Shock response of iron between 143 and 1275 K

Journal of Applied Physics

Volumn 106, Issue 2, 2009, Pages

  Zaretsky, E B ^a  

^a BEN GURION UNIVERSITY OF THE NEGEV   (Israel)

Author keywords

[No Author keywords available]

Indexed keywords

DYNAMIC YIELD; FREE SURFACES; HIGH-PRESSURE PHASE; IMPACT EXPERIMENT; LASER INTERFEROMETER; MIXED PHASE REGION; POLYCRYSTALLINE IRON; SHOCK LOADINGS; SHOCK RESPONSE; STRESS INDUCED PHASE TRANSFORMATIONS; TEMPERATURE RANGE; WAVE FORMS; WAVE STRUCTURES;

ELECTROLUMINESCENCE; INTERFEROMETERS; LASER INTERFEROMETRY; ORGANIC POLYMERS; TENSILE STRENGTH;

IRON ANALYSIS;

EID: 68249149287     PISSN: 00218979     EISSN: None     Source Type: Journal    
DOI: 10.1063/1.3174442     Document Type: Article

References (66)

1. A. Westgren, J. Iron Steel Inst., London 0021-1567 103, 303 (1921).
2. F. Birch, Am. J. Sci. 0002-9599 238, 192 (1940).
3. D. Bancroft, E. L. Peterson, and S. Minshall, J. Appl. Phys. 0021-8979 27, 291 (1956). 10.1063/1.1722359
4. J. C. Jamieson and A. W. Lawson, J. Appl. Phys. 0021-8979 33, 776 (1962). 10.1063/1.1777167
5. T. Takahashi and W. A. Bassett, Science 0036-8075 145, 483 (1964). 10.1126/science.145.3631.483
6. R. L. Clendenen and H. G. Drickamer, J. Phys. Chem. Solids 0022-3697 25, 865 (1964). 10.1016/0022-3697(64)90098-8
7. F. P. Bundy, J. Appl. Phys. 0021-8979 36, 616 (1965). 10.1063/1.1714038
8. T. S. Duffy, Rep. Prog. Phys. 0034-4885 68, 1811 (2005). 10.1088/0034-4885/68/8/R03 (Pubitemid 41024592)
9. V. N. Mineev and A. I. Funtikov, Izv., Acad. Sci., USSR, Phys. Solid Earth 41, 539 (2005).
10. A. K. Singh, A. Jain, H. P. Liermann, and S. K. Saxena, J. Phys. Chem. Solids 0022-3697 67, 2197 (2006). 10.1016/j.jpcs.2006.06.003 (Pubitemid 44321932)
11. S. Klotz, Y. Le Godec, Th. Strässle, and U. Stuhr, Appl. Phys. Lett. 0003-6951 93, 091904 (2008). 10.1063/1.2976128
12. T. Uchida, Y. Wang, M. L. Rivers, and S. R. Sutton, J. Geophys. Res. 0148-0227 106, 21799 (2001). 10.1029/2001JB000258
13. R. G. McQueen and S. P. Marsh, J. Appl. Phys. 0021-8979 31, 1253 (1960). 10.1063/1.1735815
14. L. V. Al'tshuler, K. K. Krupnikov, B. N. Ledenev, V. I. Zhuchikhin, and M. I. Brazhnik, Zh. Eksp. Teor. Fiz. 0044-4510 34, 874 (1958).
15. P. C. Johnson, B. A. Stein, and R. S. Davis, J. Appl. Phys. 0021-8979 33, 557 (1962). 10.1063/1.1702465
16. A. V. Anan'in, A. N. Dremin, and G. I. Kanel, Combust., Explos. Shock Waves 0010-5082 9, 381 (1973) 10.1007/BF00745120 G. I. Kanel, [Fiz. Goreniya Vzryva 0430-6228 9, 437 (1973)].
17. D. S. Hughes, L. E. Gourley, and M. F. Gourley, J. Appl. Phys. 0021-8979 32, 624 (1961). 10.1063/1.1736060
18. J. W. Taylor and M. H. Rice, J. Appl. Phys. 0021-8979 34, 364 (1963). 10.1063/1.1702614
19. P. L. Hereil, J. Phys. (Paris) 49, 77 (1988).
20. S. A. Novikov, I. I. Divnov, and A. G. Ivanov, Fiz. Met. Metalloved. 0015-3230 21, 608 (1966).
21. R. W. Rohde, Acta Metall. 0001-6160 17, 353 (1969). 10.1016/0001-6160(69) 90075-3
22. R. W. Rohde, Acta Metall. 0001-6160 18, 903 (1970). 10.1016/0001-6160(70) 90018-0
23. Z. Rosenberg, Y. Partom, and D. Yaziv, J. Phys. D 0022-3727 13, 1489 (1980). 10.1088/0022-3727/13/8/017
24. A. V. Anan'in, A. N. Dremin, and G. I. Kanel', Combust., Explos. Shock Waves 0010-5082 17, 320 (1981) 10.1007/BF00751308 A. V. Anan'in, A. N. Dremin, and G. I. Kanel', [Fiz. Goreniya Vzryva 0430-6228 17, 93 (1981)].
25. L. M. Barker and R. E. Hollenbach, J. Appl. Phys. 0021-8979 43, 4669 (1972). 10.1063/1.1660986
26. L. M. Barker and R. E. Hollenbach, J. Appl. Phys. 0021-8979 45, 4872 (1974). 10.1063/1.1663148
27. B. J. Jensen, P. A. Rigg, M. D. Knudson, R. S. Hixson, G. T. Gray III, B. H. Sencer, and F. J. Cherne, in Shock Compression of Condensed Matter 2005, edited by, M. D. Furnish, M. Elert, T. P. Russell, and, C. T. White, (AIP, Melville, New York, 2006), Vol. CP 845, p. 232.
28. C. Voltz and G. Roy, in Shock Compression of Condensed Matter 2003, edited by, M. D. Furnish, Y. M. Gupta, and, J. W. Forbes, (AIP, Melville, New York, 2004), Vol. CP 707, p. 511.
29. D. H. Kalantar, J. F. Belak, G. W. Collins, J. D. Colvin, H. M. Davies, J. H. Eggert, T. C. Germann, J. Hawreliak, B. L. Holian, K. Kadau, P. S. Lomdahl, H. E. Lorenzana, M. A. Meyers, K. Rosolankova, M. S. Schneider, J. Sheppard, J. S. Stölken, and J. S. Wark, Phys. Rev. Lett. 0031-9007 95, 075502 (2005). 10.1103/PhysRevLett.95.075502 (Pubitemid 41506036)
30. B. Yaakobi, T. R. Boehly, D. D. Meyerhofer, T. J. B. Collins, B. A. Remington, P. G. Allen, S. M. Pollaine, H. E. Lorenzana, and J. H. Eggert, Phys. Rev. Lett. 0031-9007 95, 075501 (2005). 10.1103/PhysRevLett.95.075501 (Pubitemid 41506035)
31. G. I. Kanel, S. V. Razorenov, and V. E. Fortov, J. Phys.: Condens. Matter 0953-8984 16, S1007 (2004). 10.1088/0953-8984/16/14/010
32. G. E. Duvall and R. A. Graham, Rev. Mod. Phys. 0034-6861 49, 523 (1977). 10.1103/RevModPhys.49.523
33. H. Nahme and M. Hiltl, in Metallurgical and Materials Application of Shock-Wave and High-Strain-Rate Phenomena, edited by, L. E. Murr, K. P. Staudhammer, and, M. A. Meyers, (Elsevier Science, Amsterdam, 1995), pp. 731-738.
34. J. M. Leger, C. Lorriers-Susse, and B. Vodar, Phys. Rev. B 6, 4250 (1972). 10.1103/PhysRevB.6.4250
35. N. A. Gokcen and R. G. Reddy, Thermodynamics, 2nd ed. (Springer, New York, 1996), p. 352.
36. D. J. Dever, J. Appl. Phys. 0021-8979 43, 3293 (1972). 10.1063/1.1661710
37. S. K. Satija, R. P. Com̀s, and G. Shirane, Phys. Rev. B 0163-1829 32, 3309 (1985). 10.1103/PhysRevB.32.3309
38. J. J. Adams, D. S. Agosta, R. G. Leisure, and H. Ledbetter, J. Appl. Phys. 0021-8979 100, 113530 (2006). 10.1063/1.2365714 (Pubitemid 46012160)
39. The elements with the largest, >1 ppm, content were C (20), O (50), Ge (5), Mn (1), Cu (2), P (2), N (5), Ni (2), S (5), Si (8), Ta (5), and Cr (2). The numbers in the parentheses correspond to the average, for four purchased plates, element content in ppm.
40. E. B. Zaretsky, J. Appl. Phys. 0021-8979 105, 093508 (2009). 10.1063/1.3122523
41. E. B. Zaretsky, J. Appl. Phys. 0021-8979 104, 123505 (2008). 10.1063/1.3042229
42. The ceramic rod of 3 mm diameter having two 0.8 mm bores approached the sample free surface at 45° so that the argon outlet was some 3 mm above the sample surface and for the same 3 mm above the VISAR beam spot. The gas flow was controlled by a needle valve so that the optimal flow reduced the free-of-flow thermocouple reading for 0.5 K.
43. T. Antoun, L. Seaman, D. Curran, G. I. Kanel, S. V. Razorenov, and A. V. Utkin, Spall Fracture (Springer, New York, 2002), pp. 90 and 99.
44. Y. S. Touloukian, R. K. Kirby, R. E. Taylor, and P. D. Desai, Thermal Expansion-Metallic Elements and Alloys, Thermophysical Properties of Matter Vol. 12 (Plenum, New York, 1975).
45. G. I. Kanel, S. V. Razorenov, and V. E. Fortov, Shock Wave Phenomena and the Properties of Condensed Matter (Springer, New York, 2004), p. 33.
46. R. Fowles and R. F. Williams, J. Appl. Phys. 0021-8979 41, 360 (1970). 10.1063/1.1658348
47. E. B. Zaretsky, G. I. Kanel, S. V. Razorenov, and K. Baumung, Int. J. Impact Eng. 0734-743X 31, 41 (2005). 10.1016/j.ijimpeng.2003.11.004
48. X. -J. Li, X. -M. Zhou, F. -H. Wang, and F. -Q. Jing, Chin. Phys. Lett. 0256-307X 18, 85 (2001). 10.1088/0256-307X/18/1/330
49. Y. S. Touloukian and E. H. Buyco, The TPRC Data Series (Plenum, New York, 1970), Vol. 4.
50. The differences between the specific heats at constant pressure and volume as well as the differences between the moduli at constant entropy and temperature were ignored.
51. M. A. Shtremel, Strength of Alloy (MISiS, Moscow, Russia, 1999), Vol. 1, p. 173 (in Russian).
52. R. Chang, Philos. Mag. 0031-8086 16, 1021 (1967) 10.1080/ 14786436708229690; R. Chang and L. J. Graham, Phys. Status Solidi 18, 99 (1966). 10.1002/pssb.19660180110
53. Additional cause of so wide range of variation in the low-temperature yield strength of different types of pure iron may be solute softening produced in bcc metal by certain elements, e.g., D. R. Trinkle and C. Woodward, Science 0036-8075 310, 1665 (2005). 10.1126/science.1118616 (Pubitemid 41780785)
54. V. A. Al'shitz and V. L. Indenbom, Sov. Phys. Usp. 0038-5670 18, 1 (1975). 10.1070/PU1975v018n01ABEH004689
55. γ transformation in iron has a two-stage mechanism (O. A. Boedtker, " Delay time in the alpha to gamma transformation of iron.," Ph.D. thesis, California Institute of Technology, 1961). At the first stage a comparatively slow (microseconds) thermally activated formation and growth, to some critical size, of the nuclei of γ -phase takes place. At the second stage the nuclei of the critical size complete the transformation through a shear mechanism.
56. γ transformation in iron vary between 1178 and 1185 K. The Tα-γ =1184 K of Refs. was chosen as some reference.
57. J. C. Boettger and D. C. Wallace, Phys. Rev. B 0163-1829 55, 2840 (1997). 10.1103/PhysRevB.55.2840
58. β=0.2.
59. The temperature at the upper boundary of the mixed phase region was calculated using formula T tr fin = Ttr exp [tr (Vtr-V tr fin) / Vtr], where tr is the Grüneisen parameter corrected for the initial temperature Ttr.
60. Tmax determined in the isentropic approximation using (1274 K) =2.31.
61. In the case of the first-order phase transition: A. L. Korzhenevskii, R. Bausch, and R. Schmitz, Phys. Rev. B 0163-1829 67, 100103 (R) (2003) 10.1103/PhysRevB.67.100103; In the case of the second-order phase transition: A. P. Levaniuk and N. V. Schedrina, Sov. Phys. Solid State 0038-5654 25, 1338 (1983).
62. L. R. Veeser, G. T. Gray III, J. E. Vorthman, P. J. Rodriguez, R. S. Hixson, and D. B. Hayes, in Shock Compression of Condensed Matter-1999, edited by, M. D. Furnish, L. C. Chhabildas, and, R. S. Hixson, (American Institute of Physics, Melville, NY, 2000), p. 73; C. Voltz and G. Roy, in Shock Compression of Condensed Matter-2003, edited by, M. D. Furnish, Y. M. Gupta, and, J. W. Forbes, (American Institute of Physics, Melville, NY, 2004), p. 511; T. de Resseguier and M. Hallouin, Phys. Rev. B 0163-1829 77, 174107 (2008). 10.1103/PhysRevB.77.174107
63. K. Kadau, T. C. Germann, P. S. Lomdahl, R. C. Albers, J. S. Wark, A. Higginbotham, and B. L. Holian, in Shock Compression of Condensed Matter-2007, edited by, M. Elert, M. D. Furnish, R. Cliau, N. Holmes, and, J. Nguyen, (American Institute of Pliysics, Melville, NY, 2007), Vol. 313.
64. G. Shen, V. B. Prakapenka, M. L. Rivers, and S. R. Sutton, Phys. Rev. Lett. 0031-9007 92, 185701 (2004). 10.1103/PhysRevLett.92.185701
65. K. Kadau, T. C. Germann, P. S. Lomdahl, R. C. Albers, J. S. Wark, A. Higginbotham, and B. L. Holian, Phys. Rev. Lett. 0031-9007 98, 135701 (2007). 10.1103/PhysRevLett.98.135701 (Pubitemid 46496422)
66. γ is about 1% (Ref.).