Effect of pulsed electromagnetic field on growth and structure properties of ZnO nanorod arrays

Journal of Nanoscience and Nanotechnology

Volumn 12, Issue 8, 2012, Pages 6385-6388

  Tang, Li Dan ^a   Wang, Bing ^a   Du, Huiling ^a   Wang, Jianzhong ^a  

^a LIAONING UNIVERSITY OF TECHNOLOGY   (China)

Author keywords

Hydrothermal Methods; Nanorod Arrays; Pulsed Electromagnetic Field; ZnO

Indexed keywords

HYDROTHERMAL METHODS; LENGTH TO DIAMETER RATIO; NANOROD ARRAYS; PULSED ELECTROMAGNETIC FIELDS; RAMAN ANALYSIS; SEM ANALYSIS; STRUCTURE PROPERTY; WELL-ALIGNED; WURTZITE STRUCTURE; XRD; ZNO; ZNO NANOROD ARRAYS;

ELECTROMAGNETIC FIELDS; ZINC OXIDE; ZINC SULFIDE;

NANORODS;

EID: 84865147134     PISSN: 15334880     EISSN: 15334899     Source Type: Journal    
DOI: 10.1166/jnn.2012.6422     Document Type: Conference Paper

References (18)

1. A. Hagfeldt and M. Grätzel, Acc. Chem. Res. 33, 269 (2000).
2. M. Grätzel, Nature 414, 338 (2001).
3. K. Tennakone, G. R. R. A. Kumara, I. R. M. Kottegoda, and V. P. S. Perera, Chem. Commun. 1, 15 (1999).
4. S. T. Aruna, S. Tirosh, and A. Zaban, J. Mater. Chem. 10, 2388 (2000).
5. Z. Qin, Q. Liao, Y. Huang, L. Tang, X. Zhang, and Y. Zhang, Mater. Chem. Phys. 123, 811. (2010).
6. W. Tan, X. Yin, X. Zhou, J. Zhang, X. Xiao, and Y. Lin, Electrochim. Acta 54, 4467 (2009).
7. D. Pradhan and K. T. Leung, Langmuir 24, 9707 (2008).
8. L. E. Greene, M. Law, D. H. Tan, M. Montano, J. Goldberger, G. Somorjai, and P. D. Yang, Nano Lett. 5, 1231. (2005).
9. L. Vayssieres, Adv. Mater. 15, 464 (2003).
10. X. Mo, C. Y. Wang, M. You, Y. Zhu, Z. Y. Chen, and Y. Hu, Mater. Res. Bull. 36, 2277 (2001).
11. H. Niu, Q. Chen, H. Zhu, Y. Lin, and X. Zhang, J. Mater. Chem. 13, 1803 (2003).
12. H. Du, J. Wang, B. Wang, and D. Cang, Powder Technology 199, 149 (2010).
13. C. A. Arguello, D. L. Rousseau, and S. P. S. Porto, Phys. Rev. 181, 1351. (1969).
14. J. M. Calleja and M. Cardona, Phys. Rev. B. 16, 3753 (1977).
15. J. Serrano, A. H. Romeo, F. J. Manjón, R. Lauck, M. Cardona, and A. Rubio, Phys. Rev. B. 69, 094306 (2004).
16. M. S. Jang, M. K. Ryu, M. H. Yoon, S. H. Lee, H. K. Kim, A. Onodera, and S. Kojima, Curr. Appl. Phys. 9, 651. (2009).
17. F. Li, Y. Jiang, L. Hu, L. Liu, Z. Li, and X. Huang, J. Alloys Compd. 474, 531. (2009).
18. S. Ashoka, G. Nagaraju, C. N. Tharamani, and G. T. Chandrapp, Mater. Lett. 63, 873 (2009).