Influence of carbide precipitation and rolling direction on intergranular stress corrosion cracking of austenitic stainless steels in hydrogenated high-temperature water

Corrosion

Volumn 62, Issue 7, 2006, Pages 568-575

  Arioka, K ^a   Yamada, T ^a   Terachi, T ^a   Chiba, G ^a  

^a INSTITUTE OF NUCLEAR SAFETY SYSTEM   (Japan)

Author keywords

Carbide precipitation; Cold work; Grain boundary sliding; Intergranular stress corrosion cracking; Stainless steel

Indexed keywords

CARBIDES; COLD WORKING; GRAIN BOUNDARIES; HYDROGENATION; PRECIPITATION (CHEMICAL); STAINLESS STEEL;

CARBIDE PRECIPITATION; GRAIN BOUNDARY SLIDING; INTERGRANULAR STRESS CORROSION CRACKING;

STRESS CORROSION CRACKING;

CARBIDES; COLD WORKING; GRAIN BOUNDARIES; HYDROGENATION; PRECIPITATION (CHEMICAL); STAINLESS STEEL; STRESS CORROSION CRACKING;

EID: 33750883685     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3280670     Document Type: Article

References (33)

1. K. Arioka, "Effect of Temperature, Hydrogen, and Boric Acid Concentration of IGSCC Susceptibility of Annealed 316 Stainless Steel," Proc. Int. Symp. on Fontevraud 5 (France: French Nuclear Energy Society, 2002), p. 149.
2. K. Arioka, T. Yamada, T. Terachi, "Influence of Hydrogen, Boric Acid, and Grain Boundary Carbide on IGSCC Behaviors of SUS316 Under Hydrogenated PWR Primary Water," Proc. 11th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (LaGrange Park, IL: American Nuclear Society, 2003).
3. K. Arioka, T. Yamada, T. Terachi, R.W. Stachle, Corrosion 62, 1 (2006): p. 74.
4. W.E. Berry, E.L. White, W.K. Boyd, Corrosion 29 (1973): p. 451.
5. R.L. Cowan, B.M. Gordon, "Intergranular Stress Corrosion Cracking and Grain Boundary Composition of Fe-Ni-Cr Alloys," Proc. Stress Corrosion Cracking and Hydrogen Embrittlement of Iron-Based Alloys, eds. R.W. Stachle, J. Hochmann, R.D. McCright, J.E. Slater (Houston, TX: NACE International, 1978), p. 1,023.
6. K. Arioka, M. Hourai, S. Okamoto, K. Onimura, "The Effect of Boric Acid, Solution Temperature, and Sensitization on SCC Behavior Under Elevated Temperature Water," CORROSION/83, paper no. 135 (Houston, TX: NACE, 1983).
7. F.P. Ford, D.F. Taylor, P.L. Andresen, R.G. Ballinger, "Environmentally Controlled Cracking of Stainless Steels in Light Water Reactor Environments," NP-5064M (Palo Alto, CA: Electric Power Research Institute, 1987).
8. S.M. Bruemmer, B.W. Arey, L.A. Charlot, Corrosion 48 (1992): p. 42.
9. W.H. Bamford, J.P. Foster, R.S. Pathania. "An Investigation of Alloy 182 Stress Corrosion Cracking in Simulated PWR Environment," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, eds. S. Bruemmer, P. Ford, G. Was (Warrendale, PA: The Minerals, Metals, and Materials Society 1999), p. 279.
10. G.P. Airey, Metallography 13 (1981): p. 21.
11. T. Yonezawa, K. Onimura, N. Sakamoto, N. Sasaguri, H. Nakata, R. Susukida, "Effect of Heat Treatment on Stress Corrosion Cracking Resistance of High-Nickel Alloys In High-Temperature Water," Proc. Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ed. W. Berry (Houston, TX: NACE, 1983). p. 345.
12. J.L. Hertzberg, G.S. Was, Metall. Mater. Trans. A 29A (1998): p. 1,035.
13. F. Vaillant, J.-D. Mithieux, O. de Bouvier, D. Vacon, G. Zacharie, Y. Brechet. F. Louchet, "Influence of Chromium Content and Microstructure on Creep and PWSCC Resistance of Nickel-Based Alloys," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, eds. S. Bruemmer, P. Ford, G. Was (Warrendale, PA: The Minerals, Metals, and Materials Society, 1999), p. 251.
14. P.L. Andresen, "Effect of Noble Metal Coating and Alloying on the Stress Corrosion Crack Growth of Austenitic Stainless Steel in 288°C Water," Proc. 6th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, eds. R.E. Gold, Ed.P. Simonen (New York, NY: American Institute of Mining. Metallurgical, and Petroleum Engineers (AIME], 1994), p. 245-253.
15. P.L. Andresen, "Effect of Specific Anionic Impurities on Environmental Cracking of Austenitic Materials in 288°C Water," Proc. 5th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (LaGrange Park, IL: American Nuclear Society, 1991), p. 209-218.
16. P.L. Andresen, P.W. Emigh, M.M. Morra, R.M. Horn, "Alloy X750 Stress Corrosion Crack Growth Rate Behavior in High-Temperature Water." Proc. 11th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ed. G.S. Was (LaGrange Park, IL: American Nuclear Society, 2003).
17. M.E. Indig, D.A. Vermilea. Corrosion 31 (1975): p. 51.
18. S.M. Bruemmer, B.W. Arey, L.A. Chariot, "Grain Boundary Chromium Concentration Effects on the IGSCC and IASCC of Austenitic Stainless Steels," Proc. 6th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, eds. R.E. Gold, P. Simonen (New York, NY: American Institute of Mining, Metallurgical, and Petroleum Engineers [AIME], 1994), p. 277-285.
19. J.B. Lee, Corrosion 37 (1981): p. 467.
20. J.K. Sung, G.S. Was, Corrosion 47 (1991): p. 824.
21. G.S. Was, J.K. Sung, T.M. Angeliu, Metall. Trans. A. 23A (1992): p. 1,033.
22. T.M. Angeliu, J.K. Sung, G.S. Was, The Role of Carbon and Chromium on the Mechanical and Oxidation Behavior of Nickel-Based Alloys in High-Temperature Water," Proc. 5th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (LaGrange Park, IL: American Nuclear Society, 1992), p. 475.
23. T.M. Angeliu, G.S. Was, Metall. Trans. A25A (1994): p. 1,169.
24. T.M. Angeliu, D.J. Paraventi, G.S. Was, Corrosion 51 (1995): p. 837.
25. Y. Yi, G.S. Was, J. Cookson, "Creep of Nickel-Based Alloys in High-Temperature Water," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, eds. S. Bruemmer, P. Ford, G. Was (Warrendale, PA: The Minerals, Metals, and Materials Society, 1999). p. 269.
26. B. Capell, L. Fournier, G.S. Was, "Intergranular Cracking Behavior of Ni-xCr-9Fe-C Alloys in Hydrogenated Steam," Proc. 10th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Houston, TX: NACE, 2001).
27. P.L. Andresen, T.M. Angeliu, L.M. Young, "Effect of Martensite and Hydrogen on SCC of Stainless Steels and Alloy 600," CORROSION/2001, paper no. 01228 (Houston, TX: NACE, 2001).
28. M.O. Speidel, R. Magdowski, "Stress Corrosion Cracking of Stabilized Austenitic Stainless Steels in Various Types of Nuclear Power Plants," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, eds. S. Bruemmer, P. Ford, G. Was (Warrendale, PA: The Minerals, Metals, and Materials Society, 1999), p. 325.
29. M.P. Puls, R. Dutton, R.N. Stevens, Acta Metall. 22 (1974): p. 639.
30. R. Raj, M.F. Ashby, Acta Metall. 23 (1975): p. 653.
31. K. Sadananda, Metall. Trans. A 9A (1978): p. 635.
32. V. Vitek, Acta Metall. 26 (1978): p. 1,345.
33. K. Sadananda, Metall. Trans. A 11A (1980): p. 1,980.