Effect of oxygen plasma pretreatment and titanium dioxide overlay coating on flame retardant finished cotton fabrics

BioResources

Volumn 6, Issue 2, 2011, Pages 1454-1474

  Lam, Yin Ling ^a   Kan, Chi Wai ^a   Yuen, Chun Wah ^a  

^a HONG KONG POLYTECHNIC UNIVERSITY   (Hong Kong)

Author keywords

Cotton; Flame retardant; Plasma pretreatment; Titanium dioxide

Indexed keywords

ATMOSPHERIC PRESSURE PLASMA JETS; BREAKING LOAD; COCATALYST; CONTROL SAMPLES; CROSS LINKING AGENTS; CROSS-LINKING PROCESS; EFFECT OF OXYGEN; ETCHING EFFECT; FINISHING AGENTS; FLAME-RETARDANCY; FLAMMABILITY PROPERTIES; FREE FORMALDEHYDES; MATERIAL PROPERTY; MELAMINE RESIN; METAL OXIDES; NANO-TIO; PLASMA PRE-TREATMENT; SIDE EFFECT; TEARING STRENGTH; TIO; WRINKLED FABRIC;

ATMOSPHERIC PRESSURE; CATALYSTS; COTTON; COTTON FABRICS; FLAMMABILITY; FLAMMABILITY TESTING; MELAMINE FORMALDEHYDE RESINS; METAL FINISHING; METALLIC COMPOUNDS; OXIDES; OXYGEN; PHOSPHORIC ACID; PHOSPHORUS; PHOSPHORUS COMPOUNDS; PLASMAS; RESINS; TENSILE STRENGTH; TITANIUM; TITANIUM DIOXIDE;

PLASMA DEPOSITION;

GOSSYPIUM HIRSUTUM;

EID: 79953741224     PISSN: None     EISSN: 19302126     Source Type: Journal    
DOI: None     Document Type: Article

References (24)

1. Bourbigot, S., and Duquesne, S. (2007). "Fire retardant polymers: Recent developments and opportunities," Journal of Material Science 17, 2283-2300.
2. Chen, L., and Wang, Y. Z. (2010). "Aryl polyphosphonates: useful halogen-free flame retardants for polymers," Materials 3, 4746-4760.
3. Hwang, Y. J., and McCord, M. G. (2005). "Effects of helium atmospheric pressure plasma treatment on low-stress mechanical properties of polypropylene nonwoven fabrics," Textile Research Journal 75(11), 771-778.
4. Kan, C. W., and Yuen, C. W. M. (2006). "Evaluation of some of the properties of plasma treated wool fabric," Journal of Applied Polymer Science 102(6), 5958-5964.
5. Kang, I., Yang, C. Q., Wei, W., and Lickfield, G. C. (1998). "The mechanical strength of cotton fabrics crosslinked by polycarboxylic acids, Part I: Acid degradation and crosslinking of cellulose," Textile Research Journal 68, 865-870.
6. Kaplan, S. (2004). "Plasma processes for wide fabric, film and non-wovens," Surface and Coatings Technology 186, 214-217.
7. Lam, Y. L., Kan, C. W., and Yuen, C. W. M. (2010a). "Effect of titanium dioxide on flame-retardant finishing of cotton fabric," Journal of Applied Polymer Science (Accepted).
8. 2 as co-catalyst," Journal of Applied Polymer Science (Accepted).
9. Laoutid, F., Bonnaud, L., Alexandre, M., Lopez-Cuesta, J. M., and Dubois, Ph. (2009). "New prospects in flame retardant polymer materials: From fundamentals to nanocomposites," Material Science and Engineering R: Reports 63(3), 100-125.
10. Mostashari, S. M., and Mostashari, S. Z. (2004). "Burning of cotton fabric impregnated by ammonium chloride as a flame-retardant," Journal of Applied Fire Science 13(4), 329-337.
11. Mostashari, S. M., and Mostashari, S. Z. (2005). "Synergistic effect of boric acid-urea on the flame retardancy imparted to cotton fabric," Asian Journal of Chemistry 17(4), 2331-2334.
12. 2 and siloxane copolymers as environmentally safe flame-retardant materials," Journal of Macromolecular Science: Pure and Applied Chemistry 45(11), 943-947.
13. Rajpreet, K. V., and Gita, N. R. (2004). "Plasma and antimicrobial treatment of nonwoven fabrics for surgical gowns," Textile Research Journal 74(12), 1073-1079.
14. Siriviriyanun, A., O'Rear, E. A., and Yanumet, N. (2008). "Self-extinguishing cotton fabric with minimal phosphorus deposition," Cellulose 15(5), 731-737.
15. Wakelyn, P. J., Adair, P. K., and Barker, R. H. (2004). "Do open flame ignition resistance treatments for cellulosic and cellulosic blend fabrics also reduce cigarette ignitions?" Fire and Materials 29(1), 15-26.
16. Wang, C. X., and Qiu, Y. P. (2007). "Two sided modification of wool fabrics by atmospheric pressure plasma jet - Influence of processing parameters on plasma penetration," Surface and Coatings Technology 201, 6273-6277.
17. Wang, C. X., Liu, Y., Xu, H. L., Ren, Y., and Qiu, Y. P. (2008). "Influence of atmospheric pressure plasma treatment time on penetration depth of surface modification into fabric," Applied Surface Science 254(8), 2499-2505.
18. Wang, X. Y., Lin, J., Fan, L. H., and Di, Q. Y. (2004). "Effects of plasma treatment on crease-resist finish of cotton fabric," Dyeing and Finishing 5, 10-12.
19. Wong, K. K., Tao, X. M., Yuen, C. W. M., and Yeung, K. W. (1999). "Low temperature plasma treatment of linen," Textile Research Journal 69(11), 846-855.
20. Wu, W. D., and Yang, C. Q. (2006). "Comparison of different reactive organophosphorus flame retardant agents for cotton: Part I. The bonding of the flame retardant agents to cotton," Polymer Degradation and Stability 91(11), 2541-2548.
21. Yang, C. Q., Wei, W., and Lickfield, G. C. (2000). "Mechanical strength of durable press finsihed cotton fabric, Part III: Change in cellulose molecular weight," Textile Research Journal 70, 910-915.
22. Yang, C. Q., Wu, W. D., and Xu, Y. (2004). "The combination of a hydroxy-functional organophosphorus oligomer and melamine-formaldehyde as a flame retarding finishing system for cotton," Fire and Materials 29(2), 109-120.
23. Yang, H., and Yang, C. Q. (2005). "Durable flame retardant finishing of the nylon/cotton blend fabric using a hydroxyl-functional organophosphorus oligomer," Polymer Degradation and Stability 88(3), 363-370.
24. Yang, H., and Yang, C. Q. (2007). "Nonformaldehyde flame retardant finishing of the Nomex/cotton blend fabric using a hydroxy-functional organophosphorus oligomer," Journal of Fire Sciences 25(5), 425-446.