High temperature failure of natural gas feed burner pipe

Engineering Failure Analysis

Volumn 27, Issue , 2013, Pages 74-83

  Kaewkumsai, S ^a   Khonraeng, W ^a   Sathirachinda, N ^a  

^a NATIONAL METAL AND MATERIALS TECHNOLOGY CENTER   (Thailand)

Author keywords

Carbide precipitation; Carburization; High temperature failure; Metal dusting

Indexed keywords

CARBIDE PRECIPITATE; CARBIDE PRECIPITATION; CARBURIZATION; FAILURE PREVENTION; HIGH TEMPERATURE; HIGH TEMPERATURE FAILURE; INTERNAL SURFACES; MATERIAL SELECTION; METAL DUSTING; MICROHARDNESS MEASUREMENT; REDUCING ATMOSPHERE; SCALE SEPARATION; SERVICE CONDITIONS; SERVICE TEMPERATURE;

AUSTENITIC STAINLESS STEEL; CARBIDES; ENERGY DISPERSIVE SPECTROSCOPY; OPTICAL MICROSCOPY; SCANNING ELECTRON MICROSCOPY; X RAY DIFFRACTION;

SPALLING;

EID: 84867047343     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2012.08.004     Document Type: Article

References (17)

1. 2 carburizing gas mixture at high temperatures. Mater Sci Eng A 2005, 391:19-28.
2. 2 gas mixture. Corros Sci 2005, 47(8):1896-1910.
3. 4 mixtures at 750°C. Mater Chem Phys 2005, 89(2-3):445-453.
4. Tawancy H.M. Degradation of mechanical strength of pyrolysis furnace tubes by high-temperature carburization in a petrochemical plant. Eng Fail Anal 2009, 16(7):2171-2178.
5. ASM Specialty handbook. stainless steels. vol. 4. ASM International; 1996.
6. Hänsel M., Boddington C.A., Young D.J. Internal oxidation and carburisation of heat-resistant alloys. Corros Sci 2003, 45(5):967-981.
7. Zhang J., Young D.J. Kinetics and mechanisms of nickel metal dusting I kinetics and morphology. Corros Sci 2007, 49(3):1496-1512.
8. Tabet N., Allam I., Yin R. X-ray photoelectron spectroscopy investigation of the carburization of 310 stainless steel. Appl Surf Sci 2003, 220(1-4):259-272.
9. Metals Handbook. Failure analysis and prevention. vol. 11. Ohio: ASM Int Metals Park; 1995.
10. Li H., Zheng Y., Benum L.W., Oballa M., Chen W. Carburization behaviour of Mn-Cr-O spinel in high temperature hydrocarbon cracking environment. Corros Sci 2009, 51(10):2336-2341.
11. Smith P.J., Van der Biest O., Corish J. The initial stages of high-temperature corrosion of Fe-Cr-Ni and Cr-Ni alloys in a carburizing atmosphere of low oxygen partial pressure. Oxid Met 1985, 24(1-2):47-83.
12. Chu W.F., Rahmel A. The conversion of chromium oxide to chromium carbide. Oxid Met 1981, 15(3-4):331-337.
13. Gojić M., Nagode A., Kosec B., KoŽuh S., Šavli Š., Holjevac-Grgurić T., et al. Failure of steel pipes for hot air supply. Eng Failure Anal 2011, 18(8):2330-2335.
14. Pandey R.K. Failure analysis of styrene reactor tubes. Eng Failure Anal 2006, 13(8):1314-1325.
15. Ul-Hamid A., Tawancy H.M., Mohammed A.I., Abbas N.M. Failure analysis of furnace radiant tubes exposed to excessive temperature. Eng Failure Anal 2006, 13:1005-1021.
16. Holland M.L., De Bruyn H.J. Metal dusting failures in methane reforming plant. Int J Pres Ves Piping 1996, 66:125-133.
17. Wysiekierski A.G., Fisher G., Schillmoller C.M. Control coking for olefins plants. Hydrocarb Process 1999, 78(1):97-100.