Corrosion process of steel bar in concrete in full lifetime

ACI Materials Journal

Volumn 107, Issue 6, 2010, Pages 562-567

  Yuan, Yingshu ^a   Jiang, Jianhua ^b   Peng, Tao ^b  

^a CHINA UNIVERSITY OF MINING AND TECHNOLOGY   (China)

^b CHINA UNIVERSITY OF MINING AND TECHNOLOGY   (China)

Author keywords

Chloride attack; Corrosion rate; Interfacial transition zone; Time variation

Indexed keywords

CHLORIDE ATTACK; CORROSION CRACKING; CORROSION CURRENT DENSITIES; CORROSION LAYERS; CORROSION LEVELS; CORROSION LOSS; CORROSION PROCESS; INTERFACIAL TRANSITION ZONE; MECHANISM ANALYSIS; STEEL BARS; TIME VARIANT; TIME VARIATIONS; TIME-DEPENDENT MODELS; WATER-CEMENT RATIO;

BARS (METAL); CHLORINE COMPOUNDS; CORROSION PREVENTION; CURRENT DENSITY; STRESS CORROSION CRACKING;

CORROSION RATE;

EID: 78650029106     PISSN: 0889325X     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (9)

1. Liu, T., and Weyers, R. W., "Modeling the Dynamic Corrosion Process in Chloride Contaminated Concrete Structures," Cement and Concrete Research, V. 28, No. 3,1998, pp. 356-379. (Pubitemid 128634256)
2. Schiessl, P., and Raupach, M., "Laboratory Studies and Calculations on the Influence of Crack Width on Chloride-Induced Corrosion of Steel in Concrete," ACI Materials Journal, V. 94, No. 1, Jan.-Feb. 1997, pp. 56-62.
3. Baweja, D.; Roper, H.; and Sirivivatnanon, V., "Chloride-Induced Steel Corrosion in Concrete: Part 1-Corrosion Rates, Corrosion Activity, and Attack Areas," ACI Materials Journal, V. 95, No. 3, May-June 1998, pp. 207-217. (Pubitemid 128551335)
4. Vu, K.; Stewart, M. G.; and Mullard, J., "Corrosion-Induced Cracking: Experimental Data and Predictive Models," ACI Structural Journal, V. 102, No. 5, Sept.-Oct. 2005, pp. 719-726. (Pubitemid 41358333)
5. Mechers, R. E., and Li, C. Q., "Phenomenological Modeling of Reinforcement Corrosion in Marine Environment," ACI Materials Journal, V. 103, No. 1, Jan.-Feb. 2006, pp. 25-32.
6. Francois, R., and Arliguie, G., "Effect of Micro-Cracking and Cracking on the Development of Corrosion in Reinforced Concrete Members," Magazine of Concrete Research, V. 51, No. 2, Apr. 1999, pp. 143-150.
7. Yuan, Y. S.; Ji, Y. S.; and Jiang, J. H., "Effect of Corrosion Layer of Steel Bar in Concrete on Time-Variant Corrosion Rate," Materials and Structures, V. 42, No. 10, 2009, pp. 1443-1450.
8. Yuan, Y. S., and Ji, Y. S., "Modeling Corroded Section Configuration of Steel Bar in Concrete Structure," Construction and Building Materials, V. 23, No. 6, 2009, pp. 2461-2466.
9. Liu, Y. P., and Weyers, R. E., "Modeling the Time-to-Corrosion Cracking in Chloride Contaminated Reinforced Concrete Structures," ACI Materials Journal, V. 95, No. 6, Nov.-Dec. 1998, pp. 675-680.