Tg and rheological properties of triazine-based molecular glasses: Incriminating evidence against hydrogen bonds

Journal of Physical Chemistry B

Volumn 113, Issue 45, 2009, Pages 14884-14891

  Plante, André ^a   Mauran, Damien ^b   Carvalho, Simão P ^a   Pagé, J Y S Danny ^a   Pellerin, Christian ^b   Lebel, Olivier ^a  

^a ROYAL MILITARY COLLEGE OF CANADA   (Canada)

^b UNIVERSITÉ DE MONTRÉAL   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

FOURIER TRANSFORM INFRARED SPECTROSCOPY; GLASS; GLASS BONDING; GLASS TRANSITION; HYDROGEN; NUCLEAR MAGNETIC RESONANCE SPECTROSCOPY; RHEOLOGY; VISCOSITY;

ASSOCIATION CONSTANT; FTIR AND NMR SPECTROSCOPY; GLASS TRANSITION TEMPERATURE; GLASSY PHASIS; HYDROGEN BONDINGS; MOLECULAR GLASS; RHEOLOGICAL PROPERTY; SELF-ASSEMBLE; STRUCTURAL MODIFICATIONS; SUPRAMOLECULAR AGGREGATES;

HYDROGEN BONDS;

EID: 72449175844     PISSN: 15206106     EISSN: None     Source Type: Journal    
DOI: 10.1021/jp905268a     Document Type: Article

References (39)

1. For example, see:(a) Pearson, R. G. Plastics Rubber 1976, 1, 21-22.
2. (b) Pearson, G. H.; Garfield, L. J. Polym. Eng. Sci. 1978, 18, 583-589.
3. (c) Rojo, E.; Muñoz, M. E.; Santamaria, A.; Peña, B. Macromol. Rapid Commun. 2004, 25, 1314-1318.
4. (a) Ozawa, T. Polymer 1971, 12, 150-158.
5. (b) Kotek, J.; Raab, M.; Baldrian, J.; Grellmann, W. J. Appl. Polym. Sci. 2002, 85, 1174-1184.
6. (a) Kwack, T.-H.; Han, C.-D. J. Appl. Polym. Sci. 1983, 28, 3419-3433.
7. (b) Oyanagi, Y.; Kubota, K. J. Polym. Eng. 1986, 7, 47-75.
8. (c) Chivers, R. A.; Moore, D. P. Polymer 1994, 35, 110-116.
9. For example, see: (a) Shirota, Y. J. Mater. Chem. 2000, 10, 1-25.
10. (b) Strohriegl, P.; Grazulevicius, J. V. AdV. Mater. 2002, 14, 1439-1452.
11. (c) Shirota, Y. J. Mater. Chem. 2005, 15, 75-93.
12. (d) Grazulevicius, J. V. Polym. AdV. Technol. 2006, 17, 694-696.
13. (e) Shirota, Y.; Kageyama, H. Chem. ReV. 2007, 107, 953-1010.
14. For example, see:(a) Angell, C. A. Science 1995, 267, 1924-1935.
15. (b)Ediger, M. D.; Angell, C. A.; Nagel, S. R. J. Phys. Chem. 1996, 100, 13200-13212.
16. (c) Hancock, B. C.; Zografi, G. J. Pharm. Sci. 1997, 86, 1-12.
17. (d) Yu, L. AdV. Drug DeliVery ReV. 2001, 48, 27-42.
18. (a) Hancock, B. C.; Shalaev, E. Y.; Shamblin, S. L. J. Pharm. Pharmacol. 2002, 54, 1151-1152.
19. For example, see: (a) Angell, C. A.; Ngai, K. L.; McKenna, G. B.; McMillan, P. F.; Martin, S. W. J. Appl. Phys. 2000, 88, 3113-3157.
20. (b) Gutzow, I.; Grigorova, Ts.; Todorova, S. J. Non-Cryst. Solids 2002, 304, 4-18.
21. (c) Roland, C. M. Soft Matter 2008, 4, 2316-2322.
22. Naito, K. Chem. Mater. 1994, 6, 2343-2350.
23. (a) De Rosa, M. E.; Adams, W. W.; Bunning, T. J.; Shi, H.; Chen, S. H. Macromolecules 1996, 29, 5650-5657.
24. (b) Boils, D.; Perron, M.-È.; Monchamp, F.; Duval, H.; Maris, T.; Wuest, J. D. Macromolecules 2004, 37, 7351-7357.
25. Lebel, O.; Maris, T.; Perron, M.-È.; Demers, E.; Wuest, J. D. J. Am. Chem. Soc. 2006, 128, 10372-10373.
26. Wang, R.; Pellerin, C.; Lebel, O. J. Mater. Chem. 2009, 19, 2747-2753.
27. Wuest, J. D.; Lebel, O. Tetrahedron 2009, 65, 7393-7402.
28. Since we could not quantify the absolute molar fraction of N-H groups participating in hydrogen bonding in the samples, the concept of hydrogen bonding index is used herein in a qualitative fashion to describe differences in hydrogen bonding as a function of temperature.
29. Hynes, M. J. J. Chem. Soc., Dalton Trans. 1993, 311-312. Software available on request at: michael.j.hynes@nuigalway.ie.
30. This temperature was chosen because viscosity is low enough that the apparatus does not reach shear stress limit at high shear rate.
31. Carreau, P. J.; De Kee, D. Can. J. Chem. Eng. 1979, 57, 3-15.
32. Mezger, T. G. The Rheology-Handbook; Zorll, U., Ed.; Vincentz: Hannover, 2002.
33. The high resistance of compound 9a to crystallization under thermal conditions was already reported. See ref 11.
34. Frequency scans were performed at various amplitudes, but the results did not vary significantly.
35. No degradation was observed in the same temperature range by DSC, possibly because the DSC measurement was taken under nitrogen atmosphere. Chlorinated polymers such as PVC are known to degrade upon heating: Fuchsman, C. H. SPE J. 1959, 15, 787-790.
36. For ease of comparison, bonded N-H vs free N-H ratios (which were calculated by comparing the heights of the respective bands) were normalized to a value of 1 for the measure taken at the lowest temperature for each data set. Thus, for every sample, the bonded N-H vs free N-H ratio for every temperature was divided by the ratio taken at the lowest temperature.
37. Fielding, L. Tetrahedron 2000, 56, 6151-6170.
38. Beijer, F. H.; Sijbesma, R. P.; Vekemans, J. A. J. M.; Meijer, E. W.; Kooijman, H.; Spek, A. L. J. Org. Chem. 1996, 61, 6371-6380.
39. While the CH2 group of compound 1 rotates freely, triazine amines (such as the headgroups of compounds 6 and 9) are known to be hybridized sp2 (see refs 10 and 11) and display rotational barriers on the order of 18 kcal/mol: Hyengoyan, A. P.; Mamyan, S. S.; Gomktsyan, T. A.; Hambardzumyan, E. N.; Vorskanyan, A. S.; Eliazyan, K. A.; Pivazyan, V. A.; Dovlatyan, V. V. Chem. Heterocycl. Compd. 2005, 41, 1059-1061.