Modelling of the evolution of stress corrosion cracks from corrosion pits

Scripta Materialia

Volumn 54, Issue 4 SPEC. ISS., 2006, Pages 575-578

  Turnbull, A ^a   McCartney, L N ^a   Zhou, S ^a  

^a NATIONAL PHYSICAL LABORATORY   (United Kingdom)

Author keywords

Modelling; Pitting; Stress corrosion cracking

Indexed keywords

COMPUTER SIMULATION; CRACKS; MATHEMATICAL MODELS; PITTING;

CRACK DOMAINS; CRACK-DEPTHS; MODELING; PITS;

STRESS CORROSION CRACKING;

EID: 28544438825     PISSN: 13596462     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.scriptamat.2005.10.053     Document Type: Article

References (9)

1. Y. Kondo Corrosion 45 1989 7
2. Wei RP. Material aging and reliability of engineered systems, in: Proceedings of conference on Environmentally Assisted Cracking: Predictive methods for risk assessment and evaluation of material, equipment and structures, editor R.D. Kane, ASTM STP1401, 2000, pp. 3-19.
3. G. Engelhardt, D.D. Macdonald, Y. Zhang, and B. Dooley Power Plant Chem 6 2004 647
4. G. Engelhardt, and D.D. Macdonald Corros Sci 46 2004 2755
5. Turnbull A., McCartney LN, Zhou S. A deterministic model of pitting corrosion and the pit-to-crack transition, Corros Sci, in press, 2005.
6. Zhou S, Turnbull A. Environment assisted cracking of steam turbine disc and blade steels-Description of test procedure and preliminary results, NPL Report MAT(C) A41, 2001.
7. Zhou S, Turnbull A. Effect of Stress Transients on the Crack Propagation Rate in Steam Turbine Disc Steel, Corrosion, accepted for publication.
8. Turnbull A., Zhou S, Orkney L, McCormick N. Visualisation of Stress Corrosion Cracks Emerging from Pits, Corrosion, submitted for publication.
9. A. Turnbull, and A. Zhou Corros Eng Sci Technol 38 2003 177