Resistance to fracture of roots filled with different sealers

Dental Materials Journal

Volumn 31, Issue 4, 2012, Pages 528-532

  Saǧsen, Burak ^a   Üstün, Yakup ^a   Pala, Kanşad ^a   Demirbuǧa, Sezer ^a  

^a ERCIYES UNIVERSITY   (Turkey)

Author keywords

Calcium silicate based root canal sealers; Epoxy resin based root canal sealers; Fracture resistance; Root canal sealer

Indexed keywords

COMPRESSIVE LOADING; CONTROL GROUPS; EXPERIMENTAL GROUPS; GROUP 4; GUTTAPERCHA; ROOT CANAL SEALERS; ROOT CANALS; UNIVERSAL TESTING MACHINES;

CALCIUM SILICATE; EPOXY RESINS; FRACTURE; FRACTURE TOUGHNESS; HYDRAULIC STRUCTURES; RESINS;

CANALS;

ALUMINUM DERIVATIVE; CALCIUM DERIVATIVE; CALCIUM SILICATE; EPOXY RESIN; GUTTA PERCHA; MINERAL TRIOXIDE AGGREGATE; OXIDE; ROOT CANAL FILLING MATERIAL; SILICATE;

ARTICLE; CHEMISTRY; COMPARATIVE STUDY; COMPRESSIVE STRENGTH; DENTAL PROCEDURE; DRUG COMBINATION; ENDODONTICS; HUMAN; METHODOLOGY; TOOTH FRACTURE;

ALUMINUM COMPOUNDS; CALCIUM COMPOUNDS; COMPRESSIVE STRENGTH; DENTAL STRESS ANALYSIS; DRUG COMBINATIONS; EPOXY RESINS; GUTTA-PERCHA; HUMANS; OXIDES; ROOT CANAL FILLING MATERIALS; ROOT CANAL THERAPY; SILICATES; TOOTH FRACTURES;

EID: 84864693719     PISSN: 02874547     EISSN: 18811361     Source Type: Journal    
DOI: 10.4012/dmj.2011-266     Document Type: Article

References (37)

1. Helfer AR, Melnick S, Schilder H. Determination of the moisture content of vital and pulpless teeth. Oral Surg Oral Med Oral Pathol 1972; 34: 661-670.
2. Oliveira Fde C, Denehy GE, Boyer DB. Fracture resistance of endodontically prepared teeth using various restorative materials. J Am Dent Assoc 1987; 115: 57-60.
3. Reeh ES, Messer HH, Douglas WH. Reduction in tooth stiffness as a result of endodontic and restorative procedures. J Endod 1989; 15: 512-516.
4. Sornkul E, Stannard JG. Strength of roots before and after endodontic treatment and restoration. J Endod 1992; 18: 440-443.
5. Karapinar Kazandag M, Sunay H, Tanalp J, Bayirli G. Fracture resistance of roots using different canal filling systems. Int Endod J 2009; 42: 705-710.
6. Lee KW, Williams MC, Camps JJ, Pashley DH. Adhesion of endodontic sealers to dentin and gutta-percha. J Endod 2002; 28: 684-688.
7. Teixeira FB, Teixeira EC, Thompson J, Leinfelder KF, Trope M. Dentinal bonding reaches the root canal system. J Esthet Restor Dent 2004; 16: 348-354.
8. Teixeira FB, Teixeira EC, Thompson JY, Trope M. Fracture resistance of roots endodontically treated with a new resin filling material. J Am Dent Assoc 2004; 135: 646-652.
9. Sagsen B, Er O, Kahraman Y, Akdogan G. Resistance to fracture of roots filled with three different techniques. Int Endod J 2007; 40: 31-35.
10. Ulusoy OI, Genc O, Arslan S, Alacam T, Gorgul G. Fracture resistance of roots obturated with three different materials. Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2007; 104: 705-708.
11. Belli S, Cobankara FK, Eraslan O, Eskitascioglu G, Karbhari V. The effect of fiber insertion on fracture resistance of endodontically treated molars with MOD cavity and reattached fractured lingual cusps. J Biomed Mater Res B Appl Biomater 2006; 79: 35-41.
12. Sim TP, Knowles JC, Ng YL, Shelton J, Gulabivala K. Effect of sodium hypochlorite on mechanical properties of dentine and tooth surface strain. Int Endod J 2001; 34: 120-132.
13. Eakle WS. Fracture resistance of teeth restored with class II bonded composite resin. J Dent Res 1986; 65: 149-153.
14. Marshall GW, Jr. Dentin: microstructure and characterization. Quintessence Int 1993; 24: 606-617.
15. Versluis A, Messer HH, Pintado MR. Changes in compaction stress distributions in roots resulting from canal preparation. Int Endod J 2006; 39: 931-939.
16. Weiger R, Heuchert T, Hahn R, Lost C. Adhesion of a glass ionomer cement to human radicular dentine. Endod Dent Traumatol 1995; 11: 214-219.
17. White RR, Goldman M, Lin PS. The influence of the smeared layer upon dentinal tubule penetration by plastic filling materials. J Endod 1984; 10: 558-562.
18. White RR, Goldman M, Lin PS. The influence of the smeared layer upon dentinal tubule penetration by endodontic filling materials. Part II. J Endod 1987; 13: 369-374.
19. Chen RS, Liu CC, Cheng MR, Lin CP. Bonded amalgam restorations: using a glass-ionomer as an adhesive liner. Oper Dent 2000; 25: 411-417.
20. Dias de Souza GM, Pereira GD, Dias CT, Paulillo LA. Fracture resistance of premolars with bonded class II amalgams. Oper Dent 2002; 27: 349-353.
21. Heydecke G, Butz F, Strub JR. Fracture strength and survival rate of endodontically treated maxillary incisors with approximal cavities after restoration with different post and core systems: an in-vitro study. J Dent 2001; 29: 427-433.
22. Loney RW, Moulding MB, Ritsco RG. The effect of load angulation on fracture resistance of teeth restored with cast post and cores and crowns. Int J Prosthodont 1995; 8: 247-251.
23. Schmalz G, Horsted-Bindslev P. Root canal filling materials. In: Bergenholtz G, Horsted-Bindslev P, Reit C, editors. Textbook of endodontology. 2nd ed. West Sussex, UK: Wiley & Blackwell; 2010. p. 202.
24. Saleh IM, Ruyter IE, Haapasalo MP, Orstavik D. Adhesion of endodontic sealers: scanning electron microscopy and energy dispersive spectroscopy. J Endod 2003; 29: 595-601.
25. Sousa-Neto MD, Marchesan MA, Pecora JD, Junior AB, Silva-Sousa YT, Saquy PC. Effect of Er:YAG laser on adhesion of root canal sealers. J Endod 2002; 28: 185-187.
26. Orstavik D, Eriksen HM, Beyer-Olsen EM. Adhesive properties and leakage of root canal sealers in vitro. Int Endod J 1983; 16: 59-63.
27. Jainaen A, Palamara JE, Messer HH. Effect of dentinal tubules and resin-based endodontic sealers on fracture properties of root dentin. Dent Mater 2009; 25: 73-81.
28. Mamootil K, Messer HH. Penetration of dentinal tubules by endodontic sealer cements in extracted teeth and in vivo. Int Endod J 2007; 40: 873-881.
29. Sousa-Neto MD, Silva Coelho FI, Marchesan MA, Alfredo E, Silva-Sousa YT. Ex vivo study of the adhesion of an epoxybased sealer to human dentine submitted to irradiation with Er:YAG and Nd:YAG lasers. Int Endod J 2005; 38: 866-870.
30. Cobankara FK, Ungor M, Belli S. The effect of two different root canal sealers and smear layer on resistance to root fracture. J Endod 2002; 28: 606-609.
31. Andreasen JO, Munksgaard EC, Bakland LK. Comparison of fracture resistance in root canals of immature sheep teeth after filling with calcium hydroxide or MTA. Dent Traumatol 2006; 22: 154-156.
32. Cauwels RG, Pieters IY, Martens LC, Verbeeck RM. Fracture resistance and reinforcement of immature roots with gutta percha, mineral trioxide aggregate and calcium phosphate bone cement: a standardized in vitro model. Dent Traumatol 2010; 26: 137-142.
33. Torabinejad M, Hong CU, McDonald F, Pitt Ford TR. Physical and chemical properties of a new root-end filling material. J Endod 1995; 21: 349-353.
34. Hurmuzlu F, Serper A, Siso SH, Er K. In vitro fracture resistance of root-filled teeth using new-generation dentine bonding adhesives. Int Endod J 2003; 36: 770-773.
35. Jainaen A, Palamara JE, Messer HH. The effect of resinbased sealers on fracture properties of dentine. Int Endod J 2009; 42: 136-143.
36. Grande NM, Plotino G, Lavorgna L, Ioppolo P, Bedini R, Pameijer CH, Somma F. Influence of different root canalfilling materials on the mechanical properties of root canal dentin. J Endod 2007; 33: 859-863.
37. Kim YK, Grandini S, Ames JM, Gu LS, Kim SK, Pashley DH, Gutmann JL, Tay FR. Critical review on methacrylate resinbased root canal sealers. J Endod 2010; 36: 383-399.