Effect of decalcification on C-S-H gel microstructure in cement paste

Jianzhu Cailiao Xuebao/Journal of Building Materials

Volumn 14, Issue 3, 2011, Pages 293-298

  He, Zhen ^a   Wang, Lei ^a   Shao, Yi Xin ^b   Cai, Xin Hua ^a  

^a WUHAN UNIVERSITY   (China)

^b MCGILL UNIVERSITY   (Canada)

Author keywords

C S H; Decalcification; Molar ratio of CaO to SiO2; NMR; Polymerization

Indexed keywords

AL-DOPING; C-S-H; C-S-H GEL; CEMENT PASTE; DECALCIFICATION; DECONVOLUTION TECHNIQUES; FTIR; MAS NMR; MOLAR RATIO; MOLECULAR LEVELS; TEST RESULTS; TWO STAGE; X-RAY FLUORESCENCE SPECTROMETER;

FOURIER TRANSFORMS; GELS; INFRARED SPECTROSCOPY; MICROSTRUCTURE; POLYMERIZATION; POLYMERS; SILICON OXIDES; SPECTROMETERS; X RAY DIFFRACTION;

CALCIUM SILICATE;

EID: 79961114002     PISSN: 10079629     EISSN: None     Source Type: Journal    
DOI: 10.3969/j.issn.1007-9629.2011.03.002     Document Type: Article

References (16)

1. JEFFREY J C, JEFFREY J T, TAYLOR H F W, et al. Solubility and structure of calcium silicate hydrate [J]. Cem Concr Res, 2004, 34 (9): 1499-1519.
2. CARDE C, ESCADEILLAS G, FRANCOIS R. Use of ammonium nitrate solution to simulate and accelerate the leaching of cement pastes due to deionized water [J]. Mag Concr Res, 1997, 49 (181): 295-301.
3. HAGA K, SHIBATA M, HIRONAGA M, et al. Change in pore structure and composition of hardened cement paste during the process of dissolution [J]. Cem Concr Res, 2005, 35 (5): 943-950.
4. AGOSTINI F, LAFHAJ Z, SKOCZYLAS F, et al. Experimental study of accelerated leaching on hollow cylinders of mortar [J]. Cem Concr Res, 2007, 37 (1): 71-78.
5. SAITO H, DEGUCHI A. Leaching test on different mortars using accelerated electrochemical method [J]. Cem Concr Res, 2000, 30 (11): 1815-1825.
6. GRUTZECK M W. A new model for the formation of calcium silicate hydrate (C-S-H) [J]. Mat Res Innovat, 1999, 3 (3): 160-170.
7. CONG X, KIRKPATRICK R J. 29Si MAS NMR study of the structure of calcium silicate hydrate [J]. Advn Cem Bas Mat, 1996, 3 (3-4): 144-156.
8. SUN G K, YOUNG J F, KIRKPATRICK R J. The role of Al in C-S-H: NMR, XRD, and compositional results for precipitated samples [J]. Cem Concr Res, 2006, 36 (1): 18-29.
9. YANG Nan-ru. Progress in the investigation of structural model of C-S-H gel [J]. Journal of Nanjing University of Chemical Technology, 1998, 20 (2): 78-85. (in Chinese)
10. RICHARDSON I G. The nature of C-S-H in hardened cements [J]. Cem Concr Res, 1999, 29 (8): 1131-1147.
11. WANG Kuen-sheng, LIN Kae-long, HUANG Zuh-quia. Hydraulic activity of municipal solid waste incinerator fly-ash-slag-blended eco-cement [J]. Cem Concr Res, 2001, 31 (1): 97-103.
12. JAKOBSEN A, ANDERSON S, JAKOBSEN H J. Characterization of white Portland cement hydration and the C-S-H structure in the presence of sodium aluminate by 27Al and 29Si MAS NMR spectroscopy [J]. Cem Concr Res, 2004, 34 (5): 857-868.
13. RICHARDSON I G. Tobermorite/jennite-and tobermorite/calcium hydroxide-based models for the structure of C-S-H: Applicability to hardened pastes of tricalcium silicate, β-dicalcium silicate, Portland cement, and blends of Portland cement with blast-furnace slag, metakaolin, or silica fume [J]. Cem Concr Res, 2004, 34 (9): 1733-1777.
14. RICHARDSON I G. The calcium silicate hydrates [J]. Cem Concr Res, 2008, 38 (2): 137-158.
15. MOHAN K, TAYLOR H F W. A trimethylsilylation study of tricalcium silicate pastes [J]. Cem Concr Res, 1982, 12 (1): 25-31.
16. JEFFREY J C, THOMAS J J, JENNINGS H M. Decalcification shrinkage of cement paste [J]. Cem Concr Res, 2006, 36 (5): 801-809.