Pitting corrosion of triggering initial fractures of palm oil screw press machine shafts

Engineering Failure Analysis

Volumn 17, Issue 5, 2010, Pages 1086-1093

  Loganathan, T M ^a   Purbolaksono, J ^b   Inayat Hussain, J I ^b   Muthaiyah, G ^c   Wahab, N ^d  

^a Polytechnic of Sultan Azlan Shah   (Malaysia)

^b Universiti Tenaga Nasional   (Malaysia)

^c Megasteel Sdn Bhd   (Malaysia)

^d UNIVERSITI TEKNOLOGI MARA   (Malaysia)

Author keywords

Failure analysis; Fatigue analysis; Pitting corrosion; Shaft; Visual inspection

Indexed keywords

FATIGUE ANALYSIS; FATIGUE ENDURANCE LIMIT; MALAYSIA; PALM OIL; PITTING CORROSION; ROOT CAUSE; SCREW PRESS; SHAFT; SHAFT FAILURE; SHAFT MATERIAL; SHOULDER FILLET; SURFACE CONDITIONS; TORSIONAL LOADINGS; VISUAL INSPECTION;

CORROSION FATIGUE; FAILURE ANALYSIS; INDUCTION MOTORS; INSPECTION; MICROSCOPIC EXAMINATION; MINING; PRESSES (MACHINE TOOLS); QUALITY ASSURANCE; VEGETABLE OILS; VISUAL COMMUNICATION;

PITTING;

EID: 77952427748     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2010.01.002     Document Type: Article

References (18)

1. Taylor D., Bologna P., Bel Knani K. Prediction of fatigue failure location on a component using a critical distance method. Int J Fatigue 2000, 22(9):735-742.
2. Neuber H. Theory of notch stresses 1958, Springer, Berlin.
3. Peterson R.E. Notch sensitivity. Metal fatigue 1959, 293-306. McGraw-Hill, New York. G. Sines, J.L. Waisman (Eds.).
4. Cerit M., Genel K., Eksi S. Numerical investigation on stress concentration of corrosion pit. Eng Fail Anal 2009, 16:2467-2472.
5. Rokhlin S.I., Kim J.-Y., Nagy H., Zoofan H. Effect of pitting corrosion on fatigue crack initiation and fatigue life. Eng Fract Mech 1999, 62:425-444.
6. Wang Q.Y., Kawagoishi N., Chen Q. Effect of pitting corrosion on very high cycle fatigue behavior. Scripta Mater 2003, 49:711-716.
7. Shi P., Mahadevan S. Damage tolerance approach for probabilistic pitting corrosion fatigue life prediction. Eng Fract Mech 2001, 68:1493-1507.
8. Wulpi DJ. Failures of shafts. In: Failure analysis and prevention. ASM metals handbook, vol. 11. Metals Park (OH): American Society for Metals; 1986. p. 459-82.
9. Shigley J.E., Mitchell L.D. Mechanical engineering design 1983, McGraw-Hill, New York. 4th ed.
10. ASME ANSI B17.1-67.R98, keys and keyseats 1998, American Society of Mechanical Engineers, New York.
11. Murakami Y. Metal Fatigue: effects of small defects and nonmetallic inclusions 2002, Elsevier, Oxford.
12. Juvinall R.C. Engineering consideration of stress, strain and strength 1967, McGraw-Hill, New York.
13. Kuhn P, Hardrath HF. An engineering method for estimating notch size effect in fatigue. NACA TN 2805; 1952.
14. Collins J.A. Mechanical design of machine elements and machines: a failure prevention perspective 2003, John Wiley & Sons, New York.
15. Maleque M.A., Masjuki H.H., Haseeb A.S.M.A. Effect of mechanical factors on tribological properties of palm oil methyl ester blended lubricant. Wear 2000, 239:117-125.
16. Wan Y., Cao L., Xuet Q. Friction and wear characteristics of ZDDP in the sliding of steel against aluminium alloy. Tribol Int 1997, 30:767-772.
17. Ang C.Y.W., Liu K., Huang Y.-W. Asian food: science and technology 1999, Technomic Publishing Company, Pennsylvania.
18. Sabnavis G., Kirk G., Kasarda M., Quinn D. Cracked shaft detection and diagnostics: a literature review. Shock Vib Dig 2004, 36(4):287-295.