Controllable synthesis and luminescence properties of La(OH)3 and La(OH)3ITb3+ nanocrystals with multiform morphologies

European Journal of Inorganic Chemistry

Volumn , Issue 25, 2009, Pages 3721-3726

  Jia, Guang ^a,b   Huang, Yeju ^a,b   Song, Yanhua ^a,b   Yang, Mei ^a,b   Zhang, Lihui ^a,b   You, Hongpeng ^a  

^a CHANGCHUN INSTITUTE OF APPLIED CHEMISTRY   (China)

^b UNIVERSITY OF CHINESE ACADEMY OF SCIENCES   (China)

Author keywords

Hydrothermal synthesis; Lanthanum; Luminescence; Nanostructures; Polymorphism

Indexed keywords

ALKALINITY; HYDROTHERMAL SYNTHESIS; LANTHANUM; LUMINESCENCE OF INORGANIC SOLIDS; MORPHOLOGY; NANOCRYSTALS; PHOSPHORS; TERBIUM COMPOUNDS;

ALKALINE SOURCES; CONTROLLABLE SYNTHESIS; HYDROTHERMAL PROCESS; INITIAL SOLUTION; LUMINESCENCE PROPERTIES; MORPHOLOGY AND SIZE; ONE-DIMENSIONAL; PH VALUE; SYNTHESISED; ]+ CATALYST;

LANTHANUM COMPOUNDS;

EID: 69049118080     PISSN: 14341948     EISSN: 10990682     Source Type: Journal    
DOI: 10.1002/ejic.200900495     Document Type: Article

References (45)

1. X. Wang, Y. D. Li, Angew. Chem. Int. Ed. 2002, 41, 4790-4793.
2. J. L. Zhuang, L. F. Liang, H. Sung, X. F. Yang, M. M. Wu, I. D. Williams, S. H. Feng, Q. Su, Inorg. Chem. 2007, 46, 5404-5410.
3. L. F. Liang, H. F. Xu, Q. Su, H. Konishi, Y. B. Jiang, M. M. Wu, Y. F. Wang, D. Y. Xia, Inorg. Chem. 2004, 43, 1594-1596.
4. J. M. Wang, L. Gao, J. Mater. Chem. 2003, 13, 2551-2554.
5. J. Nishijo, O. Oishi, K. Judai, N. Nishi, Chem. Mater. 2007, 19, 4627-4629.
6. M. H. Huang, S. Mao, H. Feick, H. Yan, Y. Wu, H. Kind, E. Weber, R. Russo, P. D. Yang, Science 2001, 292, 1897-1899.
7. Y. N. Xia, P. D. Yang, Y. G. Sun, Y. Y. Wu, B. Mayers, B. Gates, Y. D. Yin, F. Kim, H. Q. Yan, Adv. Mater. 2003, 15, 353-389.
8. L. Zhao, T. Lu, M. Yosef, M. Steinhart, M. Zacharias, U. Go-sele, S. Schlecht, Chem. Mater. 2006, 18, 6094-6096.
9. B. Wang, L. F. Zhu, Y. H. Yang, N. S. Xu, G. W. Yang, J. Phys. Chem. C 2008, 112, 6643-6647.
10. D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, Y. Tang, Adv. Mater. 2000, 12, 520-523.
11. M. Yada, M. Mihara, S. Mouri, M. Kuroki, T. Kijima, Adv. Mater. 2002, 14, 309-313.
12. X. F. Duan, C. M. Lieber, Adv. Mater. 2000, 12, 298-302.
13. Z. W. Pan, Z. R. Dai, Z. L. Wang, Science 2001, 291, 1947-1949.
14. G. P. Patzke, F. Krumeich, R. Nesper, Angew. Chem. Int. Ed. 2002, 41, 2446-2461.
15. X. Wang, Y. D. Li, Chem. Eur. J. 2003, 9, 5627-5635.
16. X. Wang, Y. D. Li, Inorg. Chem. 2006, 45, 7522-7534.
17. G. F. Zou, H. Li, Y. G. Zhang, K. Xiong, Y. T. Qian, Nanotech-nology 2006, 17, S313-S320.
18. J. Yang, C. X. Li, Z. Y. Cheng, X. M. Zhang, Z. W. Quan, C. M. Zhang, J. Lin, J. Phys. Chem. C 2007, 111, 18148-18154.
19. J. Zhang, Z. Liu, J. Lin, J. Fang, Cryst. Growth Des. 2005, 5, 1527-1530.
20. M. S. Palmer, M. Neurock, M. M. Olken, J. Am. Chem. Soc. 2002, 124, 8452-8461.
21. W. H. Di, X. J. Wang, B. J. Chen, H. S. Lai, X. X. Zhao, Opt. Mater. 2005, 27, 1386-1390.
22. J. P. Cotter, J. C. Fitzmaurice, I. P. Parkin, J. Mater. Chem. 1994, 4, 1603-1609.
23. G. Jia, M. Yang, Y. H. Song, H. P. You, H. J. Zhang, Cryst. Growth Des. 2009, 9, 301-307.
24. A. H. Peruski, L. H. Johnson, L. F. Peruski, J. Immunol. Methods 2002, 263, 35-41.
25. C. G. Hu, H. Liu, W. T. Dong, Y. Y. Zhang, G. Bao, C. S. Lao, Z. L. Wang, Adv. Mater. 2007, 19, 470-474.
26. R. X. Yan, X. M. Sun, X. Wang, Q. Peng, Y. D. Li, Chem. Eur. J. 2005, 11, 2183-2195.
27. Y. P. Fang, A. W. Xu, R. Q. Song, H. X. Zhang, L. P. You, J. C. Yu, H. Q. Liu, J. Am. Chem. Soc 2003, 125, 16025-16034.
28. G. Wang, Z. D. Wang, Y. X. Zhang, G. T. Fei, L. D. Zhang, Nanotechnology 2004, 15, 1307-1311.
29. A. W. Xu, Y. P. Fang, L. P. You, H. Q. Liu, J. Am. Chem. Soc. 2003, 125, 1494-1495.
30. C. K. Chang, Q. A. Zhang, D. L. Mao, Nanotechnology 2006, 17, 1981-1.985.
31. F. Niu, A. M. Cao, W. G. Song, L. J. Wan, J. Phys. Chem. C. 2008, 112, 17988-17993.
32. J. L. Zhu, Y. H. Zhou, H. X. Yang, J. Power Sources 1997, 69, 169-173.
33. M. P. Rosynek, D. T. Magnuson, J. Catal. 1977, 46, 402-413.
34. B. Tang, J. C. Ge, L. H. Zhuo, Nanotechnology 2004, 15, 1749.
35. Q. Tang, Z. P. Liu, S. Li, S. Y. Zhang, X. M. Liu, Y. T. Qian, J. Cryst. Growth 2003, 259, 208-214.
36. H. P. You, G. Y. Hong, X. Y. Wu, J. K. Tang, H. P. Hu, Chem. Mater. 2003, 15, 2000-2004.
37. M. Yu, H. Wang, C. K. Lin, G. Z. Li, J. Lin, Nanotechnology 2006, 17, 3245-3252.
38. Y. X. Zhang, S. S. Pan, X. M. Teng, Y. Y. Luo, G. H. Li, J. Phys. Chem. C 2008, 112, 9623-9626.
39. J. C. Boyer, J. Gagnon, L. A. Cuccia, J. A. Capobianco, Chem. Mater. 2007, 19, 3358-3360.
40. J. X. Wan, Z. H. Wang, X. Y. Chen, L. Mu, Y. T. Qian, J. Cryst. Growth 2005, 284, 538-543.
41. M. Yu, J Lin, Z. Wang, J. Fu, S. Wang, H. J. Zhang, Y. C. Han, Chem. Mater. 2002, 14, 2224-2231.
42. K. B. Kim, Y. I. Kim, H. G. Chun, T. Y. Cho, J. S. Jung, J. G. Kang, Chem. Mater. 2002, 14, 5045-5052.
43. K. Y. Jung, H. W. Lee, H. K. Jung, Chem. Mater. 2006, 18, 2249-2255.
44. X. M. Zhang, J. H. Zhang, L. F. Liang, Q. Su, Mater. Res. Bull. 2005, 40, 281-288.
45. Q. Y. Zhang, K. Pita, W. Ye, W. X. Que, Chem. Phys. Lett. 2002, 351, 163-170.