. Tsotsis, S. Keller, J. Bardis, and J. Bish Preliminary evaluation of the use of elevated pressure to accelerate thermo-oxidative aging in composites Polym Degrad Stab 64 2 1999 207 212
16. L. Olivier, C. Baudet, D. Bertheau, J.C. Grandidier, and M.C. Lafarie-Frenot Development of experimental, theoretical and numerical tools for studying thermo-oxidation of CFRP composites Composites Part A 40 8 2009 1008 1016