Mechanism of factory-roof formation

Engineering Fracture Mechanics

Volumn 77, Issue 11, 2010, Pages 1763-1771

  Pokluda, J ^a   Slamecka K ^a   Sandera P ^a  

^a BRNO UNIVERSITY OF TECHNOLOGY   (Czech Republic)

Author keywords

Factory roof; Formation mechanism; Stereophotogrammetry; Torsional fatigue loading

Indexed keywords

CYCLIC TORSION; ELEMENTARY MODE; FORMATION MECHANISM; LOW CYCLE FATIGUES; MIXED MODE; MODE II; MODE III; SCANNING ELECTRON MICROSCOPE; SEMI-ELLIPTICAL SURFACE CRACKS; SIZE REDUCTIONS; STEEL SPECIMENS; STEREOPHOTOGRAMMETRY; THREE-DIMENSIONAL MODEL; TORSIONAL FATIGUE; TORSIONAL FATIGUE LOADING; WEAR DAMAGE;

CRACKS; FATIGUE DAMAGE; PHOTOGRAMMETRY; ROOFS; SCANNING ELECTRON MICROSCOPY; SHAFTS (MACHINE COMPONENTS); SURFACE DEFECTS; THREE DIMENSIONAL; TORSIONAL STRESS;

LOADING;

EID: 77954033220     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfracmech.2010.03.031     Document Type: Article

References (15)

1. Nayeb-Hashemi H., McClintock F.A. Effects of friction and high torque on fatigue crack propagation in mode III. Metall Trans 1982, A13:2197-2204.
2. Ritchie R.O., McClintock F.A., Nayeb-Hashemi H., Rittler M.A. Mode III fatigue crack propagation in low alloy steel. Metall Trans 1982, A13:101-110.
3. Tschegg E.K. The influence of the static I load mode and R ratio on mode III fatigue crack growth behavior in mild steel. Mater Sci Engng 1982, A54:127-137.
4. Nayeb-Hashemi H., McClintock F.A., Ritchie R.O. Micro-mechanical modeling of mode III fatigue crack growth in rotor steels. Int J Fract 1983, 23:163-185.
5. Multiaxial fatigue, ASTM STP 853 1985, ASTM, Philadelphia. K.J. Miller, M.W. Brown (Eds.).
6. Tanaka K., Akinawa Y., Yu H. The propagation of a circumferential fatigue crack in medium-carbon steel bars under combined torsional and axial loadings. Mixed-mode crack behaviour, ASTM STP 1359 1999, 295-311. ASTM, West Conshohocken. K.J. Miller, D.L. McDowel (Eds.).
7. Makabe C., Anggit M., Sueyoshi T., Yafuso T. The formation mechanism of the factory-roof pattern in a torsional fatigue specimen with circumferential notch. J Test Eval 2006, 34:423-429.
8. Vaziri A., Nayeb-Hashemi H. The effect of crack surface interaction on the stress intensity factor in mode III crack growth in round shafts. Engng Fract Mech 2005, 72:617-629.
9. Vaziri A., Nayeb-Hashemi H. A theoretical investigation on the vibrational characteristics and torsional dynamic response of circumferentially cracked turbo-generator shafts. Int J Sol Struct 2006, 43:4063-4081.
10. Slámečka K., Pokluda J., Ponížil P., Major Š., Šandera P. On the topography of fracture surfaces in bending-torsion fatigue. Engng Frac Mech 2008, 75:760-767.
11. Pook L.P. Crack paths 2002, Wit Press, Southampton.
12. Pokluda J., Pippan R. Can a pure mode III fatigue loading contribute to crack propagation in metallic materials? Fatigue Fract Engng Mater Struct 2005, 28:179-186.
13. Kasir M.K., Sih G.C. Three-dimensional stress distribution around an elliptical crack under arbitrary loading. J Appl Mech 1966, 33:601-611.
14. Pilkey W.D., Pilkey D.F. Peterson's stress concentration factors 2008, John Willey & Sons, New York.
15. Holáň L, Pippan R, Pokluda J, Horníková J, Hohenwarter T, Slámečka K. Near-threshold propagation of mode II and mode III cracks. In: Atzori B, Carpinteri A, Lazzarin P, Pook LP, editors. Crack Paths - CP2009, University of Padua, Vicenza; 2009. p. 585-92.