Hydrogen embrittlement type stress corrosion cracking behavior of wrought magnesium alloy AZ31

Procedia Engineering

Volumn 10, Issue , 2011, Pages 578-582

  Uematsu, Yoshihiko ^a   Kakiuchi, Toshifumi ^a   Nakajima, Masaki ^b  

^a GIFU UNIVERSITY   (Japan)

^b TOYOTA NATIONAL COLLEGE OF TECHNOLOGY   (Japan)

Author keywords

Crack propagation rate; Hydrogen embrittlement; Magnesium alloy; Stress corrosion cracking

Indexed keywords

CORROSION; CRACK PROPAGATION; CRACKS; HYDROGEN; HYDROGEN EMBRITTLEMENT; MAGNESIUM; MAGNESIUM ALLOYS; RESIDUAL STRESSES; STEEL PIPE;

CATHODIC POTENTIALS; COMPACT TENSION SPECIMEN; CRACK PROPAGATION RATE; NACL SOLUTION; POURBAIX DIAGRAM; SCC TEST; WROUGHT MAGNESIUM ALLOYS;

STRESS CORROSION CRACKING;

EID: 80052934164     PISSN: 18777058     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1016/j.proeng.2011.04.096     Document Type: Conference Paper

References (7)

1. Alvarez RB, Martin HJ, Horstemeyer MF, Chandler MQ, Williams N, Wang PT, Ruiz A. Corrosion relationships as a function of time and surface roughness on a structural AE44 magnesium alloy. Corrosion Sci 2010;52:1635-48.
2. Nan ZY, Ishihara S, Goshima T. Corrosion fatigue behavior of extruded magnesium alloy AZ31in sodium chloride solution. Int J Fatigue 2008;30:1181-8.
3. Khana SA, Miyashitab Y, Mutoh Y, Koike T. Fatigue behavior of anodized AM60 magnesium alloy under humid environment. Mat Sci Eng A 2008;498: 377-83.
4. Stampella RS, Procter RPM, Ashworth V. Environmentally-induced cracking of magnesium. Corrosion Sci 1984;24:325-41.
5. Ben-Hamu G, Eliezer D, Dietzel W, Shin KS. Stress corrosion cracking of new Mg-Zn-Mn wrought alloys containing Si. Corrosion Sci 2008;50:1505-17.
6. Winzer N, Atrens A, Dietzel W, Raja VS, Songe G, Kainer KU. Characterisation of stress corrosion cracking (SCC) of Mg-Al alloys. Mat Sci Eng A 2008;448:339-51.
7. Srinivasan PB, Riekehr S, Blawert C, Dietzel W, Kocak M. Slow strain rate stress corrosion cracking behaviour of as-welded and plasma electrolytic oxidation treated AZ31HP magnesium alloy autogenous laser beam weldment. Mat Sci Eng A 2009;517:197-203.