Failure mode transition in AHSS resistance spot welds. Part II: Experimental investigation and model validation

Materials Science and Engineering: A

Volumn 528, Issue 29-30, 2011, Pages 8344-8352

  Pouranvari, M ^a   Marashi, S P H ^b   Safanama, D S ^b  

^a ISLAMIC AZAD UNIVERSITY   (Iran)

^b AMIRKABIR UNIVERSITY OF TECHNOLOGY   (Iran)

Author keywords

AHSS; Failure mode; HAZ softening; Microstructure; Resistance spot welding

Indexed keywords

BEARINGS (MACHINE PARTS); FAILURE MODES; HARDNESS; METALLOGRAPHY; SPOT WELDING; TENSILE STRENGTH; TENSILE TESTING; WELDS;

AHSS; EXPERIMENTAL INVESTIGATIONS; EXPERIMENTAL MODELLING; FAILURE MODE TRANSITION; FUSION ZONE SIZE; HAZ SOFTENING; MODEL VALIDATION; PULL-OUT FAILURE; RESISTANCE SPOT WELD; RESISTANCE SPOT WELDING;

MICROSTRUCTURE;

EID: 80053620892     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2011.08.016     Document Type: Article

References (30)

1. Pouranvari M., Asgari H.R., Mosavizadeh S.M., Marashi P.H., Goodarzi M. Sci. Technol. Weld. Joining 2007, 12:217-225.
2. Zuniga S., Sheppard S.D. Fatigue and Fracture Mechanics, ASTM STP 1296 1997, 27:469-489. ASTM, Philadelphia, USA.
3. Marya M., Wang K., Hector L.G., Gayden X. J. Manufact. Sci. Eng. 2006, 128:287-298.
4. S.M. Zuniga, Predicting overload pull-out failures in resistance spot welded, Ph.D. thesis, Stanford University, 1994.
5. Lee H., Kim N., Lee T.S. Eng. Fract. Mech. 2005, 72:1203-1221.
6. Han Z., Indacochea J.E. J. Mater. Eng. Perform. 1993, 2:437-444.
7. Goodarzi M., Marashi S.P.H., Pouranvari M. J. Mater. Process. Technol. 2009, 209:4379-4384.
8. Marashi P., Pouranvari M., Amirabdollahian S., Abedi A., Goodarzi M. Mater. Sci. Eng. A 2008, 480:175-180.
9. Pouranvari M., Abedi A., Marashi P., Goodarzi M. Sci. Technol. Weld. Joining 2008, 13:39-43.
10. Radakovic D.J., Tumuluru M.D. Weld. J. 2008, 87:96s-105s.
11. Tumuluru M.D. Weld. J. 2007, 86:31-37.
12. Sun X., Stephens E.V., Khaleel M.A. Eng. Fail. Anal. 2008, 15:356-367.
13. R.M. Rivett, " Assessment of resistance spot weld in low carbon and high strength steel sheet-part 1 static properties" , Research report, The Welding Institute, 1982.
14. M. Pouranvari, S.P.H. Marashi, Mater. Sci. Eng. A, accepted for publication. doi:10.1016/j.msea.2011.08.017.
15. American Welding Society, ANSI/AWS/SAE/D8.9-97, Recommended Practices for Test Methods and Evaluation the Resistance Spot Welding Behavior of Automotive Sheet Steels, 1997.
16. M.V. Li, D. Dong, M. Kimchi: SAE Technical Paper 982278, SAE International, Warrendale, PA, USA, 1998.
17. Gould J.E., Khurana S.P., Li T. Weld. J. 2006, 85:111s-116s.
18. Easterling K.E. Modelling the weld thermal cycle and transformation behavior in the heat-affected zone. Mathematical Modelling of Weld Phenomena 1993, The Institute of Materials. H. Cerjak, K.E. Easterling (Eds.).
19. Bhadeshia H.K.D.H., Honeycombe R. Steels: Microstructure and Properties 2006, Butterworth-Heinemann, Oxford. third ed.
20. British Standard Institute. December 1974 Specification for metal-arc welding of carbon and carbon manganese steels. BS5135.
21. Baltazar Hernandez V.H., Panda S.K., Kuntz M.L., Zhou Y. Mater. Lett. 2010, 64:207-210.
22. Xia M., Biro E., Tian Z., Zhou Y. ISIJ Int. 2008, 48:809-814.
23. Khan M.I., Kuntz M.L., Zhou Y. Sci. Technol. Weld. Joining 2008, 13:294-304.
24. Sun X., Stephens E.V., Khaleel M.A. Weld. J. 2007, 86:18s-25s.
25. Burgmann P., Clymer K., Cobb S., Miller M., O'Loughlin A., Findley K.O., Liu S. Iron Steel Technol. 2010, 7:76-85.
26. Rathbun R.W., Matlock D.K., Speer J.G. Weld. J. 2003, 83:207s-218s.
27. Marya M., Gayden X.Q. Weld. J. 2005, 84:172s-182s.
28. W. Chuko, J.E. Gould: 'Development of appropriate resistance spot welding practice for transformation-hardened steels - phase 2: evaluation of post-weld cooling rate techniques', Report to the American Iron and Steel Institute, 2002.
29. Hertzberg R.W. Deformation and Fracture Mechanics of Engineering Materials 1996, John Wiley & Sons. second ed.
30. Fourlaris G., Hambling S.J., Jones T.B. Mater. Sci. Technol. 2006, 22:39-44.