Evaluation of environment-assisted cracking susceptibility of a grade X100 pipeline steel

Corrosion Science

Volumn 54, Issue 1, 2012, Pages 5-9

  Mustapha, A ^a   Charles, E A ^a   Hardie, D ^a  

^a NEWCASTLE UNIVERSITY   (United Kingdom)

Author keywords

A. Low alloy steel; B. Potentiostatic; C. Effects of strain; C. Hydrogen embrittlement; C. Stress corrosion

Indexed keywords

A. LOW ALLOY STEEL; B. POTENTIOSTATIC; C. HYDROGEN EMBRITTLEMENT; C. STRESS CORROSION; EFFECTS OF STRAINS;

EMBRITTLEMENT; HEAT RESISTANCE; HYDROGEN; HYDROGEN EMBRITTLEMENT; RESIDUAL STRESSES; SODIUM; STEEL TESTING; STRAIN RATE; TEXTURES;

STRESS CORROSION CRACKING;

EID: 80655127654     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2011.08.030     Document Type: Article

References (20)

1. Jin T.Y., Cheng Y.F. In situ characterization by localized electrochemical impedance spectroscopy of the electrochemical activity of microscopic inclusions in an X100 steel. Corros. Sci. 2011, 53:850-853.
2. Charles E.A., Parkins R.N. Generation of stress corrosion cracking environments at pipeline surfaces. Corrosion 1995, 51:518-527.
3. Parkins R.N., Fessler R.R. Stress corrosion cracking of high-pressure gas transmission pipelines. Mater. Eng. Appl. 1978, 1:80-96.
4. Wang J.Q., Atrens A. SCC initiation for X65 pipeline steel in the high pH carbonate-bicarbonate solution. Corros. Sci. 2003, 45:2199-2217.
5. R.N. Parkins, A review of stress corrosion cracking of high pressure gas pipelines, Corrosion 2000, NACE, Houston, Paper No. 00363.
6. Hardie D., Charles E.A., Lopez A.H. Hydrogen embrittlement of high strength pipeline steels. Corros. Sci. 2006, 48:4378-4385.
7. A.J. Sedriks, Stress corrosion cracking test methods, NACE (1990) 15-18.
8. ASTM, Standard practice for slow strain rate testing to evaluate the susceptibility of metallic materials to environmentally assisted cracking, G129-00 (2006).
9. R.N. Parkins, Development of strain-rate testing and its implications Special Technical Publication 665, ASTM (1979) 5-25.
10. 2-HCO3--CO32- solutions. I: stress corrosion data. Corros. Sci. 1997, 39:159-173.
11. ASTM, Standard test methods for determining average grain size, E112-96 (2004).
12. Parkins R.N., Markworth A.J., Holbrook J.H., Fessler R.R. Hydrogen gas evolution from cathodically protected surfaces. Corrosion 1985, 41:389-397.
13. Capelle J., Dmytrakh I., Pluvinage G. Comparative assessment of electrochemical hydrogen absorption by pipeline steels with different strength. Corros. Sci. 2010, 52:1554-1599.
14. Sutcliffe J.M., Fessler R.R., Boyd W.K., Parkins R.N. Stress corrosion cracking of carbon steel in carbonate solutions. Corrosion 1972, 28:313-320.
15. Poulson B. The fractography of the stress corrosion cracking in carbon steels. Corros. Sci. 1975, 15:469-477.
16. Li G., Zhang G., Zhou J., Huang C., Yang W. Characteristics and mechanism of high pH stress corrosion cracking of pipeline steel X70. Key Eng. Mater. 2007, 353-358:219-222.
17. Rebak R.B., Xia Z., Safruddin R., Szklarska-Smialowska Z. Effect of solution composition and electrochemical potential on stress corrosion cracking of X-52 pipeline steel. Corrosion 1996, 52:396-405.
18. Wang Z.F., Atrens A. Initiation of stress corrosion cracking for pipeline steels in a carbonate-bicarbonate solution. Met. Mat. Trans. 1996, 27A:2686-2691.
19. Xue H.B., Cheng Y.F. Characterization of inclusions of X80 pipeline steel and its correlation with hydrogen-induced cracking. Corros. Sci. 2011, 53:1201-1208.
20. Mitsui H., Takahashi R., Asano H., Taniguchi N., Yui M. Susceptibility to stress corrosion cracking for low-carbon steel welds in carbonate-bicarbonate Solution. Corrosion 2008, 64:939-948.