Volumn 9, Issue 4, 2009, Pages 370-379
|
|
Failure analysis of HAZ cracking in Low C-CrMoV steel weldment
|
|
Author keywords
GTAW; Heat affected zone; Nozzle; Residual stresses; Untempered martensite; Weld cracking
|
|
Indexed keywords
ALLOY STEEL;
CIRCUMFERENTIAL WELDING;
CONSTRAINT CONDITIONS;
CRMOV STEEL;
GAS TUNGSTEN ARC WELDING;
GTAW;
INTERGRANULAR BRITTLE;
LOCALIZED HEATING;
MICROHARDNESS MEASUREMENT;
NON DESTRUCTIVE TESTING;
ROOT CAUSE;
SINGLE PASS;
TRANSFORMATION STRESS;
UNTEMPERED MARTENSITE;
VISUAL EXAMINATION;
VISUAL INSPECTION;
WELD BEAD;
WELD CRACKING;
WELDING HEAT INPUT;
WELDING SPEED;
WELDMENTS;
BRITTLE FRACTURE;
CRACKING (CHEMICAL);
CRACKS;
ELECTRIC WELDING;
FAILURE ANALYSIS;
GAS METAL ARC WELDING;
GAS WELDING;
HEATING;
MARTENSITE;
NONDESTRUCTIVE EXAMINATION;
NOZZLES;
OPTICAL MICROSCOPY;
QUALITY ASSURANCE;
RESIDUAL STRESSES;
SAFETY FACTOR;
TUNGSTEN;
VISUAL COMMUNICATION;
X RAY RADIOGRAPHY;
HEAT AFFECTED ZONE;
|
|
EID: 70449523531
PISSN: 15477029
EISSN: None
Source Type: Journal
DOI: 10.1007/s11668-009-9256-8 Document Type: Article |
|
Times cited : (7)
|
|
References (10)
|