Cross-linking of poly(methyl methacrylate) by oxozirconate and oxotitanate clusters

Macromolecular Symposia

Volumn 175, Issue , 2001, Pages 357-366

  Trimmel, Gregor ^a   Moraru, Bogdan ^a   Gross, Silvia ^b   Di Noto, Vito ^b   Schubert, Ulrich ^a  

^a VIENNA UNIVERSITY OF TECHNOLOGY   (Austria)

^b UNIVERSITY OF PADOVA   (Italy)

Author keywords

[No Author keywords available]

Indexed keywords

CROSS-LINKED POLYMERS; IMPEDANCE SPECTRUM; INORGANIC-ORGANIC HYBRID POLYMERS; RADICAL POLYMERIZATION; SOLVENT UPTAKE; THERMAL STABILITY;

ACRYLIC MONOMERS; ESTERS; FREE RADICAL POLYMERIZATION; ORGANIC SOLVENTS; PHOTORESISTS; ZIRCONIUM;

ORGANIC POLYMERS;

EID: 70449462013     PISSN: 10221360     EISSN: 15213900     Source Type: Journal    
DOI: 10.1002/1521-3900(200110)175:1<357::AID-MASY357>3.0.CO;2-D     Document Type: Article

References (25)

1. For example: T. S. Haddad, J. D. Lichtenhan, Macromolecules, 29, 7302 (1996).
2. J. J. Schwab, J. D. Lichtenhan, K. P. Chaffee, P. T. Mather, A. Romo-Uribe, Mat. Res. Soc. Symp. Proc., 519, 21 (1998).
3. J. D. Lichtenhan, T. S. Haddad, J. J. Schwab, M. J. Karr, K. P. Chaffee, P. T. Mather, Polym. Prep, 39(1), 489 (1998).
4. J. Pynn, K. Matyjaszewski, Macromolecules, 33, 217 (2000).
5. For example: A. Sellinger, R. M. Laine, Macromolecules, 29, 2327 (1996).
6. E. K. Lin, C.-R. Snyder, F. I. Mopsik, W. E. Wallace, W. L. Wu, C. X. Zhang, R. M. Laine, Mat. Res. Soc. Symp. Proc., 519, 15 (1998).
7. F. Ribot, F. Banse, C. Sanchez, M. Lahcini, B. Jousseaumme, J. Sol-Gel Sci. Technol., 8, 529 (1997).
8. L. Angiolini, D. Caretti, C. Carlini, R. De Vito, F. T. Niesei, E. Salatelli, F. Ribot, C. Sanchez, J. Inorg. Organomet. Polym., 7, 151 (1998).
9. L. G. Hubert-Pfalzgraf, N. Pajot, R. Papiemik, S. Parraud, Mat. Res. Soc. Symp. Proc., 435, 137(1996).
10. C. R. Mayer, R. Thouvenot, T. Lalot, Chem.Mater., 12, 257 (2000).
11. G. Kickelbick, U. Schubert, Mat. Res. Soc. Symp. Proc., 519, 401 (1998).
12. G. Kickelbick, U. Schubert, Chem.Ber., 130, 473 (1997).
13. G. Trimmel, S. Gross, G. Kickelbick, U. Schubert, Appl. Organomet. Chem., in press.
14. G. Kickelbick, P. Wiede, U. Schubert, Inorg. Chim. Acta, 284, 1 (1999).
15. U. Schubert, E. Arpac, W, Glaubitt, A. Helmerich, C. Chau, Chem.Mater. 4, 291 (1992).
16. G. Kickelbick, U, Schubert, Europ. J. Inorg. Chem. 159 (1998).
17. A typical procedure is as follows: To a solution of 2.62 g (26.2 mmol) methyl methacrylate (filtered over alumina to remove the stabilizer) and 0.91 g (0.54 mmol) of 1 in 6 ml benzene, 21 mg (0.09 mmol) of dibenzoylperoxide were added. When heated to 65 °C, the solution became turbid after 2-3 h and then solidified. Heating was continued for 9-10 h, and then the solvent was removed at 70 °C / 8 mbar. The remaining benzene was extracted with ethyl acetate, and then the solvent was again removed under reduced pressure. The olefin : initiator : solvent ratio was kept constant when the cluster: olefin ratio was varied.
18. G. Trimmel, P. Fratzl, U. Schubert, Chem.Mater. 12, 602 (2000).
19. S. Besecke, G. Schröder, W, Gänzler, German patent DE 31 37 840 C2 (1981).
20. R. Di Maggio, L. Fambri, A. Guerriero, Chem. Mater., 10, 1777 (1998).
21. C. Sanchez, M. In, J Non-Cryst. Solids, 147&148, 1 (1992),
22. M. In, C. Gerardin, J., Lambard, C. Sanchez, J. Sol-Gel Sci. Technol., 5, 101 (1995).
23. M. Camail, M. Humbert, A. Margaillan, J. L. Vernet, Polymer, 39, 6533 (1998).
24. H, T. Neher, W. R. Conn, E. H. Kroeker, US patent US 2,502,411 (1947).
25. V. Di Noto, D. Barreca, C. Furlan, L. Armelao, Polym. Adv. Technol. 11, 108 (2000).