Stress intensity factor expression for center-cracked butt joint considering the effect of joint shape

Materials and Design

Volumn 35, Issue , 2012, Pages 72-79

  Wang, T ^a   Yang, J G ^a   Liu, X S ^a   Dong, Z B ^a   Fang, H Y ^a  

^a HARBIN INSTITUTE OF TECHNOLOGY   (China)

Author keywords

E. Fatigue; F. Defects; H. Failure analysis

Indexed keywords

BASE METALS; BUTT JOINTS; E. FATIGUE; F. DEFECTS; H. FAILURE ANALYSIS; SHAPE PARAMETERS; SMOOTH TRANSITIONS; STATIC LOADS; TENSILE LOADS; WELD REINFORCEMENT; WELD TOE;

DEFECTS; FAILURE ANALYSIS; FINITE ELEMENT METHOD; STRESS INTENSITY FACTORS;

BUTT WELDING;

EID: 80155183732     PISSN: 02641275     EISSN: 18734197     Source Type: Journal    
DOI: 10.1016/j.matdes.2011.09.020     Document Type: Article

References (34)

1. Mirapeix J., Garcia-Allende P.B., Cobo A., Conde O.M., Lopez-Higuera J.M. Real-time arc-welding defect detection and classification with principal component analysis and artificial neural networks. NDT&E Int 2007, 40:315-323.
2. Fujii H., Umakoshi H., Aoki Y., Nogi K. Bubble formation in aluminium alloy during electron beam welding. J Mater Process Technol 2004, 155(156):1252-1255.
3. Durocher A., Ayrault D., Chagnot Ch, Lipa M., Saikaly W. CuCrZr alloy hot cracking during electron beam welding. J Nucl Mater 2007, 367(370):1208-1212.
4. Kim Y.G., Fujii H., Tsumura Y., Komazaki T., Nakata K. Three defect types in friction stir welding of aluminum die casting alloy. Mat Sci Eng A-Struct 2006, 415:250-254.
5. Lee H.W., Choe W.H., Park J.U., Kang C.Y., Park W.J. Weld metal hydrogen assisted cracking in 50mm TMCP steel plate with SAW process. Sci Technol Weld Joi 2006, 11:243-249.
6. Hao S., Schwalbe K.-H., Cornec A. The effect of yield strength mis-match on the fracture analysis of welded joints: slip-line field solutions for pure bending. Int J Solids Struct 2000, 37:5385-5411.
7. Li B., Shen Y.F., Hu W.Y. The study on defects in aluminum 2219-T6 thick butt friction stir welds with the application of multiple non-destructive testing methods. Mater Des 2011, 32:2073-2084.
8. Dubourg L., Merati A., Jahazi M. Process optimisation and mechanical properties of friction stir lap welds of 7075-T6 stringers on 2024-T3 skin. Mater Des 2010, 31:3324-3330.
9. Hu L.H., Huang J., Li Z.G., Wu Y.X. Effects of preheating temperature on cold cracks, microstructures and properties of high power laser hybrid welded 10Ni3CrMoV steel. Mater Des 2011, 32:1931-1939.
10. Ayatollahi M.R., Torabi A.R. Brittle fracture in rounded-tip V-shaped notches. Mater Des 2010, 31:60-67.
11. Edwards K.L. Selecting materials for optimum use in engineering components. Mater Des 2005, 26:469-473.
12. Edwards K.L., Deng Y.M. Supporting design decision-making when applying materials in combination. Mater Des 2007, 28:1288-1297.
13. Wang J.G., Ju D.Y., Sun M.J., Li S.L. A new analytical method for stress intensity factors based on in situ measurement of crack deformation under biaxial tension. Mater Des 2011, 32:664-670.
14. Bouiadjra B.B., Achour T., Berrahou M., Ouinas D., Feaugas X. Numerical estimation of the mass gain between double symmetric and single bonded composite repairs in aircraft structures. Mater Des 2010, 31:3073-3077.
15. Ouinas D., Hebbar A., Bouiadjra B.B., Benderdouche N., Serier B. Interaction effect crack-interfacial crack using finite element method. Mater Des 2010, 31:375-381.
16. Shahani A.R., Amini Fasakhodi M.R. Finite element analysis of dynamic crack propagation using remeshing technique. Mater Des 2009, 30:1032-1041.
17. Konsta-Gdoutos M. Limitations in mixed-mode stress intensity factor evaluation by method of caustics. Eng Fract Mech 1996, 55:371-382.
18. Newman J.C. Stress-intensity factors and crack-opening displacements for round compact specimens. Int J Fract 1981, 17:567-578.
19. Sarangi H., Murthy K.S.R.K., Chakraborty D. Radial locations of strain gages for accurate measurement of mode I stress intensity factor. Mater Des 2010, 31:2840-2850.
20. Liu H.J., Fujii H., Maeda M., Nogi K. Tensile properties and fracture locations of friction-stir-welded joints of 2017-T351 aluminum alloy. J Mater Process Techol 2003, 142:692-696.
21. Sharifitabar M., Halvaee A., Khorshahian S. Microstructure and mechanical properties of resistance upset butt welded 304 austenitic stainless steel joints. Mater Des 2011, 32:3854-3864.
22. Xu W.F., Liu J.H., Zhu H.Q. Analysis of residual stresses in thick aluminum friction stir welded butt joints. Mater Des 2011, 32:2000-2005.
23. Hobbacher A. Stress intensity factors of welded-joints. Eng Fract Mech 1993, 46:173-182.
24. Moreira P.M.G.P., de Matos P.F.P., Camanho P.P., Pastrama S.D., de Castro P.M.S.T. Stress intensity factor and load transfer analysis of a cracked riveted lap joint. Mater Des 2007, 28:1263-1270.
25. Marc A.M., Krishan K.C. Mechanical behavior of materials 2009, Cambridge University Press, New York.
26. Wu X.F., Dzenis Y.A., Gokdag E. Edge-cracked orthotropic bimaterial butt joint under antiplane singularity. Int J Nonlin Sci Num 2004, 5:347-354.
27. Reedy E.D., Guess T.R. Butt-joint tensile-strength-interface corner stress intensity factor prediction. J Adhes Sci Technol 1995, 9:237-251.
28. Kirkhope K.J., Bell R., Caron L., Basu R.I., Ma K.-T. Weld detail fatigue life improvement techniques. Mar Struct 1999, 12:447-496.
29. Nguyen T.N., Wahab M.A. The effect of residual stresses and weld geometry on the improvement of fatigue life. J Mater Process Technol 1995, 48:581-588.
30. Tada H., Paris P.C., Irwin G.R. The stress analysis of cracks handbook 2000, ASME, New York.
31. Murakami Y. Stress intensity factors handbook 1987, Pergamon Press, England.
32. Boscolo M., Zhang X. A modeling technique for calculating stress intensity factors for structures reinforced by bonded straps. Part I: mechanisms and formulation. Eng Fract Mech 2010, 77:883-895.
33. Li W., Sakai T., Li Q., Wang P. Statistical analysis of fatigue crack growth behavior for grade B cast steel. Mater Des 2011, 32:1262-1272.
34. Kim D.H., Kim H.K. Fatigue strength evaluation of cross-tension spot weld joints of cold rolled mild steel sheet. Mater Des 2009, 30:3286-3290.