Water-soluble monodispersed lanthanide oxide submicrospheres: PVP-assisted hydrothermal synthesis, size-control and luminescence properties

ChemPhysChem

Volumn 13, Issue 10, 2012, Pages 2610-2614

  Cui, Ying ^a,c   Lai, Xiaoyong ^a   Li, Li ^a   Hu, Zhudong ^a   Wang, Shuo ^a   Halpert, Jonathan E ^a   Yu, Ranbo ^b   Wang, Dan ^a  

^a INSTITUTE OF PROCESS ENGINEERING   (China)

^b UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

^c UNIVERSITY OF CHINESE ACADEMY OF SCIENCES   (China)

Author keywords

hydrothermal synthesis; lanthanides; luminescence; materials science; monodispersed submicrosphere

Indexed keywords

FIELD EMISSION DISPLAYS; LIQUID CRYSTAL DISPLAYS; LUMINESCENCE; MATERIALS SCIENCE; METABOLISM; MORPHOLOGY; RARE EARTH ELEMENTS; SURFACE ACTIVE AGENTS; UREA;

GOOD WATER-SOLUBILITY; LANTHANIDE HYDROXIDE; LUMINESCENCE PROPERTIES; N-VINYL-2-PYRROLIDONE; NARROW SIZE DISTRIBUTIONS; POLY(N-VINYL-2-PYRROLIDONE); SPHERICAL MORPHOLOGIES; SUBMICROSPHERES;

HYDROTHERMAL SYNTHESIS;

EID: 84863709626     PISSN: 14394235     EISSN: 14397641     Source Type: Journal    
DOI: 10.1002/cphc.201100806     Document Type: Article

References (50)

1. Y. N. Xia, B. Gates, Y. D. Yin, Y. Lu, Adv. Mater. 2000, 12, 693-713.
2. Y. D. Yin, Y. Lu, Y. N. Xia, J. Mater. Chem. 2001, 11, 987-989.
3. M. Niu, M. H. Du, Z. Y. Gao, C. H. Yang, X. Y. Lu, R. R. Qiao, M. Y. Gao, Macromol. Rapid Commun. 2010, 31, 1805-1810.
4. P. Pieranski, Contemp. Phys. 1983, 24, 25-73.
5. D. J. Norris, Y. A. Vlasov, Adv. Mater. 2001, 13, 371-376.
6. Y. N. Xia, B. Gates, Z. Y. Li, Adv. Mater. 2001, 13, 409-413.
7. M. S. Fleming, T. K. Mandal, D. R. Walt, Chem. Mater. 2001, 13, 2210-2216.
8. F. Járai-Szabõ, S. Aştilean, Z. Néda, Chem. Phys. Lett. 2005, 408, 241-246.
9. Z. H. Kim, S. R. Leone, J. Phys. Chem. B 2006, 110, 19804-19809.
10. H. Z. Zhong, Z. X. Wei, M. F. Ye, Y. Yan, Y. Zhou, Y. Q. Ding, C. H. Yang, Y. F. Li, Langmuir 2007, 23, 9008-9013.
11. J. G. Li, X. D. Li, X. D. Sun, T. Ikegami, T. Ishigaki, Chem. Mater. 2008, 20, 2274-2281.
12. J. G. Li, X. D. Li, X. D. Sun, T. Ishigaki, J. Phys. Chem. C 2008, 112, 11707-11716.
13. Z. X. Li, L. L. Li, Q. Yuan, W. Feng, J. Xu, L. D. Sun, W. G. Song, C. H. Yan, J. Phys. Chem. C 2008, 112, 18405-18411.
14. H. Guo, Y. M. Qiao, Opt. Mater. 2009, 31, 583-589.
15. G. Jia, M. Yang, Y. H. Song, H. P. You, H. J. Zhang, Cryst. Growth Des. 2009, 9, 301-307.
16. T. T. Yan, D. S. Zhang, L. Y. Shi, H. P. Yang, H. L. Mai, J. H. Fang, Mater. Chem. Phys. 2009, 117, 234-243.
17. B. Liu, B. B. Liu, Q. J. Li, Z. P. Li, R. Liu, X. Zou, W. Wu, W. Cui, Z. D. Liu, D. M. Li, B. Zou, T. A. Cui, G. T. Zou, J. Alloys Compd. 2010, 503, 519-524.
18. X. P. Qin, G. H. Zhou, H. Yang, Y. Yang, J. Zhang, S. W. Wang, J. Alloys Compd. 2010, 493, 672-677.
19. S. R. Whaley, D. S. English, E. L. Hu, P. F. Barbara, A. M. Belcher, Nature 2000, 405, 665-668.
20. W. C. Chien, J. Cryst. Growth 2006, 290, 554-559.
21. H. Wang, M. Yu, C. Lin, X. M. Liu, J. Lin, J. Phys. Chem. C 2007, 111, 11223-11230.
22. Q. Zhu, J. G. Li, X. D. Li, X. D. Sun, Acta Mater. 2009, 57, 5975-5985.
23. J. Feng, G. M. Shan, A. Maquieira, M. E. Koivunen, B. Guo, B. D. Hammock, I. M. Kennedy, Anal. Chem. 2003, 75, 5282-5286.
24. G. K. Das, B. C. Heng, S. C. Ng, T. White, J. S. C. Loo, L. D'Silva, P. Padmanabhan, K. K. Bhakoo, S. T. Selvan, T. T. Y. Tan, Langmuir 2010, 26, 8959-8965.
25. J. H. Wu, G. X. Xie, J. M. Lin, Z. Lan, M. L. Huang, Y. F. Huang, J. Power Sources 2010, 195, 6937-6940.
26. X. J. Zhou, L. Zhao, Q. C. Feng, X. T. Wei, C. K. Duan, Mater. Res. Bull. 2009, 44, 1935-1938.
27. J. Yang, Z. W. Quan, D. Y. Kong, X. M. Liu, J. Lin, Cryst. Growth Des. 2007, 7, 730-735.
28. L. S. Wang, Y. H. Zhou, Z. W. Quan, J. Lin, Mater. Lett. 2005, 59, 1130-1133.
29. Z. Y. Hou, P. P. Yang, C. X. Li, L. L. Wang, H. Z. Lian, Z. W. Quan, J. Lin, Chem. Mater. 2008, 20, 6686-6696.
30. B. Qin, H. Y. Chen, H. Liang, L. Fu, X. F. Liu, X. H. Qiu, S. Q. Liu, R. Song, Z. Y. Tang, J. Am. Chem. Soc. 2010, 132, 2886-2888.
31. S. S. Ho, K. Critchley, G. D. Lilly, B. Shim, N. A. Kotov, J. Mater. Chem. 2009, 19, 1390-1394.
32. F. Candau, Y. S. Leong, R. M. Fitch, J. Polym. Sci. Part A: Polym. Chem. 1985, 23, 193-214.
33. Z. C. Kang, Z. L. Wang, Philos. Mag. B 1996, 73, 905-929.
34. M. H. Zhai, W. M. Zhang, E. H. Shen, Z. Fu, F. Zhang, Acta Phys.-Chim. Sin. 1999, 15, 747-751.
35. K. Ishizu, S. Shiratori, J. Colloid Interface Sci. 2001, 236, 266-269.
36. J. G. Li, C. C. Tang, D. Li, H. Haneda, T. Ishigaki, J. Am. Ceram. Soc. 2004, 87, 1358-1361.
37. S. Sohn, Y. Kwon, Y. Kim, D. Kim, Powder Technol. 2004, 142, 136-153.
38. H. Deng, X. L. Li, Q. Peng, X. Wang, J. P. Chen, Y. D. Li, Angew. Chem. 2005, 117, 2842-2845
39. Angew. Chem. Int. Ed. 2005, 44, 2782-2785.
40. C. W. Sun, J. Sun, G. L. Xiao, H. R. Zhang, X. P. Qiu, H. Li, L. Q. Chen, J. Phys. Chem. B 2006, 110, 13445-13452.
41. B. L. Cushing, V. L. Kolesnichenko, C. J. O'Connor, Chem. Rev. 2004, 104, 3893-3946.
42. D. V. Goia, J. Mater. Chem. 2004, 14, 451-458.
43. D. Sordelet, M. Akinc, J. Colloid Interface Sci. 1988, 122, 47-59.
44. E. Matijevic, W. P. Hsu, J. Colloid Interface Sci. 1987, 118, 506-523.
45. B. Aiken, W. P. Hsu, E. Matijevic, J. Am. Ceram. Soc. 1988, 71, 845-853.
46. V. K. Lamer, R. H. Dinegar, J. Am. Chem. Soc. 1950, 72, 4847-4854.
47. X. G. Peng, J. Wickham, A. P. Alivisatos, J. Am. Chem. Soc. 1998, 120, 5343-5344.
48. Z. A. Peng, X. G. Peng, J. Am. Chem. Soc. 2002, 124, 3343-3353.
49. S. Georgescu, A. Chinie, A. Stefan, O. Toma, Phys. Status Solidi C 2007, 4, 946-949.
50. Y. Jung, H. K. Yang, B. K. Moon, B. C. Choi, J. H. Jeong, J. H. Kim, J. S. Bae, E. D. Jeong, Surf. Rev. Lett. 2010, 17, 73-79.