Corrosion-induced cracking: Experimental data and predictive models

ACI Structural Journal

Volumn 102, Issue 5, 2005, Pages 719-726

  Vu, Kim ^a   Stewart, Mark G ^b   Mullard, John ^b  

^a HANOI ARCHITECTURAL UNIVERSITY   (Viet Nam)

^b UNIVERSITY OF NEWCASTLE   (Australia)

Author keywords

Concrete; Corrosion; Cracking

Indexed keywords

BRIDGE DECKS; CONCRETE REINFORCEMENTS; CONCRETE SLABS; CRACK INITIATION; CRACK PROPAGATION; MATHEMATICAL MODELS; MECHANICAL TESTING; PITTING; STRESS CORROSION CRACKING; STRUCTURAL LOADS;

CORRECTION FACTOR; CORROSION RATE; CORROSION TESTING; PREDICTIVE MODEL;

REINFORCED CONCRETE;

EID: 25444483656     PISSN: 08893241     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (32)

1. Stewart, M. G., and Val, D. V., "Multiple Limit States and Expected Failure Costs for Deteriorating RC Bridges," Journal of Bridge Engineering, ASCE, V. 8, No. 6, 2003, pp. 405-415.
2. fib, "Bond of Reinforcement in Concrete: State-of-the-Art Report" Task Group on Bond Models, Lausanne, 2000.
3. Hartt, W. L.; Lee, S. K.; and Costa, E., "Condition Assessment and Deterioration Rate for Chloride Contaminated Reinforced Concrete Structures," Proceedings of the International Seminar on Repair and Rehabilitation of RC Structures: the State of the Art, ASCE, 1998, pp. 82-104.
4. Sterritt, G.; Chryssanthopoulos, M. K; and Shetty, N. K., "Reliability-Based Inspection Planning for RC Highway Bridges," Proceedings of the International Conference on Safety, Risk, and Reliability, IABSE, 2001, pp. 1001-1007.
5. Andrade, C.; Alonso, C.; and Molina, F. J., "Cover Cracking as a Function of Rebar Corrosion: Part 1 - Experimental Test," Material and Structures, V. 26, 1993, pp. 453-464.
6. Sakai, K.; Shimomura, T.; and Sugiyama, T., "Design of Concrete Structures in the 21st Century," Concrete, Durability and Repair Technology, R. K. Dhir and M. J. McCarthy, eds., Thomas Telford, UK, 1999, pp. 28-44.
7. Lin, Y., and Weyers, R. E., "Modeling the Time-to-Corrosion Cracking in Chloride Contaminated Reinforced Concrete Structures," ACI Materials Journal, V. 95, No. 6, Nov.-Dec. 1998, pp. 675-680.
8. Alonso, C.; Andrade, C.; Rodriguez, J.; and Diez, J. M., "Factors Controlling Cracking of Concrete Affected by Reinforcement Corrosion," Materials and Structures, V. 31, 1998, pp. 435-441.
9. Shayan, A., and Xu, A., "Progress of Corrosion and Time to Cracking in Chloride-Contaminated Concrete," Proceedings of Corrosion and Prevention 02, Australasian Corrosion Association, Adelaide, Australia, Nov. 2002. (CD-ROM)
10. Vu, K. A. T., "Corrosion-Induced Cracking and Spatial Timme-Dependent Reliability Analysis of Reinforced Concrete Structures," PhD thesis, University of Newcastle, Newcastle, Australia, 2003.
11. Stewart, M. G., and Vu, K. A. T., "Predicting the Proportion of a Concrete Surface Subject to Corrosion-Induced Cracking and Damage," Second International Conference on Bridge Maintenance, Safety, and Management, Balkema, Rotterdam, 2004. (CD-ROM)
12. Stewart, M. G., "Spatial Variability of Corrosion-Induced Damage and Life-Cycle Cost Analysis of RC Bridge Decks," Second International Conference on Bridge Maintenance, Safety, and Management, Balkema, Rotterdam, 2004. (CD-ROM)
13. ASTM 01-90, "Standard Practice for Preparing, Cleaning and Evaluating Corrosion Test Specimens," ASTM International, West Conshohocken, Pa., 1990, 8 pp.
14. Williamson, S. J., and Clark, L. A., "Effect of Corrosion and Load on Reinforcement Bond Strength," Structural Engineering International, V. 12, No. 2, 2002, pp. 117-122.
15. Molina, F. J.; Alonso, C.; and Andrade, C., "Cover Cracking as a Function of Rebar Corrosion: Part 2 - Numerical Model," Materials and Structures, V. 26, 1993, pp. 532-548.
16. Ovstaas, G., and Morgan, D. R., "Investigation of Concrete Jetties at CFB Esquimalt and Prediction of Future Life," Durability of Building Materials and Components 8: Service Life and Asset Management, M. A. Lacasse and D. J. Vanier, eds., V. 1, 1999, pp. 46-55.
17. Rodriguez, J.; Ortega, L. M.; Casal, J.; and Diez, J. M., "Corrosion of Reinforcement and Service Life of Concrete Structures," Proceedings of the 7th International Conference on Durability of Building Materials and Components, C. Sjostrom, ed., E&FN Spon, 1996, pp. 117-126.
18. Suda, K.; Mista, S.; and Motohashi, K., "Corrosion Products of Reinforcing Bars Embedded in Concrete," Corrosion Science, V. 35, No, 5 through 8, 1993, pp. 1543-1549.
19. Williamson, S. J., and Clark, L. A., "Pressure Required to Cause Cover Cracking of Concrete Due to Reinforcement Corrosion," Magazine of Concrete Research, V. 52, No. 6, 2000, pp. 455-467.
20. Ohtsu, M., and Yosimura, S., "Analysis of Crack Propagation and Crack -Initiation Due to Corrosion of Reinforcement," Construction and Building Materials, V. 11, No. 7 and 8, 1997, pp. 437-442.
21. Hansen, E. J., and Saouma, V. E., "Numerical Simulation of Reinforced Concrete Deterioration: Part HC Steel Corrosion and Concrete Cracking," ACI Materials Journal, V. 96, No. 3, May-June 1999, pp. 331-338.
22. Maruyama, K.; Takaoka, Y.; and Shimizu, K., "Cracking Behaviour of Concrete Due to Corrosion of Reinforcing Bars," Transactions of the Japan Concrete Institute, V. 11, 1989, pp. 163-170.
23. Rasheeduzzafar; Al-Sandoun, S. S.; and Al-Gahtani, A. S., "Corrosion Cracking in Relation to Bar Diameter, Cover, and Concrete Quality," Journal of Materials in Civil Engineering, ASCE, V. 4, No. 4, 1992, pp. 327-342.
24. Bazant, Z. P., "Physical Model for Steel Corrosion in Sea Structures-Theory," Journal of Structural Division, ASCE, V. 105, No. ST6, 1979, pp. 1137-1153.
25. Bazant, Z. P., "Physical Model for Steel Corrosion in Sea Structures-Applications," Journal of Structural Division, ASCE, V. 105, No. ST6, 1979, pp. 1155-1166.
26. ACI Committee 318, "Building Code Requirements for Structural Concrete (ACI 318M-02) and Commentary (318RM-02)," American Concrete Institute, Farmington Hills, Mich., 2002, 443 pp..
27. Stewart, M. G.; Vu, K. A. T.; and Mullard, J., "Corrosion-Induced Crack Initiation and Propagation for Reinforced Concrete Structures: Experimental Data and Predictive Models," Research Report No. 247.06.2004, Centre of Infrastructure Performance and Reliability, School of Engineering, The University of Newcastle, Newcastle, Australia, 2004.
28. Saifullah, M., and Clark, L. A., "Effects of Corrosion Rate on the Bond Strength of Corroded Reinforcement," Corrosion and Corrosion Protection of Steel in Concrete, Proceedings of International Conference held at the University of Sheffield, R. N. Swamy, ed., Sheffield Academic Press, 1994, pp. 591-602.
29. El Manddawy, T. A., and Soudki, K. A., "Effectiveness of Impressed Current Technique to Simulate Corrosion of Steel Reinforcement in Concrete," Journal of Materials in Civil Engineering,V. 15, No. 1, 2003, pp. 41-47.
30. Mangat, P., and Elgarf, M., "Flexural Strength of Concrete Beams with Corroding Reinforcement," ACI Structural Journal, V. 96, No. 1, Jan.-Feb. 1999, pp. 149-158.
31. Vu, K. A. T., and Stewart, M. G., "Structural Reliability of Concrete Bridges Including Improved Chloride-Induced Corrosion Models," Structural Safety, V. 22, No. 4, 2000, pp. 313-333.
32. Aligizaki, K. K., "Modeling of Concrete Cracking due to Corrosion of Embedded Reinforcement," PhD thesis, The Pennsylvania State University, University Park, Pa., 1999.