Microscopic observations on the origin of defects during machining of direct aged (DA) inconel 718 superalloy

Journal of Materials Engineering and Performance

Volumn 19, Issue 8, 2010, Pages 1193-1198

  Dosbaeva, G K ^a   Veldhuis, S C ^a   Elfizy, A ^b   Fox Rabinovich, G ^a   Wagg, T ^a  

^a MCMASTER UNIVERSITY   (Canada)

^b Manufacturing Engineering Development   (Canada)

Author keywords

Aerospace; Coatings; Failure analysis; Machining; Metallography

Indexed keywords

AEROSPACE; CEMENTED CARBIDES; COMPLEX CARBIDE; CROSS SECTION; INCONEL-718; MACHINED SURFACE; METALLOGRAPHIC OBSERVATIONS; MICROSCOPIC OBSERVATIONS; OPTICAL METALLOGRAPHY; OXIDE LAYER; SEM/EDS; SERVICE CHARACTERISTICS; SURFACE DEFECT FORMATION; SURFACE QUALITIES; TIALN COATINGS; TOOL LIFE;

AEROSPACE INDUSTRY; CARBIDES; COATINGS; CRACK DETECTION; DENDRITES (METALLOGRAPHY); FAILURE ANALYSIS; MACHINING; METALLOGRAPHY; MICROSTRUCTURE; NIOBIUM OXIDE; OXYGEN; QUALITY ASSURANCE; SUPERALLOYS;

SURFACE DEFECTS;

EID: 78149283752     PISSN: 10599495     EISSN: None     Source Type: Journal    
DOI: 10.1007/s11665-009-9587-3     Document Type: Article

References (17)

1. RS Pawade S Suhas S Joshi PK Brahmankar M Rahman 2007 An Investigation of Cutting Forces and Surface Damage in High-Speed Turning of Inconel 718 J. Mater. Proc. Technol. 192-193 139 146 10.1016/j.jmatprotec.2007.04.049 (Pubitemid 47187994)
2. SP Lynch TC Radtke BJ Wicks RT Byrnes 1994 Fatigue Crack Grows in Nickel-Based Superalloys at 500-700 °C. II: Direct-Aged Alloy 718 Fatigue Fract. Eng. Mater. Struct. 17 3 313 325 1:CAS:528:DyaK2cXks1eiurY%3D 10.1111/j.1460-2695.1994.tb00232.x
3. W Gailian W Cuiwei Z Maicang D Jianxin X Xishan J Radavich AB Lindsley G Shen 2003 The Microstructural Changes and Their Effect on CCGR After Long Time Thermal Exposure in DA718 and STD718 Mater. Sci. Eng. A358 71 75
4. J.R. Davis, ASM Specialty Handbook: Heat-Resistant Materials, ASM International, OH, 1997, p 591
5. RF Decker 2006 The Evolution of Wrought Age-Hardenable Superalloys JOM 58 9 32 36 1:CAS:528:DC%2BD28XhtVakt7bK 10.1007/s11837-006-0079-8
6. A Devillez F Schneider S Dominiak D Dudzinski D Larrouquere 2007 Cutting Forces and Wear in Dry Machining of Inconel 718 with Coated Carbide Tools Wear 262 931 942 1:CAS:528:DC%2BD2sXitFyku78%3D 10.1016/j.wear.2006.10.009
7. ARC Sharman A Amarasinghe K Ridgway 2008 Tool Life and Surface Integrity Aspects When Drilling and Hole Making in Inconel 718 J. Mater. Proc. Technol. 200 424 432 1:CAS:528:DC%2BD1cXjsFGhtrs%3D 10.1016/j.jmatprotec.2007.08.080 (Pubitemid 351318185)
8. YC Fayman 1987 Microstructural Characterization and Elemental Partitioning in a Direct-Aged Superalloy (DA 718) Mater. Sci. Eng. 92 159 171 1:CAS:528:DyaL2sXltlyqtbg%3D 10.1016/0025-5416(87)90166-2 (Pubitemid 17638393)
9. AY Shinyaev YV Solov'ev 1993 Effect of Alloying on the Plasticity and Heat Resistance of Niobium Metal Sci. Heat Treat. 35 3-4 237 241 10.1007/BF00775144
10. A Strondl R Fischer G Frommeyer A Schneider 2008 Investigations of MX and γ′/γ″ Precipitates in the Nickel-Based Superalloy 718 Produced by Electron Beam Melting Mater. Sci. Eng. 480 1-2 138 147
11. J-K Hong N-K Park S-J Kim C-Y Kang 2005 Microstructures of Oxidized Primary Carbides on Superalloy Inconel 718 Mater. Sci. Forum 502 249 256 1:CAS:528:DC%2BD2MXht1Ojtb%2FI 10.4028/www.scientific.net/MSF.502.249
12. EO Ezugwu J Bonney Y Yamane 2003 An Overview of the Machinability of Aeroengine Alloys J. Mater. Proc. Technol. 134 2 233 253 1:CAS:528: DC%2BD3sXpslSktw%3D%3D 10.1016/S0924-0136(02)01042-7
13. A Sharman RC Dewes DK Aspinwall 2001 Tool Life When High Speed Ball Nose End Milling Inconel 718 J. Mater. Proc. Technol. 118 1-3 9 35
14. J Ma M Wu Y Du S Chen W Jin L Fu Q Yang A Wen 2009 Formation of Nanocrystalline Niobium Carbide (NbC) with a Convenient Route at Low Temperature J. Alloys Compd. 475 1-2 415 417 1:CAS:528:DC%2BD1MXktlynt78%3D 10.1016/j.jallcom.2008.07.039 2009AIPC.1133..415M
15. R Arunachalam MA Mannan 2000 Machinability of Nickel-Based High Temperature Alloys Mach. Sci. Technol. 4 1 127 168 1:CAS:528: DC%2BD3cXivVCnt7o%3D 10.1080/10940340008945703
16. G Byrne D Dornfeld B Denkena 2003 Advancing Cutting Technology Ann. CIRP 52 2 483 507 10.1016/S0007-8506(07)60200-5
17. M.G. Fontana, Corrosion Engineering, 3rd ed., McGraw-Hill, New York, 1986, p 505-506