Corrosion behavior of 3C magnesium alloys in simulated sweat solution

Materials and Corrosion

Volumn 62, Issue 3, 2011, Pages 234-239

  Wu, F ^a   Zhang, S ^a   Tao, Z ^a  

^a CHONGQING UNIVERSITY   (China)

Author keywords

corrosion behavior; magnesium alloys; simulated sweat solution

Indexed keywords

AZ31; CORROSION BEHAVIOR; CORROSION PROCESS; CORROSION PRODUCTS; ELECTROCHEMICAL TECHNOLOGY; ELECTROCHEMICAL TEST; MG ALLOY; PH MEASUREMENTS; PITTING CORROSION; SEM; SIMULATED SWEAT SOLUTION;

ALLOYS; CORROSION INHIBITORS; CORROSION PREVENTION; CORROSION RESISTANCE; CORROSIVE EFFECTS; ELECTROCHEMISTRY; LACTIC ACID; MAGNESIUM; MAGNESIUM ALLOYS; PH; PITTING; POTENTIOMETRIC SENSORS; SCANNING ELECTRON MICROSCOPY; SODIUM CHLORIDE; SURFACE ANALYSIS; SURFACE MORPHOLOGY; UREA; X RAY DIFFRACTION;

SOLUTION MINING;

EID: 79951938061     PISSN: 09475117     EISSN: 15214176     Source Type: Journal    
DOI: 10.1002/maco.200905510     Document Type: Article

References (32)

1. Y. J. Zhang, C. W. Yan, F. H. Wang, Corros. Sci. 2005, 47, 2861.
2. F. Zucchi, V. Grassi, F. Zanotto, Mater. Corros. 2009, 60, 199.
3. M. B. Kannan, W. Dietzel, C. Blawert, S. Riekehr, M. Kocak, Mater. Sci. Eng. A 2007, 444, 220.
4. C. Jihua, C. Zhenhua, Y. Hongge, Z. Fuquan, C. Yingliang, Mater. Corros. 2008, 59, 934.
5. J. Wloka, T. Hack, S. Virtanen, Mater. Corros. 2008, 59, 5.
6. J. Chen, J. Wang, E. Han, J. Dong, W. Ke, Mater. Corros. 2005, 57, 10.
7. A. Pardo, M. C. Merino, A. E. Coy, R. Arrabal, F. Viejo, E. Matykina, Corros. Sci. 2008, 50, 832.
8. J. G. Kim, Y. S. Choi, J. H. Yeo, S. K. Kim, Y. J. Kim, J. H. Joo, Corrosion 2003, 59, 228.
9. S. Bender, J. Goellner, A. Heyn, E. Boese, Mater. Corros. 2007, 58, 12.
10. R. F. Zheng, C. H. Liang, Mater. Corros. 2007, 58, 3.
11. C. Berziou, K. Remy, A. Billard, J. Creus, Corros. Sci. 2007, 49, 4276.
12. M. F. Montemor, M. G. S. Ferreira, Electrochem. Acta 2007, 52, 7486.
13. J. E. Gray, B. Luan, J. Alloy Compd. 2002, 336, 88.
14. G. Song, D. Stjohn, Corros. Sci. 2004, 46, 1381.
15. Y. W. Song, D. Y. Shan, E. H. Han, Electrochim. Acta 2007, 53, 2009.
16. X. W. Guo, J. W. Chang, S. M. He, W. J. Ding, X. S. Wang, Electrochim. Acta 2007, 52, 2570.
17. D. M. Draxiica, J. P. Popic, J. Appl. Electrochem. 1999, 29, 43.
18. L. J. li, H. S. Yu, J. L. Lei, C. P. Liu, S. T. Zhang, F. S. Pang, Electrochemistry 2008, 14, 95.
19. M. Baumgartner, H. Kaesche, Corros. Sci. 1990, 31, 231.
20. C. H. Zhang, X. H. Huang, M. L. Zhang, L. L. Gao, R. Z. Wu, Mater. Lett. 2008, 62, 2177.
21. A. Shi, B. A. Shaw, E. Sikora, Corrosion 2005, 61, 534.
22. A. M. A. Gaber, B. A. A. Nabey, M. Saadawy, Corros. Sci. 2009, 51, 1038.
23. G. Quartarone, A. Zingales, T. Bellomi, M. Gajo, G. Paolucci, Corrosion 2005, 61, 1041.
24. G. Song, A. Atrens, X. Wu, B. Zhang, Corros. Sci. 1998, 40, 1769.
25. G. Baril, C. Blanc, N. Pebere, J. Electrochem. Soc. 2001, 148, 489.
26. G. Song, A. Atrens, D. S. John, X. Wu, J. Nairn, Corros. Sci. 1997, 39, 1981.
27. F. Zucchi, G. Trabanelli, V. Grassi, A. Frignani, Corrosion 2004, 60, 362.
28. A. Srinivasan, S. Ningshen, U. K. Mudali, U. T. S. Pillai, B. C. Pai, Intermetallics 2007, 12, 1511.
29. A. Bakkar, V. Neubert, Corros. Sci. 2007, 49, 1110.
30. Y. W. Song, D. Y. Shan, R. S. Chen, E. H. Han, Corros. Sci. 2009, 51, 1087.
31. J. G. Kim, Y. S. Choi, J. H. Yeo, S. K. Kim, Y. J. Kim, J. H. Joo, Corrosion 2003, 59, 228.
32. Q. Wang, Y. H. Liu, L. N. Zhang, Y. L. Song, D. W. Zhang, C. F. Li, Mater. Corros. 2010, 61, 222.