Damage mechanisms induced by cyclic ply-stresses in carbon-epoxy laminates: Environmental effects

International Journal of Fatigue

Volumn 28, Issue 10 SPEC. ISS., 2006, Pages 1202-1216

  Lafarie Frenot, M C ^a  

^a CNRS   (France)

Author keywords

Durability; Fatigue; Matrix cracking; Oxidation; Thermo mechanical properties

Indexed keywords

CARBON FIBER REINFORCED PLASTICS; DEGRADATION; DURABILITY; OXIDATION; THERMAL CYCLING; THERMAL LOAD;

DEGRADATION MECHANISMS; FATIGUE; MATRIX CRACKING; THERMO-MECHANICAL PROPERTIES;

LAMINATED COMPOSITES;

EID: 33746310561     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2006.02.014     Document Type: Article

References (26)

1. Arendt C, Brunner M, Wang J, Cebeci T. Long term durability testing of polymer composite materials. In: Massard T, Vautrin A, editors, 12th International conference on composite materials (ICCM12), Paris, France, 5-9 July; 1999.
2. Gates TS. Durability assessment of polymeric composites for high speed civil transport. In: Cardon AH, Fukuda H, Reifsnider KL, Verchery G, editors. Proceedings of the DURACOSYS 99, Brussels, Belgium, July 11-14, 'Recent developments in durability analysis of composite systems', Balkema; 1999.
3. Hénaff-Gardin C., Lafarie-Frenot M.C., and Desmeuzes J.L. Modelling of crack evolution under cyclic thermal loading in cross-ply laminates. In: Poursartip A., and Street K. (Eds). 10th International conference on composite materials, (ICCM10), Whistler, Canada, August 14-18 (1995), Woodhead Publishing Limited 447-454
4. Hénaff-Gardin C, Goupillaud I, Lafarie-Frenot MC. Evolution of matrix cracking in cross-ply CFRP laminates: differences between mechanical and thermal loadings. In: Cardon AH, Fukuda H, Reifsnider KL, Verchery G, editors. DURACOSYS 99, Brussels, Belgium, July 11-14, 1999, 'Recent developments in durability analysis of composite systems', Balkema; 1999. p. 69-76.
5. Madhukar M.S., Bowles K., and Papadopoulos D.S. Thermo-oxidative stability and fiber surface modification effects on the in plane shear properties of graphite/PMR 15 composites. J Compos Mater 31 6 (1997) 596-618
6. Colin X, Marais C, Favre JP. Damage/weight loss relationship of polymer matrix composites under thermal ageing. In: Massard T, Vautrin A, editors, 12th International conference on composite materials (ICCM12), Paris, France, 5-9 July; 1999.
7. Colin X, Marais C, Cochon JL. Kinetic modelling of weight changes during the isothermal oxidative ageing of bismaleimide matrix. In: Cardon AH, Fukuda H, Reifsnider KL, Verchery G, editors. DURACOSYS 99, Brussels, Belgium, July 11-14, 'Recent developments in durability analysis of composite systems', Balkema; 1999. p. 49-55.
8. Decelle J., Huet N., and Bellenger V. Oxidation induced shrinkage for thermally aged epoxy networks. Polym Degrad Stabil 81 (2003) 239-248
9. Tsotsis T.K., and Keller S. Aging of polymeric composite specimens for 5000 hours at elevated pressure and temperature. Compos Sci Technol 61 1 (2001) 75-86
10. Bowles KJ, Meyers A. Specimen geometry effects on graphite/PMR 15 composites during thermo-oxidative ageing. In: 31st International SAMPE symposium; 1986. p. 1285-99.
11. Nam J.D., and Seferis J.C. Anisotropic thermo-oxidative stability of carbon fibre reinforced polymeric composites. SAMPE Quart 24 1 (1992) 10-18
12. Salin I.M., and Seferis J.C. Anisotropic effects in thermogravimetry of polymeric composites. J Polym Sci B Polym Phys 31 (1993) 1019-1027
13. Bowles K.J., Madhukar M.S., Papadopoulos D.S., Inghram L., and Me Corkle L. The effects of fiber surface modification and thermal aging on composite toughness and its measurement. J Compos Mater 31 6 (1997) 552-579
14. Parvatareddy H., and Wang J.Z. An evaluation of chemical aging/oxidation in high performance composites using the Vickers mirco-indentation technique. J Compos Mater 30 2 (1996) 210-230
15. Bowles KJ. Predicting the durability of PMR-15 composites aged at elevated temperature. In: Cardon AH, Fukuda H, Reifsnider KL, Verchery G, editors. DURACOSYS 99, Brussels, Belgium, July 11-14, 'Recent developments in durability analysis of composite systems', Balkema; 1999. p. 441-7.
16. Favre J.P., Levadoux H., Ochin T., and Cinquin J. Vieillissement des composites à matrice organique aux températures moyennes: Un premier bilan. In: Baptiste D., and Vautrin A. (Eds). 10èmes Journées Nationales sur les Composites JNC10, Paris, France (1996), AMAC 205-214
17. Cinquin J, Colombaro AM, et al., Etude et prévision du vieillissement de structures composites á matrice organique soumises á des chargements thermomécaniques répétés. in: Candel S (editor), Recherche Aéronautique sur le Supersonique, Paris, France, Ministère de la Recherche, Ministère de l'Equipement, des Transports et du Logement; 2002. p. 125-40.
18. Lafarie-Frenot M.C., and Rouquié S. Influence of oxidative environments on damage in C/epoxy laminates subjected to thermal cycling. Compos Sci Technol 64 10-11 (2004) 1725-1735
19. Lafarie-Frenot M.C., Rouquié S., Ho N.Q., and Bellenger V. Comparison of damage development in C/epoxy laminates during isothermal ageing or thermal cycling. Composites Part A, Applied Science and Manufacturing 37 4 (2006) 662-671
20. Lafarie-Frenot MC, Rouquié S, Bellenger V. Experimental evidence of coupling between matrix cracking and oxidation during thermal ageing of carbon/epoxy laminates. In: Proceedings of ECCM11, May 31-June 3, Rhodes, Greece; 2004.
21. Datoo M.H. Residual stresses. Mechanics of fibrous composites (1991), Elsevier Applied Science 367-420
22. Hancox N.L. Thermal effects on polymer matrix composites: Part 1. Thermal cycling. Mater Desig 19 3 (1998) 85-91
23. Buch X., and Shanahan M.E.R. Thermal and thermo-oxidative ageing of an epoxy adhesive. Polym Degrad Stabil 68 3 (2000) 403-411
24. Colin X. Modélisation cinétique de la thermo-oxydation de matériaux polymères et composites à hautes performances thermomécaniques. Ph.D. thesis, ENSAM - Paris; 2000.
25. Decelle J, Huet N, Bellenger V. Ageing of a carbon epoxy composite. In: Proceedings of ICCE-10, New Orleans; 2003.
26. Bellenger V., Decelle J., and Huet N. Ageing of a carbon epoxy composite for aeronautic application. Compos Part B Eng 36 3 (2005) 189-194