Microwave-assisted synthesisof monodisperse nickel nanoparticles using a complex of nickel formate with long-chainamine ligands

Bulletin of the Chemical Society of Japan

Volumn 82, Issue 8, 2009, Pages 1044-1051

  Yamauchi, Tomohisa ^a   Tsukahara, Yasunori ^a   Sakamoto, Tetsuo ^b   Kono, Takumi ^b   Yasuda, Makoto ^a   Baba, Akio ^a   Wada, Yuji ^c  

^a OSAKA UNIVERSITY   (Japan)

^b NIPPON STEEL CORPORATION   (Japan)

^c TOKYO INSTITUTE OF TECHNOLOGY   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

ALKYL AMINES; AVERAGE SIZE; DODECYL AMINES; FACE-CENTERED CUBIC; MICROWAVE-ASSISTED; MONODISPERSE; NI NANOPARTICLES; NI2+ ION; NICKEL FORMATE; NICKEL NANOPARTICLES; OLEYLAMINE; REACTION TEMPERATURE;

CARBON DIOXIDE; HYDROGEN; IONS; LIGANDS; MAGNETIC PROPERTIES; MICROWAVE IRRADIATION; NANOPARTICLES; NICKEL ALLOYS;

NICKEL;

EID: 68949170489     PISSN: 00092673     EISSN: 13480634     Source Type: Journal    
DOI: 10.1246/bcsj.82.1044     Document Type: Article

References (49)

1. G. Schmid, Chem. Rev. 1992, 92, 1709.
2. K. R. Gopidas, J. K. Whitesell, M. A. Fox, Nano Lett. 2003, 3, 1757.
3. D. J. Maxwell, J.R.Taylor, S. Nie, J. Am. Chem. Soc. 200, 124, 9606.
4. P. V. Kamat, J. Phys. Chem. B 2002, 106, 7729.
5. T. K. Sau, C. J. Murphy, J. Am. Chem. Soc. 2004, 126, 8648.
6. M.-C. Daniel, D. Astruc, Chem. Rev. 2004, 104, 293.
7. M.M.Oliveira, E. G. Castro, C. D. Canestraro, D. Zanchet, D. Ugarte, L. S. Roman, A. J. G. Zarbin, J. Phys. Chem. B 2006, 110, 17063.
8. S. Sun, C. B. Murray, D. Weller, L. Folks, A. Moser, Science 2000, 287, 1989.
9. W. X. Zhang, C. B. Wang, H. L. Lien, Catal. Today 1998, 40, 387.
10. D. V. Leff, P. C. Ohara, J. R. Heath, W. M. Gelbart, J. Phys. Chem. 1995, 99, 7036.
11. C. Burda, X. Chen, R. Narayanan, M. A. El-Sayed, Chem. Rev. 2005, 105, 1025.
12. M. Tsuji, R. Matsuo, P. Jiang, N. Miyamae, D. Ueyama, M. Nishio, S. Hikino, H. Kumagae, K. S. N. Kamarudin, X.-L. Tang, Cryst. Growth Des. 2008, 8, 2528.
13. M. G. Perichaud, J. Y. Deletage, H. Fremont, Y. Danto, C. Faure, M. Salagoity, IEEE, International Electronics Manufacturing Technology Symposium 1998, p. 377.
14. T. R. Rao, Fundamentalsof Microsystem Packaging, McGraw Hill International Edition, 2001.
15. W. Chen, L. Li, J. Qi, Y. Wang, Z. Gui, J. Am. Ceram. Soc. 1998, 81, 2751.
16. N. Sato, H. Katayama, S. Ogasawara, Kawasaki Seitetsu Giho 2002, 34, 120.
17. Y. Koltypin, A. Fernandez, T. C. Rojas, J. Campora, P. Palma, R. Prozorov, A. Gedanken, Chem. Mater. 1999, 11, 1331.
18. D.-H. Chen, S.-H. Wu, Chem. Mater. 2000, 12, 1354.
19. S.-H. Wu, D.-H. Chen, Chem. Lett. 2004, 33, 406.
20. O. Margeat, C. Amiens, B. Chaudret, P. Lecante, R. E. Benfield, Chem. Mater. 2005, 17, 107.
21. M. Green, P. O'Brien, Chem. Commun. 2001, 1912.
22. Y. Hou, S. Gao, J. Mater. Chem. 2003, 13, 1510.
23. H. Winnischofer, T. C. R. Rocha, W. C. Nunes, L. M. Socolovsky, M. Knobel, D. Zanchet, ACS Nano 2008, 2, 1313.
24. L. K. Kurihara, G. M. Chow, P. E. Schoen, Nanostruct. Mater. 1995, 5, 607.
25. N. Chakroune, G. Viau, C. Ricolleau, F. Fievet-Vincent, F. Fievet, J. Mater. Chem. 2003, 13, 312.
26. G. M. Chow, J. Ding, J. Zhang, K. Y. Lee, D. Surani, S.H. Lawrence, Appl. Phys. Lett. 1999, 74, 1889.
27. H. Yin, G. M. Chow, J. Electrochem. Soc. 2002, 149, C68.
28. P. Toneguzzo, G. Viau, O. Acher, F. Guillet, E. Bruneton, F. Fievet-Vincent, F. Fievet, J. Mater. Sci. 2000, 35, 3767.
29. C. N. Chinnasamy, B. Jeyadevan, K. Shinoda, K. Tohji, A. Narayanasamy, K. Sato, S. Hisano, J. Appl. Phys. 2005, 97, 10J309.
30. Z. Zhang, X. Chen, X. Zhang, C. Shi, Solid State Commun. 2006, 139, 403.
31. V. Rosenband, A. Gany, J. Mater Process. Technol. 2004, 153-154, 1058.
32. P. G. Fox, J. Ehretsmann, C. E. Brown, J. Catal. 1971, 20, 67.
33. E. Iglesia, M. Boudart, J. Catal. 1984, 88, 325.
34. A. B. Edwards, C. D. Garner, K. J. Roberts, J. Phys. Chem. B 1997, 101, 20.
35. J.-H. Lee, C.-K. Kim, S. Katoh, R. Murakami, J. Alloys Compd. 2001, 325, 276.
36. F. Bondioli, A. M. Ferrari, C. Leonelli, C.Siligardi, G.C. Pellacani, J. Am. Ceram. Soc. 2001, 84, 2728.
37. M. N. Nadagouda, R. S. Varma, Cryst. Growth Des. 2008, 8, 291.
38. T. Yamamoto, Y. Wada, T. Sakata, H. Mori, M. Goto, S. Hibino, S. Yanagida, Chem. Lett. 2004, 33, 158.
39. T. Nakamura, Y. Tsukahara, T. Sakata, H. Mori, Y. Kanbe, H. Bessho, Y. Wada, Bull. Chem. Soc. Jpn. 2007, 80, 224.
40. T. Nakamura, Y. Tsukahara, T. Yamauchi, T. Sakata, H. Mori, Y. Wada, Chem. Lett. 2007, 36, 154.
41. Y. Wada, H. Kuramoto, T. Sakata, H. Mori, T. Sumida, T. Kitamura, S. Yanagida, Chem. Lett. 1999, 607.
42. M. Tsuji, M. Hashimoto, T. Tsuji, Chem. Lett. 2002, 1232.
43. D. Li, S. Komarneni, J. Am. Ceram. Soc. 2006, 89, 1510.
44. 45, 46 An aqueous solution of nickel dichloride (12 mmol) was mixed with acetylacetone (24 mmol) and an aqueous solution of potassium hydroxide (24 mmol). The resulting solution was stirred for 10 min. Then tmen (15 mmol) was added into the mixture and the solution was stirred for 20 min. The complex was extracted with 1, 2-dichloromethane and purified by recrystallizing from 1, 2- dichloromethane under air atmosphere Preparation of the Ni2+ complex [Ni(acac)2(tmen)]; Crystalline [Ni(acac)2(tmen)] was prepared in the following procedure.45, 46 An aqueous solution of nickel dichloride (12 mmol) was mixed with acetylacetone (24 mmol) and an aqueous solution of potassium hydroxide (24 mmol). The resulting solution was stirred for 10 min. Then tmen (15 mmol) was added into the mixture and the solution was stirred for 20 min. The complex was extracted with 1, 2-dichloromethane and purified by recrystallizing from 1, 2- dichloromethane under air atmosphere.
45. T. Yoshida, T. Suzuki, K. Kanamori, S.Kaizaki, Inorg. Chem. 1999, 38, 1059.
46. S. Kaizaki, T. Yamauchi, Inorg. Chim. Acta 2007, 360, 649.
47. M. Yasuda, K. Chiba, A. Baba, J. Am. Chem. Soc. 2000, 122, 7549.
48. M. Yasuda, K. Chiba, N. Ohigashi, Y. Katoh, A. Baba, J. Am. Chem. Soc. 2003, 125, 7291.
49. R. Ivaniková, R. Bǒca, L. Dlháň, H. Fuess, A. Mašlejová, V. Mrázová, I. Svoboda, J. Titiš, Polyhedron 2006, 25, 3261.